Intragranular nucleation of austenite

The mechanism of intragranular nucleation of austenite in a duplex stainless steel (Fe-23.1 Cr-6.1 Ni-3.1 Mo-O.165 N-0.017 C, wt.%) weld metal and heat-affected zone (HAZ) has been examined. In the weld metal the acicular austenite is found to nucleate intragranularly on inclusions and subsequent plates form sympathetically resulting in a fine interlocked microstructure. Austenite plates adopt the Kurdjumov-Sachs orientation relationship with the ferrite matrix and grow with diffusion-controlled mechanism as evident from partitioning of substitutional alloying elements. At least one set of fine intrinsic dislocations on the austenite/ferrite interphase interfaces is observed suggesting that the boundaries are semi-coherent. The high cooling rates involved in the HAZ result in a supersaturated ferrite matrix where precipitation of intragranular austenite occurs as a result of reheating associated with subsequent passes. Austenite particles in the HAZ nucleate preferentially away from gain boundary austenite allotriomorphs indicating that intragranular precipitation is favoured by the supersaturated matrix.

The mechanical properties and formability of dual-phase steel

In recent years dual phase steels comprising of 5-20% martensite in a ferrite matrix have come into the limelight of high strength cold formable steels because of their potential for vehicle weight saving. They show the following features: no yield point; relatively low initial flow stress; high initial workhardening rate; well sustained work hardening. As a consequence of these characteristics, dual phase steels exhibit a better combination of strength and elongation than other HSLA steels. In this thesis, a broad view of the factors which influence their properties is presented. Mechanical properties and forming ability of a commercially available dual phase steel and an AL-Si killed steel processed to dual phase form are investigated to ascertain the effect of their microstructure on their properties. It is found that the yield phenomena are masked by the transformation induced stresses present during processing and so yield point could be recovered under suitable ageing treatment; that apart from giving the above properties dual phasing gives rise to very low strain-rate sensitivity and a low R value ~ 1; that the mechanical response under rolling conditions is not different from those under tension; that there is a danger of damage to tooling during forming operations of these steels if fracture should precede instability as a result of grain size dependent strength found for these steels. It is also found that very little deformation of the martensite islands took place during deformation except at high strains. The work-hardening and the strength levels can be controlled by either decreasing the grain size or increasing the martensite volume fraction, but it is found that increasing martensite has a detrimental effect on ductility and the ductility and fracture strength can be controlled better by refining the grain size. A remarkable effect found in the dual phase steel tested is that the compressive strength is higher than the tensile strength. The reason for this observation is not yet clear but it is suggested that it might be due to the introduction of emissary type dislocations into the ferrite lattice as a result of twins formed in the martensite during transformation from austenite. The twins are envisaged to be {111} <112> in character.

The effect of thermochemical treatment on the fatigue properties of alloy steels

The effect of thermochemical treatment namely carburising on the fatigue behaviour of one carbon and two alloy steels has been studied in rotating and unidirectional bending. The effect of carbon profile on the unidirect¬ional bending fatigue strength of 63SA14 was assessed, and it was found that single stage carburising with a surface carbon content of 0.8% has resulted in a higher fatigue strength than other types of carbon profiles. Residual stresses and other metallurgical variables arising from different carbon profiles, were also considered. The highest compressive stresses h~e resulted from boost-diffuse-carburising. On the other hand surface decarburisation was associated with tensile residual stresses and a reduced fatigue strength. Retained austenite was found to be detrimental in unidirectional bending fatigue; however its presence in carburised 83SAIS did not seem to influence the rotating bending fatigue strength. Carbide particles in globular and/or intergranular form were detrimental to compressive residual stresses; the unidirectional bending fatigue strength is markedly lowered. The highest fatigue strength was accomplished by vacuum carburising. The absence of internal oxidation was the key factor in the increased fatigue strength; the presence of uniformly distributed fine carbide particles did not upset the superior fatigue strength of vacuum carburised pieces. The effect of mean stress on the fatigue strength of carburised 63SA14 was studied. Increasing the mean stress as would be expected resulted in a decreased fatigue strength. Carburisation showed its advantages at low mean stress, but at high mean stress it offers little advantage over the uncarburised hardened conditions. Notch effect was also studied in unidirectional bending of carburised 080MlS. The general trend showed that the fatigue strength decreases with increasing the stress concentration factor. But different carburising conditions have different effect on notch sensitivity.

