Preparation of a poly(L-lactide-co-caprolactone) copolymer using a novel tin(II) alkoxide initiator and its fiber processing for potential use as an absorbable monofilament surgical suture

A poly(L-lactide-co-caprolactone) copolymer, P(LL-co-CL), of composition 75:25 mol% was synthesized via the bulk ring-opening copolymerization of L-lactide and ε-caprolactone using a novel bis[tin(II) monooctoate] diethylene glycol coordination-insertion initiator, OctSn-OCH2CH2OCH2CH2O-SnOct. The P(LL-co-CL) copolymer obtained was characterized by a combination of analytical techniques, namely nuclear magnetic resonance spectroscopy, gel permeation chromatography, dilute-solution viscometry, differential scanning calorimetry, and thermogravimetric analysis. For processing into a monofilament fiber, the copolymer was melt spun with minimal draw to give a largely amorphous and unoriented as-spun fiber. The fiber's oriented semicrystalline morphology, necessary to give the required balance of mechanical properties, was then developed via a sequence of controlled offline hot-drawing and annealing steps. Depending on the final draw ratio, the fibers obtained had tensile strengths in the region of 200–400 MPa.

Increased expression of phosphorylated forms of RNA-dependent protein kinase and eukaryotic initiation factor 2 alpha may signal skeletal muscle atrophy in weight-losing cancer patients

Previous studies suggest that the activation (autophosphorylation) of dsRNA-dependent protein kinase (PKR) can stimulate protein degradation, and depress protein synthesis in skeletal muscle through phosphorylation of the translation initiation factor 2 (eIF2) on the alpha-subunit. To understand whether these mediators are important in muscle wasting in cancer patients, levels of the phospho forms of PKR and eIF2alpha have been determined in rectus abdominus muscle of weight losing patients with oesophago-gastric cancer, in comparison with healthy controls. Levels of both phospho PKR and phospho eIF2alpha were significantly enhanced in muscle of cancer patients with weight loss irrespective of the amount and there was a linear relationship between phosphorylation of PKR and phosphorylation of eIF2alpha (correlation coefficient 0.76, P=0.005). This suggests that phosphorylation of PKR led to phosphorylation of eIF2alpha. Myosin levels decreased as the weight loss increased, and there was a linear relationship between myosin expression and the extent of phosphorylation of eIF2alpha (correlation coefficient 0.77, P=0.004). These results suggest that phosphorylation of PKR may be an important initiator of muscle wasting in cancer patients.

Poly(3-hexylthiophene) based block copolymers prepared by "click" chemistry

p-Conjugated block copolymers have been prepared from terminal azide functionalized polystyrenes (PS) and alkyne functionalized poly(3- hexylthiophene)s (P3HT) via a copper(I) catalyzed Huisgen [3 + 2] dipolar cycloaddition reaction. The functionalized a-azido-PS homopolymer was prepared by atom transfer radical polymerization from a specifically designed initiator bearing the azide function, whereas ?-ethynyl-P3HT and a,?-pentynyl-P3HT were synthesized by a modified Grignard metathesis polymerization using alkynyl Grignard derivatives. The electronic environment of the alkynyl end groups was shown to be decisive in determining triazole ring formation.

Le prix de l'individualité. Maine de Brian, Samuel Taylor Coleridge et la volonté: Deux postétités distinctes

