Degradation and stabilisation of diisocyanate cured polybutadiene

Hydroxyl terminated polybutadiene (HTPB) has been used as a rocket propellant binder which is required to be stored for at least twenty years. It is found that the excellent stress-strain characteristics of this propellant can be totally lost, during this long storage, due to the deterioration of the polybutadiene chains. As a result, the propellant can not stand the service loads, which may lead to a catastrophe. The study of the HTPB binder degradation, below 80°C, has been carried out by investigating the environmental factors and the changes which occur along the macromolecular chains. Results have shown that oxygen is the main factor which causes the crosslinking and chain scission reactions. The former is the predominant reaction and proceeds rapidly under oxygen sufficient environment. The unsaturation of polymer chain, which provides the desired physical properties to the binder, was lost with the increase in crosslink density. At the same time hydroperoxides were found to form and decompose along the polymer chains. Therefore, the deterioration of the binder results from the oxidation of polymer chains. Since the oxidation reaction occurred at higher rate than oxygen diffusion rate and oxygen diffusion rate is inversely proportional to the crosslink density, the binder, below the surface layer in a thick section container, could be naturally protected under an oxygen deficient condition for a long time. Investigation of the effectiveness of antioxidants in HTPB binder has shown that the efficiency of an antioxidant depends on its ability to scavenge radicals. Generally, aromatic amines are the most effective binder antioxidants. But when a peroxide decomposer is combined with an aromatic amine at the appropriate ratio, a synergistic effect is obtained, which gives the lowest binder gel increase rate.

Compatibilisation and stabilisation of immiscible polymer blends by reactive processing

The main objectives of this research were to develop optimised chemical compositions and reactive processing conditions for grafting a functional monomer maleic anhydride (MA) in polypropylene (PP), ethylene propylene diene monomer (EPDM) and mixtures of PP-EPDM, and to optimise synthetic routes for production of PP/EPDM copolymers for the purpose of compatibilisation of PP/EPDM blends. The MA-functionalisation was achieved using an internal mixer in the presence of low concentrations (less than 0.01 molar ratio) of a free radical initiator. Various methods were used to purify MA-functionalised PP and the grafting yield was determined using either FTIR or titrametry. The grafting yield of MA alone, which due to its low free-radical reactivity towards polymer macroradicals, was accompanied by severe degradation in the case of PP and crosslinking for EPDM. In the case of MA-functionalised PP/EPDM, both degradation and crosslinking occurred though not to a great extent. The use of tri-functional coagents e.g. trimethylopropane triacrylates (TRIS) with MA, led to high improvement of the grafting yield of MA on the polymers. This is almost certainly due to high free-radical activity of TRIS leading to copolymerisation of MA and TRIS which was followed by grafting of the copolymer onto the polymer backbone. In the case of PP, the use of coagent was also found to reduce the polymer degradation. PP/EPDM copolymers with optimum tensile properties were synthesised using a 'one-step' continues reactive processing procedure. This was achieved firstly by functionalisation of a mixture of PP (higher w/w ratio) and EPDM (low w/w ratio) with MA, in the presence of the coagent TRIS and a small concentration of a free radical initiator. This was then followed by an imidisation reaction with the interlinking agent hexamethylene diamine (HEMDA). Small amount of copolymers, up to 5 phr, which were interlinked with up to 15 phr of HEMDA, were sufficient to compatibilise PP/EPDM75/25 blends resulting in excellent tensile properties compared to binary PP/EPDM 75/25 blend. Improvement in blend's compatibility and phases-stabilisation (observed through tensile and SEM analysis) was shown in all cases with significant interphases adhesion improvement between PP and EPDM, and reduction in domain size across the fractured surface indicating efficient distribution of the compatibiliser.