Cleavage initiation in the intercritically reheated coarse-grained heat-affected zone:Part I. Fractographic evidence

Tensile, crack opening displacement (COD), blunt notch, and Charpy impact tests were used to investigate cleavage initiation in the intercritically reheated coarse-grained heat-affected zone (IC CG HAZ) of three steels. The steels were chosen to provide different distributions and morphologies of MA (high-carbon martensite with some retained austenite) particles within the IC CG HAZ structure. Observation of minimum impact toughness values for the IC CG HAZ was found to be associated with a particular microstructure containing a near-connected grain boundary network of blocky MA particles, the MA particles being significantly harder than the internal grain microstructure. The initiation mechanism for this structure was determined to be from a combination of an overlap of residual transformational induced stress fields, due to the formation of the MA particles, between two closely spaced particles and stress concentration effects resulting from debonding of the particles. © 1994 The Minerals, Metals and Materials Society, and ASM International.

Effect of cooling rate on intercritically reheated microstructure and toughness in high strength low alloy steel

High strength low alloy steels have been shown to be adversely affected by the existence of regions of poor impact toughness within the heat affected zone (HAZ) produced during multipass welding. One of these regions is the intercritically reheated coarse grained HAZ or intercritical zone. Since this region is generally narrow and discontinuous, of the order of 0.5 mm in width, weld simulators are often employed to produce a larger volume of uniform microstructure suitable for toughness assessment. The steel usedfor this study was a commercial quenched and tempered steel of 450 MN m -2 yield strength. Specimen blanks were subjected to a simulated welding cycle to produce a coarse grained structure of upper bainite during the first thermal cycle, followed by a second thermal cycle where the peak temperature T p2 was controlled. Charpy tests carried out for T p2 values in the range 650-850°C showed low toughness for T p2 values between 760 and 790°C, in the intercritical regime. Microstructural investigation of the development of grain boundary martensite-retained austenite (MA) phase has been coupled with image analysis to measure the volume fraction of MAformed. Most of the MA constituent appears at the prior austenite grain boundaries during intercritical heating, resulting in a 'necklace' appearance. For values of T p2 greater than 790°C the necklace appearance is lost and the second phase areas are observed throughout the structure. Concurrent with this is the development of the fine grained, predominantly ferritic structure that is associated with the improvement in toughness. At this stage the microstructure is transforming from the intercritical regime structure to the supercritically reheated coarse grained HAZ structure. The toughness improvement occurs even though the MA phase is still present, suggesting that the embrittlement is associated with the presence of a connected grain boundary network of the MA phase. The nature of the second phase particles can be controlled by the cooling rate during the second cycle and variesfrom MA phase at high cooling rates to a pearlitic structure at low cooling rates. The lowest toughness of the intercritical zone is observed only when MA phase is present. The reason suggested for this is that only the MA particles debond readily, a number of debonded particles in close proximity providing sufficient stress concentration to initiate local cleavage. © 1993 The Institute of Materials.

Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels

Fatigue crack initiation and propagation in duplex stainless steels are strongly affected by microstructure in both inert and aggressive environments. Fatigue crack growth rates in wrought Zeron 100 duplex stainless steel in air were found to vary with orientation depending on the frequency of crack tip retardation at ferrite/austenite grain boundaries. Fatigue crack propagation rates in 3.5% NaCl solution and high purity water are increased by hydrogen assisted transgranular cyclic cleavage of the ferrite. The corrosion fatigue results are interpreted using a model for the cyclic cleavage mechanism.

Elemental partitioning and microstructural development in duplex stainless steel weld metal

A thermodynamic analysis which is capable of estimating the austenite/ferrite equilibria in duplex stainless steels has been carried out using the sublattice thermodynamic model. The partitioning of alloying elements between the austenite and ferrite phases has been calculated as a function of temperature. The results showed that chromium partitioning was not influenced significantly by the temperature. The molybdenum, on the other hand, was found to partition preferentially into ferrite phase as the temperature decreases. A strong partitioning of nickel into the austenite was observed to decrease gradually with increasing temperature. Among the alloying elements, average nitrogen concentration was found to have the most profound effect on the phase balance and the partitioning of nitrogen into the austenite. The partitioning coefficient of nitrogen (the ratio of the mole fraction of nitrogen in the austenite to that in the ferrite) was found to be as high as 7.0 around 1300 K. Consequently, the volume fraction of austenite was influenced by relatively small additions of nitrogen. The results are compared with the experimentally observed data in a duplex stainless steel weld metal in conjunction with the solid state δ → δ + γ phase transformation. Particular attention was given to the morphological instability of grain boundary austenite allotriomorphs. A compariso between the experimental results and calculations indicated that the instability associated with irregular austenite perturbations results from the high degree of undercooling. The results suggest that the model can be used successfully to understand the development of the microstructure in duplex stainless steel weld metals.