This thesis is concerned with Maine de Biran’s and Samuel Taylor Coleridge’s conceptions of will, and the way in which both thinkers’ posterities have been affected by the central role of these very conceptions in their respective bodies of thought. The research question that animates this work can therefore be divided into two main parts, one of which deals with will, while the other deals with its effects on posterity. In the first pages of the Introduction, I make the case for a comparison between two philosophers, and show how this comparison can bring one closer to truth, understood not in objective, but in subjective terms. I then justify my choice by underlining that, in spite of their many differences, Maine de Biran and Samuel Taylor Coleridge followed comparable paths, intellectually and spiritually, and came to similar conclusions concerning the essential activity of the human mind. Finally, I ask whether it is possible that this very focus on the human will may have contributed to the state of both thinkers’ works and of the reception of those works. This prologue is followed by five parts. In the first part, the similarities and differences between the two thinkers are explored further. In the second part, the connections between philosophy and singularity are examined, in order to show the ambivalence of the will as a foundation for truth. The third part is dedicated to the traditional division between subject and object in psychology, and its relevance in history and in moral philosophy. The fourth part tackles the complexity of the question of influence, with respect to both Maine de Biran’s and Coleridge’s cases, both thinkers being indebted to many philosophers of all times and places, and having to rely heavily on others for the publication, or the interpretation of their own works. The fifth part is concerned with the different aspects of the faculty of will, and primarily its relationship with interiority, as incommensurability, and actual, conditioned existence in a certain historical and spatial context. It ends with a return to the question of will and posterity and an announcement of what will be covered in the main body of the thesis. The main body is divided into three parts:‘L’émancipation’, ‘L’affirmation, and ‘La projection’. The first part is devoted to the way Maine de Biran and Samuel Taylor Coleridge extricated themselves from one epistemological paradigm to contribute to the foundation of another. It is divided in four chapters. The first chapter deals with the aforementioned change of paradigm, as corresponding to the emergence of two separate but associated movements, Romanticism and what the French philosopher refers to as ‘The Age of History’. The second chapter concerns the movement that preceded them, i.e. the Enlightenment, its main features according to both of our thinkers, and the two epistemological models that prevailed under it and influenced them heavily in their early years: Sensationism (Maine de Biran) and Associationism (Coleridge). The third chapter is about the probable influence of Immanuel Kant and his followers on Maine de Biran and Coleridge, and the various facts that allow us to claim originality for both thinkers’ works. In the fourth chapter, I contrast Maine de Biran and Coleridge with other movements and thinkers of their time, showing that, contrary to their respective thoughts, Maine de Biran and Coleridge could not but break free from the then prevailing systematic approach to truth. The second part of the thesis is concerned with the first part of its research question, namely, Maine de Biran’s and Coleridge’s conceptions of the will. It is divided into four chapters. The first chapter is a reflection on the will as a paradox: on the one hand, the will cannot be caused by any other phenomenon, or it is no longer a will; but it cannot be left purely undetermined, as if it is, it is then not different from chance. It thus needs, in order to be, to be contradictorily already moral. The second chapter is a comparison between Maine de Biran’s and Coleridge’s accounts of the origin of the will, where it is found that the French philosopher only observes that he has a will, whereas the English philosopher postulates the existence of this will. The comparison between Maine de Biran’s and Coleridge’s conceptions of the will is pursued in the third chapter, which tackles the question of the coincidence between the will and the self, in both thinkers’ works. It ends with the fourth chapter, which deals with the question of the relationship between the will and what is other to it, i.e. bodily sensations, passions and desires. The third part of the thesis focuses on the second part of its research question, namely the posterity of Maine de Biran’s and Coleridge’s works. It is divided into four chapters. The first chapter constitutes a continuation of the last chapter of the preceding part, in that that it deals with Maine de Biran’s and Coleridge’s relations to the ‘other’, and particularly their potential and actual audience, and with the way these relations may have affected their writing and publishing practices. The second chapter is a survey of both thinkers’ general reception, where it is found that, while Maine de Biran has been claimed by two important movements of thoughts as their initiator, Coleridge has been neglected by the only real movement he could have, or may indeed have pioneered. The third chapter is more directly concerned with the posterities of Maine de Biran’s and Coleridge’s conceptions of will, and attempts to show that the approach to, and the meaning of the will have evolved throughout the nineteenth century, and in the French Spiritualist and the British Idealist movements, from an essentially personal one to a more impersonal one. The fourth chapter is a partial conclusion, whose aim is to give a precise idea of where Maine de Biran and Coleridge stand, in relation to their century and to the philosophical movements and matters we are concerned with. The conclusion is a recapitulation of what has been found, with a particular emphasis on the dialogue initiated between Maine de Biran and Coleridge on the will, and the relation between will and posterity. It suggests that both thinkers have to pay the price of a problematic reception for the individuality that pervades their respective works, and goes further in suggesting that s/he who chooses to found his individuality on the will is bound to feel this incompleteness in his/her own personal life more acutely than s/he who does not. It ends with a reflection on fixedness and movement, as the two antagonistic states that the theoretician of the will paradoxically aspires to.