Stabilisation of isocyanate cross linked polybutadiene binder

Isocyanate cross-linked hydroxy terminated polybutadiene is used as a binder for solid rocket propellant. Rocket motors containing this propellant require a storage life of at least 20 years. During storage it has been found that the important rubbery properties of the binder can be lost due to oxidative cross-linking of the polybutadiene chains. This could cause catastrophic failure when the rocket motor is required. At present the bis-hindered phenol Calco 2246 is used as a thermal oxidative stabiliser, but it's performance is only adequate. This has led to the search for a more efficient stabiliser system. To hasten the evaluation of new antioxidant systems the use of dynamic thermal analysis was investigated. Results showed that a tentative relationship existed between predictions by thermal analysis and the long term oven ageing for simple single antioxidant systems. But for more complex systems containing either autosynergistic or mixed antioxidants no relationship was observed suggesting that results for such an "accelerated" technique cannot be used for the purpose of extrapolation for long term performance. This was attributed to the short time and more aggressive condition used (hjgher temperature and oxygen rich atmosphere in thermal analysis) altering the mechanism of action of the antioxidants and not allowing time for co-operative effect of the combined antioxidant system to form. One potential problem for the binder system is the use of an diisocyanate as a cross-linking agent. This reacts with the hydroxyl hydrogen on the polymer as well as other active hydrogens such as those contained in a number of antioxidants, affecting both cross-linking and antioxidant effectiveness. Studies in this work showed that only antioxidants containing amine moieties have a significant affect on binder preparation, with the phenolic antioxidants not reacting. This is due to the greater nucleophilicity of the amines. Investigation of a range of antioxidant systems, including potentially homo, hetero and autosynergistic systems, has highlighted a number of systems which show considerably greater effectiveness than the currently used antioxidant Calco 2246. The only single antioxidant which showed improvement was the partially unhindered phenol y-Tocopherol. Of the mixed systems combinations of the sulphur containing antioxidants e.g. DLTP with higher levels of chain-breaking antioxidants, especially Calco 2246, were the most promising. Also the homosynergistic mix of an aromatic amine and a phenol was seen to be very effective but the results were inconsistent. This inconsistency could be explained by the method of sample preparation used. It was shown that the efficiency of a number of antioxidant.s could be dramatically improved by the use of ultrasound during the mixing stage of preparation. The reason for this increase in performance is unclear but in the case of the homosynergistic amine/phenol mix both more efficient mixing and/or the production of a novel mechanism of action are suggested

Compatibilisation of heterogeneous polymer blends by reactive processing

Functionalisation of polystyrene, PS, and ethylene-co-propylene-co-cyclopentadiene terpolymer, EPDM, with acrylic acid, AA, in a melt reactive processing procedure, in the presence of peroxide, trigonox 101, and coagents, Divinyl benzene, DVB (for PS), and trimethylolpropane triacrylate, TRIS (for EPDM), were successfully carried out. The level of grafting of the AA, as determined by infrared analysis, was significantly enhanced by the coagents. The grafting reaction of AA takes place simultaneously with homopolymerisation of the monomers, melt degradation and crosslinking reactions of the polymers. The extent of these competing reactions were inferred from measurements of melt flow index and insoluble gel content. Through a judicious use of both the peroxide and the coagent, particularly TRIS, unwanted side reactions were minimized. Five different processing methods were investigated for both functionalisation experiments; the direct addition of the pre-mixed polymer with peroxide and reactive modifiers was found to give optimum condition for grafting. The functionalised PS, F-PS, and EPDM, F-EPD, and maleinised polypropylene carrying a potential antioxidant, N-(4-anilinophenyl maleimide), F-PP were melt blended in binary mixtures of F-PS/F-EPD and F-PP/F-EPD in the presence (or absence) of organic diamines which act as an interlinking agent, e.g, Ethylene Diamine, EDA, and Hexamethylene Diamine, HEMDA. The presence of an interlinking agent, particularly HEMDA shows significant enhancement in the mechanical properties of the blend, suggesting that the copolymer formed has acted as compatibiliser to the otherwise incompatible polymer pairs. The functionalised and amidised blends, F and A-PSIEPDM (SPOI) and F and A-PPIEPDM (SPD2) were subsequently used as compatibiliser concentrates in the corresponding PSIEPDM and PPIEPDM blends containing various weight propotion of the homopolymers. The SPD1 caused general decreased in tensile strength, albeit increased in drop impact strength particularly in blend containing high PS content (80%). The SPD2 was particularly effective in enhancing impact strength in blends containing low weight ratio of PP (<70%). The SPD2 was also a good thermal antioxidant albeit less effective than commercial antioxidant. In all blends the evidence of compatibility was examined by scanning electron microscopy.