Improved lithium storage properties of electrospun TiO2 with tunable morphology:from porous anatase to necklace rutile

Three-dimensional TiO2 with tunable morphology and crystalline phase was successfully prepared by the electrospinning technique and subsequent annealing. Porous-shaped anatase TiO2, cluster-shaped anatase TiO2, hierarchical-shaped rutile (minor) TiO2 and nano-necklace rutile (major) TiO2 were achieved at 500, 600, 700 and 800°C, respectively. The mechanism of the formation of these tailored morphologies and crystallinity was investigated. Lithium insertion properties were evaluated by galvanostatic and potentiostatic modes in half-cell configurations. By combining the large surface area, open mesoporosity and stable crystalline phase, the porous-shaped anatase TiO2 exhibited the highest capacity, best rate and cycling performance among the four samples. The present results demonstrated the usefulness of three-dimensional TiO 2 as an anode for lithium storage with improved electrode performance. © 2013 The Royal Society of Chemistry.

Synthesis of magnetically separable and recyclable g‑C3N4−Fe3O4 hybrid nanocomposites with enhanced photocatalytic performance under visible-light irradiation

Herein we demonstrate a facile, reproducible, and template-free strategy to prepare g-C3N4–Fe3O4 nanocomposites by an in situ growth mechanism. The results indicate that monodisperse Fe3O4 nanoparticles with diameters as small as 8 nm are uniformly deposited on g-C3N4 sheets, and as a result, aggregation of the Fe3O4 nanoparticles is effectively prevented. The as-prepared g-C3N4–Fe3O4 nanocomposites exhibit significantly enhanced photocatalytic activity for the degradation of rhodamine B under visible-light irradiation. Interestingly, the g-C3N4–Fe3O4 nanocomposites showed good recyclability without loss of apparent photocatalytic activity even after six cycles, and more importantly, g-C3N4–Fe3O4 could be recovered magnetically. The high performance of the g-C3N4–Fe3O4 photocatalysts is due to a synergistic effect including the large surface-exposure area, high visible-light-absorption efficiency, and enhanced charge-separation properties. In addition, the superparamagnetic behavior of the as-prepared g-C3N4–Fe3O4 nanocomposites also makes them promising candidates for applications in the fields of lithium storage capacity and bionanotechnology.