Facile synthesis of well-defined hydrophilic methacrylic macromonomers using ATRP and click chemistry

A range of well-defined hydrophilic methacrylic macromonomers has been synthesized by the judicious combination of atom transfer radical polymerization (ATRP) and copper-catalyzed 1,3-dipolar cycloaddition (azide-alkyne click chemistry). An azido a-functionalized ATRP initiator was used to produce well-defined homopolymers with terminal azide functionality via ATRP in protic media at 20 °C, with generally good control being achieved over both target molecular weight and final polydispersity (Mw/Mn = 1.10-1.35). Suitable methacrylic monomers include 2-aminoethyl methacrylate hydrochloride, 2-(diethylamino)ethyl methacrylate, 2-(dimethylamino)ethyl methacrylate, 2-hydroxyethyl methacrylate, 2-hydroxypropyl methacrylate, 2-(methacryloyloxy)ethyl phosphorylcholine, glycerol monomethacrylate, potassium 3-sulfopropyl methacrylate, and quaternized 2-(dimethylamino)ethyl methacrylate. These homopolymer precursors were then efficiently clicked using either propargyl methacrylate or propargyl acrylate to yield near-monodisperse (meth)acrylate-capped macromonomers with either cationic, anionic, nonionic, or zwitterionic character. Moreover, this generic route to well-defined hydrophilic macromonomers is also suitable for “one-pot” syntheses, as exemplified for 2-hydroxyethyl methacrylate and glycerol monomethacrylate-based macromonomers.

Compatibilisation and stabilisation of immiscible polymer blends by reactive processing

The main objectives of this research were to develop optimised chemical compositions and reactive processing conditions for grafting a functional monomer maleic anhydride (MA) in polypropylene (PP), ethylene propylene diene monomer (EPDM) and mixtures of PP-EPDM, and to optimise synthetic routes for production of PP/EPDM copolymers for the purpose of compatibilisation of PP/EPDM blends. The MA-functionalisation was achieved using an internal mixer in the presence of low concentrations (less than 0.01 molar ratio) of a free radical initiator. Various methods were used to purify MA-functionalised PP and the grafting yield was determined using either FTIR or titrametry. The grafting yield of MA alone, which due to its low free-radical reactivity towards polymer macroradicals, was accompanied by severe degradation in the case of PP and crosslinking for EPDM. In the case of MA-functionalised PP/EPDM, both degradation and crosslinking occurred though not to a great extent. The use of tri-functional coagents e.g. trimethylopropane triacrylates (TRIS) with MA, led to high improvement of the grafting yield of MA on the polymers. This is almost certainly due to high free-radical activity of TRIS leading to copolymerisation of MA and TRIS which was followed by grafting of the copolymer onto the polymer backbone. In the case of PP, the use of coagent was also found to reduce the polymer degradation. PP/EPDM copolymers with optimum tensile properties were synthesised using a 'one-step' continues reactive processing procedure. This was achieved firstly by functionalisation of a mixture of PP (higher w/w ratio) and EPDM (low w/w ratio) with MA, in the presence of the coagent TRIS and a small concentration of a free radical initiator. This was then followed by an imidisation reaction with the interlinking agent hexamethylene diamine (HEMDA). Small amount of copolymers, up to 5 phr, which were interlinked with up to 15 phr of HEMDA, were sufficient to compatibilise PP/EPDM75/25 blends resulting in excellent tensile properties compared to binary PP/EPDM 75/25 blend. Improvement in blend's compatibility and phases-stabilisation (observed through tensile and SEM analysis) was shown in all cases with significant interphases adhesion improvement between PP and EPDM, and reduction in domain size across the fractured surface indicating efficient distribution of the compatibiliser.

