Modification of the B2-type matrix of aluminide diffusion coatings on nickel-base superalloys-bulk aluminide analogues

Pack aluminide coating is a useful method for conferring oxidation resistance on nickel-base superalloys. Nominally, these coatings have a matrix composed of a Ni-Al based B2-type phase (commonly denoted as Β). However, following high-temperature exposure in oxidative envi-ronments, aluminum is depleted from the coating. Aluminum depletion in turn, leads to de-stabilization of the Β phase, resulting in the formation of a characteristic lathlike Β-derivative microstructure. This article presents a transmission electron microscopy study of the formation of the lathlike Β-derivative microstructure using bulk nickel aluminides as model alloys. In the bulk nickel aluminides, the lathlike microstructure has been found to correspond to two distinct components: L10-type martensite and a new Β derivative. The new Β derivative is characterized and the conditions associated with the presence of this feature are identified and compared with those leading to the formation of the L10 martensitic phase. © 1995 The Minerals, Metals & Material Society.

Decomposition of the B2-type matrix

The microstructural stability of aluminide diffusion coatings, prepared by means of a two-stage pack-aluminization treatment on single-crystal nickel-base superalloy substrates, is considered in this article. Edge-on specimens of coated superalloy are studied using transmission electron microscopy (TEM). The effects of coating thickness and post-coating heat treatment (duration, temperature, and atmosphere) on coating microstructure are examined. The article discusses the partial transformation of the matrix of the coating, from a B2-type phase (nominally NiAl) to a L12 phase (nominally Ni3(Al, Ti)), during exposure at temperatures of 850 °C and 950 °C in air and in vacuum for up to 138 hours. Three possible processes that can account for decom- position of the coating matrix are investigated, namely, interdiffusion between the coating and the substrate, oxidation of the coating surface, and aging of the coating. Of these processes, aging of the coating is shown to be the predominant factor in the coating transformation under the conditions considered. © 1992 The Minerals, Metals and Materials Society, and ASM International.