Intumescent formulations incorporating melamine phosphate

Once familiar with the fire test rig constructed by M Kay, and modified to allow incorporation of both video and computer facilities, Melamine Phosphate production was scaled up from small to large laboratory scale, and then commercial scale production was considered. Samples produced at each stage were compared analytically, visually and in fire testing. The separation and drying stages on a commercial scale lay unresolved practically, due to lack of test facilities. Different cure regimes for the Araldite MY753 and Versamid system were investigated along with weathering tests and cured samples. Surface priming is suggested for large scale application, though on a small scale a clean unprimed surface was thought sufficient. Some samples heat, aired, cracked at the edges but remained bonded on fire testing. An intumescent sample containing Melamine Phosphate, Araldite and Versamid could not be applied to a vertical surface successfully, the viscosity had to be increased to allow application and curing, various additives were tested, two successful ones being fumed silica and a solvent, isopropanol. The low percentages fumed silica used was incorporated into the sample and the viscosity and fire test results compared with a `standard sample'. An expanding graphite incorporated into a standard sample made mixing and application increasingly difficult, due to the lubricating affect of graphite, but the char produced was a good quality, stable char. A suitable formulation could now be mixed, applied and cured, and assuming no adverse interaction between the additives would protect the sample in the event of a fire.

Melamine phosphate as a component of intumescent coatings

Melamine orthophosphate has been shown to exhibit variations in its chemical constitution, and crystal shape and size, dependent upon the method of production. These crystal types have been incorporated with epoxy resin to produce intumescent coatings, which have been tested on a small scale fire testing device, designed and calibrated within this project. The factors influencing performance in three fire test regimes are the percentage loading of melamine phosphate, its chemical constitution, crystal size and shape, thermal degradation, and state of agglomeration . and dispersion in the coating, determined by the method of incorporation into the coating. When melamine phosphate is heat treated at 210ºC, a process designed to reduce its solubility, the performance of coatings produced with such material is profoundly affected, depending mainly on crystal size and shape alone. Consideration of heat transfer across the chars produced has allowed a quantitative evaluation of the thermal resistance of chars throughout a test. An optimum production route for melamine phosphate has been suggested, taking into account the requirements for weatherability of coatings as well as performance in a fire.

Chemical kinetic investigation of a commercial batch reactor process

The aim of this investigation was to study the chemical reactions occurring during the batchwise production of a butylated melamine-formaldehyde resin, in order to optimise the efficiency and economics of the batch processes. The batch process models are largely empirical in nature as the reaction mechanism is unknown. The process chemistry and the commercial manufacturing method are described. A small scale system was established in glass and the ability to produce laboratory resins with the required quality was demonstrated, simulating the full scale plant. During further experiments the chemical reactions of methylolation, condensation and butylation were studied. The important process stages were identified and studied separately. The effects of variation of certain process parameters on the chemical reactions were also studied. A published model of methylolation was modified and used to simulate the methylolation stage. A major result of this project was the development of an indirect method for studying the condensation and butylation reactions occurring during the dehydration and acid reaction stages, as direct quantitative methods were not available. A mass balance method was devised for this purpose and used to collect experimental data. The reaction scheme was verified using this data. The reactions stages were simulated using an empirical model. This has revealed new information regarding the mechanism and kinetics of the reactions. Laboratory results were shown to be comparable with plant scale results. This work has improved the understanding of the batch process, which can be used to improve product consistency. Future work has been identified and recommended to produce an optimum process and plant design to reduce the batch time.