Studies in the anionic polymerization of methyl methacrylate

A study has been made of the anionic polymerization of methyl methacrylate using butyllithium and polystyryl lithium as initiators and using aluminium triisobutyl as a cocatalyst. The aspects of the polymerization that were examined were the effect of changing the order of addition of reagents, the temperature at which polymerization takes place and the polarity of the solvent. Trends were assessed in terms of molecular weight, molecular weight distribution and tacticity. In addition, a second monomer addition test was carried out to verify that the polymerization was truly a living one, and a kinetic study was attempted. Studies to investigate the effect of changing the order of addition of reagents showed that polymer with similar polydispersities and tacticities are produced whether the pre-mixing (mixing initiator and cocatalyst before addition of monomer) or the post-mixing (mixing monomer and cocatalyst before addition of initiator) method were used. However, polymerizations using the post-mixing mixing method demonstrated lower initiator efficiencies, possibly indicating a different initiating species. Investigations into the effect of changing the polymerization temperature show the molecular weight distribution to narrow as the temperature decreases, although a small amount of low molecular weight tailing was also observed at low temperature. A clear relationship between tacticity and temperature was observed with syndiotacticity increasing with decreasing temperature. Changes in solvent polarity were achieved by using mixtures of the standard solvent, toluene, with varying amounts of cyclohexane, tetrahydrofuran or dichloromethane. Experiments at low solvent polarity (using toluene/cyclohexane mixtures) showed problems with initiator solubility but produced polymer with lower polydispersity and higher syndiotacticity than in toluene alone. Experiments using toluene/THF mixtures yielded no polymer, thought to be owing to a side reaction between THF and aluminium triisobutyl. Increased solvent polarity, achieved using toluene/dichloromethane mixtures produced polymer with higher polydispersity and at lower yields than the conventional system, but also with higher syndiotacticity. Second monomer addition reactions demonstrated that the polymerization was 'living' since an increase in molecular weight was observed with no increase in polydispersity. Kinetic studies demonstrated the high speed of the polymerization but yielded no useful data.

Living cationic polymerization of isobutene

The polymerization of isobutene initiated by 1-chloro-1-phenylethane has been investigated, and molecular weight studies conducted using size exclusion chromatography. Polymerizations carried out in a 40/60 (v/v) mixture of dichloromethaneIcyclohexane, using titanium (IV) chloride as a catalyst in the presence of pyridine at -30 °C were found to be controlled and living. The number average molecular weights of the polymers increased linearly with monomer conversion, and the molecular weight distributions were between 1.15 and 1.20. Efficiencies of initiation were between 80 and 100%, and evidence was found to suggest that backbiting to the initiator had occurred, resulting in the formation of cyclic oligomers during the early stages of polymerization. The kinetics of polymerization can be explained in terms of active species in. equilibrium with dormant species. The effects of temperature. and dielectric constant on this equilibrium were studied and a model based upon the Fuoss equation was developed. Pyridine was found to behave as proton trap in the system, and when it was used in excess the rate of polymerization was retarded. By assuming that the catalyst and pyridine formed a one to one complex, it was possible to show that the reaction was second order with respect to the catalyst. The synthesis of low molecular weight polyisobutenes was studied. When the concentration of initiator was increased relative to that of the isobutene, such that the theoretical degree of polymerization was 20 or less, the rate of initiation was slow compared to propagation. The efficiency of initiation in these polymerizations was typically between 30 and 40 %. Optimal conditions of temperature. and.catalyst concentration were established, leading to a 60 % efficiency of initiation. A one-pot synthesis of phenol end-capped polyisobutene was attempted by adding phenol at the end of a living polymerization. Evidence to substantiate the existence of capped polymer chains in the resultant product was inconclusive. Block copolymerizations of oxetane and isobutene were conducted using 1-chloro-1phenylethane/TiCl4, but no copolymer or oxetane homopolymer could be isolated.

Living cationic polymerization of styrene monomers

This thesis describes an experimental investigation of synthesis of polystyrene under various polymerization conditions such as solvent polarity, temperature, initial concentrations of initiator, catalyst, monomer and added salts or co-catalyst, which was achieved using the living cationic polymerization technology in conjunction with gel permeation chromatography (GPC) and NMR spectroscopy. Polymerizations of styrene were conducted using 1-phenyl ethylchloride (1-PEC) as an initiator and tin tetrachloride (SnCI4) as a catalyst in the presence of tetra-n-Butylammonium chloride (nBu4NCI). Effects of solvent polarity varied by mixing dichloromethane (DCM) and less polar cyclohexane (C.hex), temperature, initial concentrations of SnC14, 1-PEC and nBu4NCI on the polymerizations were examined, and the conditions under which a living polymerization can be obtained were optimised as: [styrene]o ~ 0.75 - 2 M; [1-PEC]o ~ 0.005 - 0.05 M; [SnCI4Jo ~ 0.05 - 0.4 M; [nBu4NCIJo ~ 0.001 - 0.1 M; DCM/C.hex ~ 50/0 - 20/30 v/v; T ~ 0 to -45°C. Kinetic studies of styrene polymerization using the Omnifit sampling method showed that the number average molecular weight (Mn) of the polymers obtained increased in direct proportion to monomer conversion and agreed well with the theoretical Mn expected from the concentration ratios of monomer to initiator. The linearities of both the 1n([MJoI[M]) vs. time plot and the Mn vs. monomer conversion plot, and the narrow molecular weight distribution (MWD) measured using GPC demonstrated the livingness of the polymerizations, indicating the absence of irreversible termination and transfer within the lifetimes of the polymerizations. The proposed 'two species' propagation mechanism was found to apply for the styrene polymerization with 1-PEC/SnCI4 in the presence of nBu4NCl. The further kinetic experiments showed that living styrene polymerizations were achieved using the 1-PEC/SnCI4 initiating system in mixtures of DCM/C.hex 30/20 v/v at -15°C in the presence of various bromide salts, tetra-n-butylammonium bromide, tetra-n-pentylammonium bromide, tetra-n-heptylammonium bromide, and tetra-n-octylammonium bromide, respectively. The types of the bromide salts were found to have no significant effect on monomer conversion, Mn, polydispersity and initiation efficiency. Living polymerizations of styrene were also achieved using titanium tetrachloride (TiCI4) as a catalyst and 1-PEC as an initiator in the presence of a small amount of 2,6-di-tert-butylpyridine or pyridine instead of nBu4NCl. GPC analysis showed that the polymers obtained had narrow polydispersities (P.D. < 1.3), and the linearities of both the In([MJo/[MJ) vs. time plot and the Mn vs. monomer conversion plot demonstrated that the polymerizations are living, when the ratio of DCM and C.hex was less than 40 : 10 and the reaction temperature was not lower than -15°C. The reaction orders relative to TiCl4 and 1-PEC were estimated from the investigations into the rate of polymerization to be 2.56 and 1.0 respectively. lH and 13C NMR analysis of the resultant polystyrene would suggest the end-functionality of the product polymers is chlorine for all living polymerizations.

Atom transfer radical polymerisation - towards the synthesis of a fully-functional photorefractive polymer

Atom transfer radical polymerisation (ATRP) of styrene in xylene solution initiated with 1-phenylethyl bromide and mediated by CuBr/N-propyl-2- pyridinemethanimine catalyst complex was studied. The polymerisation was ill-controlled, yielding polymers with broad molecular weight distributions and values of number average molecular weight considerably higher than the theoretical values calculated from 100% initiator efficiency. The degree of control afforded over the polymerisation was enhanced by use of a more soluble catalyst complex, CuBr/N-octyl-2-pyridinemethanimine. Furthermore, the use of a more polar solvent, diglyme, generated a homogeneous catalyst complex that facilitated the production of polymers having narrow molecular weight distributions (1.10 < PDi < 1.20). The kinetics of the atom transfer radical polymerisation of methyl methacrylate at 90°C in diglyme solution initiated with ethyl-2-bromoisobutyrate and mediated by CuBr/N-octyl-2-pyridinemethanimine was studied and the orders of the reaction were established. The effect on the rate of polymerisation of the ratio of CuBr:N-octyl-2-pyridinemethanimine was also determined. The temperature dependencies of the rate of polymerisation of methyl methacrylate in diglyme solution and xylene solution were studied, and were found to be non-linear and dependent upon the polarity of the solvent. The use of highly polar aprotic solvents, such as N,N-dimethylformamide and dimethylsulphoxide, was found to be detrimental to the degree of control afforded over the polymerisation of methyl methacrylate. This was circumvented by use of a 5-fold excess, over that conventionally used, of catalyst complex. The atom transfer radical polymerisation of (4-nitrophenyl)-[3-[N-[2- (methacryloyloxy)ethyl]carbazolyl]]diazene in dimethyl sulphoxide solution was studied. Although homopolymerisation yielded only oligomers, copolymerisation of this monomer with methyl methacrylate was found to be readily achievable. Keywords: ATRP, Styrene; Methyl methacrylate; Polar solvents; Fully-functional photorefractive polymer. 2

The synthesis of biodegradable polymers using aluminium alkoxide initiators

Alkyl aluminium alkoxides have been used as initiators for the ring opening polymerisation of ε-caprolactone and δ-valerolactone. The effect of the reaction solvent on the kinetics of the polymerisation of ε-caprolactone has been studied. The rate of polymerisation was found to be faster in solvents of lower polarity and donor nature such as toluene. In general solvents of higher polarity resulted in a decreased rate of polymerisation. However solvents such as THF or DMF with a lone pair of electrons capable of forming a complex with the aluminium centre slowed the polymerisation further. The size of the monomer also proved to be an important factor in the kinetics of the reaction. The six membered ring, δ-valerolactone has less ring strain than the seven membered ring ε-caprolactone and thus the polymerisation of δ-valerolactone is slower than the corresponding polymerisation of ε-caprolactone. Both the alkoxide and alkyl group structures have an effect on the polymerisation. In general bulkier alkoxide groups provide greater steric hindrance around the active site at the beginning of the reaction. This causes an induction or a build up period that is related to the both the steric hindrance and also the electronic effects provided by the alkoxide group. The alkyl group structure has an effect throughout the polymerisation because it remains adjacent to the active centre. The number of alkoxide groups on the aluminium centre is also important, using a dialkoxide as an initiator yields polymers with molecular weights approximately half that of the corresponding reactions using a mono alkoxide. Transesterification reactions have also been found to occur after most of the monomer has been consumed. These transesterification reactions are exaggerated as temperature increases. A method of producing tri-block co-polymers has also been developed. A di-hydroxy functional pre-polymer, PHBV, was reacted with an aluminium alkyl to form a di-alkoxide macroinitiator which was subsequently used as an initiator for the polymerisation of ε-caprolactone to form an ABA type tri-block co-polymer. The molecular weight and other properties were predictable from the initial monomer/initiator ratios.

The synthesis of novel biodegradable polyesters and copolyesters from anhydrosulfites

This thesis was concerned primarily with the synthesis and the ring-opening polymerisation of anhydrosulfites (1,3,2-dioxa-thiolan-4-one-2-oxides), and secondly with the copolymerisation of anhydrosulfites with -caprolactone. The polyesters and copolyesters synthesised are of considerable interest in medical applications and also for use as environmental friendly packaging. A range of anhydrosulfites were prepared according to an established method. Aliphatic anhydrosulfites were obtained with a level of purity satisfactory for polymerisation whereas aromatic anhydrosulfites decomposed during distillation and purification by chromatographic techniques. Aliphatic anhydrosulfites with a substituent, such as methyl, isopropyl, n-butyl and isobutyl were studied by NMR spectroscopy. Analysis of these spectra revealed that the five-membered anhydrosulfite ring was puckered and that when the substituent was bulky, rotations about the alkyl chains were restricted. A wide range of anionic initiators may be used to initiate anhydrosulfites. Lithium alkyls turned out to be more successful than alkali metal alkoxides and amides. The molecular weights were found to depend on the basicity of the initiator, the monomer-to-initiator ratio, the nature of the solvent and the polymerisation temperature. The molecular weight M0 of poly(L-lactic acid) ranged from (0.5 to 6)x104. Highly crystalline and purely isotactic poly(lactic acid) was synthesised from L-lactic acid anhydrosulfite (L-LAAS) whereas DL-LAAS led to an amorphous polymer with randomly distributed D-and L-lactic units. This indicated that this polymerisation was not stereoselective. However, the bulkiness of the substituent in the anhydrosulfites molecule was found to influence the stereoselectivity of the polymerisation, thus polyesters with isobutyl or n-butyl pendant group were preferentially isotactic. Block-copolymers of ε-caprolactone and several anhydrosulfites were successfully produced. Block-copolymers of LAAS with ε-caprolactone were also synthesised, but the incorporation of caprolactone units was rather small. In contrast, random copolymerisation of LAAS and ε-caprolactone led to polymers with blocky structures similar to those obtained in the block-copolymerisation of LAAS with  ε-caprolactone.

Synthesis and characterisation of vinyl block copolymers

A study has been made of the anionic polymerisation of methyl methacrylate using butyllithium and polystyryl lithium as initiators and the effects of lithium chloride and aluminium alkyls on the molecular weight and molecular weight distributions. Diblock copolymers of styrene-b-methyl methacrylate were synthesised at -78oC in THF in the presence of lithium chloride, and at ambient temperatures in toluene in the presence of aluminium alkyls. Studies in the presence of lithium chloride showed that the polymerisation was difficult to control; there was no conclusive evidence of a living system and the polydispersity indices were between 1.5 and 3. However, using relatively apolar solvents, in the presence of aluminium alkyls, homopolymerisation of methyl methacrylate showed characteristics of a living polymerisation. An investigation of the effects of the structures of the lithium and aluminium alkyls on the efficiency of initiation showed that a t-butyllithium/triisobutylaluminium initiating system exhibited an efficiency of 80%, compared with lower efficiencies (typically 30%) for systems based on butyllithium/triethylaluminium.The polydispersity index was found to decrease from ∼2.2 to ∼1.5 when butyllithium was replaced by t-butyllithium. The efficiency of the initiator was found to be solely dependent on the size of the alkyl group of the aluminium component, whereas the polydispersity index was found to be solely dependent on the size of the alkyl group on the lithium component. The aluminium alkyl is thought to be co-ordinated to the ester carbonyl groups of both the monomer and polymer. There is a critical degree of polymerisation, at which point the rate of polymerisation decreases, which probably relates to a change in structure of the active chain end. Characterisation of poly(styrene )-b-poly(4-vinylpyridine) and poly(styrene)-b-poly(4-vinylpyridine methyl iodide) diblock copolymers using static light scattering techniques, showed the formation of star-shaped 'reverse' micelles when placed in toluene. Temperature effects on micellization behaviour are only exhibited for the unquaternised micelles, which showed characterisically lower aggregation numbers than their quaternised counterparts. A suitable solvent was not obtained for characterisation of the styrene-b-methyl methacrylate diblock copolymers synthesized.

The chemical modification of polymer blends by reactive processing

The primary objective of this research was to examine the concepts of the chemical modification of polymer blends by reactive processing using interlinking agents (multi-functional, activated vinyl compounds; trimethylolpropane triacrylates {TRIS} and divinylbenzene {DVD}) to target in-situ interpolymer formation between immiscible polymers in PS/EPDM blends via peroxide-initiated free radical reactions during melt mixing. From a comprehensive survey of previous studies of compatibility enhancement in polystyrene blends, it was recognised that reactive processing offers opportunities for technological success that have not yet been fully realised; learning from this study is expected to assist in the development and application of this potential. In an experimental-scale operation for the simultaneous melt blending and reactive processing of both polymers, involving manual injection of precise reactive agent/free radical initiator mixtures directly into molten polymer within an internal mixer, torque changes were distinct, quantifiable and rationalised by ongoing physical and chemical effects. EPDM content of PS/EPDM blends was the prime determinant of torque increases on addition of TRIS, itself liable to self-polymerisation at high additions, with little indication of PS reaction in initial reactively processed blends with TRIS, though blend compatibility, from visual assessment of morphology by SEM, was nevertheless improved. Suitable operating windows were defined for the optimisation of reactive blending, for use once routes to encourage PS reaction could be identified. The effectiveness of PS modification by reactive processing with interlinking agents was increased by the selection of process conditions to target specific reaction routes, assessed by spectroscopy (FT-IR and NMR) and thermal analysis (DSC) coupled dichloromethane extraction and fractionation of PS. Initiator concentration was crucial in balancing desired PS modification and interlinking agent self-polymerisation, most particularly with TRIS. Pre-addition of initiator to PS was beneficial in the enhancement of TRIS binding to PS and minimisation of modifier polymerisation; believed to arise from direct formation of polystyryl radicals for addition to active unsaturation in TRIS. DVB was found to be a "compatible" modifier for PS, but its efficacy was not quantified. Application of routes for PS reaction in PS/EPDM blends was successful for in-situ formation of interpolymer (shown by sequential solvent extraction combined with FT-IR and DSC analysis); the predominant outcome depending on the degree of reaction of each component, with optimum "between-phase" interpolymer formed under conditions selected for equalisation of differing component reactivities and avoidance of competitive processes. This was achieved for combined addition of TRIS+DVB at optimum initiator concentrations with initiator pre-addition to PS. Improvements in blend compatibility (by tensiles, SEM and thermal analysis) were shown in all cases with significant interpolymer formation, though physical benefits were not; morphology and other reactive effects were also important factors. Interpolymer from specific "between-phase" reaction of blend components and interlinking agent was vital for the realisation of positive performance on compatibilisation by the chemical modification of polymer blends by reactive processing.

The mechanochemical modification of polyolefins using reactive modifier systems

The principal objective of this work was to improve the mechanical properties of glass fibre reinforced polypropylene (PP) composites by the mechanochemical modification of the PP. The modification of the PP was carried out by reactive processing of the PP with a modifier in a Buss Ko-Kneader. Two main types of modifier were evaluated one type based on N-substituted maleimides the others based on 2-allylamino-4,6-dichloro-1,3,5-triazine (ACCT). The modification of the PP was carried out in two stages. Firstly the PP was reactively processed with the modifier and a free radical initiator. The objective of this stage was to bind the modifier to the PP. In the second stage the modified PP was reactively processed with the glass fibre. The objective in this stage was to form a chemical bond between the bound modifier and the silane coupling agent on the surface of the glass. Two silane coupling agents were evaluated these had a aliphatic chloro group and an aliphatic amino group respectively available for reaction with the modifier. The modifiers synthesised for this work had two main functional groups. The first was a double bond for free radical addition to the PP. The second was an organic group chosen for its potential reactivity to the silane coupling agent. A preliminary investigation was carried out using maleic anhydride (MA) as the modifier, this is reactive to the amino silane coupled glass. Studies of a commercially available system were also carried out for comparison purposes. During the work it was found that the amino silane coupled glass fibres produced, without any modification being made to the PP, mechanical properties comparable to the commercial system. Further any modification added to the amino silane system failed to improve the mechanical performance and in some cases acted in the opposite fashion. This failure was evident even when a chemical bond between glass fibre and PP could be shown. In the case of the chloro silane coupled glass fibres the mechanical properties of the composite without modification were poorer than those of the commercial system. It was found that the mechanical properties of these systems could be enhanced by the modifiers, however, no system tested significantly out performed the commercial system. Of the two modifier systems tested those based on the n-substituted maleimides were more successful at enhancing mechanical properties than those based on ACCT. This was attributed to the Poor chemical binding of the ACCT based modifiers to the PP. During the work it was found that several of the modifiers improved the properties of the PP when no glass fibres were present, particularly the % elongation and impact strength. It is possible that these modifiers could be used to improve the impact performance of PP, this may be of particular interest in recycling. These modifiers have only been tested for improving the properties of glass fibre composites. The N-substituted maleimide based modifiers could be used as compatibleisers for alloys of PP and other polymers. These could function by the formation of the bond with PP via the double bond whilst the group attached to the nitrogen atom could react with the alloying polymer.