Graphene layers have been produced from multi-walled carbon nanotube (MWCNT) bulk materials by friction when polished on ground-glass, offering a novel and effective method to produce graphene layers, which, more importantly, could be transferred to other substrates by rubbing. Field emission scanning electron microscopy, Raman spectroscopy, atomic force microscopy, transmission electron microscopy and selected area electron diffraction confirmed the formation of graphene layers. They were thought to be peeled away from the MWCNT walls due to friction. The reflection spectra showed that absorption of as-produced graphene layers decreased with wavelength in the range of 250–400 nm, compared to the MWCNT bulk material having strong absorption at 350 nm. Nanoscratch test was used to determine the mechanical properties of graphene films, suggesting the tolerance of as-produced graphene film to flaws introduced by scratch.

Transport properties of hot-pressed bulk carbon nanotubes compacted by spark plasma sintering

Electrical and thermal transport properties of the carbon nanotube bulk material compacted by spark plasma sintering have been investigated. The electrical conductivity of the as-prepared sample shows a lnT dependence from 4 to 50 K, after which the conductivity begins to increase approximately linearly with temperature. A magnetic field applied perpendicularly to the sample increases the electrical conductivity in the range of 0-8T at all testing temperatures, indicating that the sample possesses the two-dimensional weak localization at lower temperatures (?50 K), while behaviors like a semimetal at higher temperatures (?50 K). This material acts like a uniform compact consisting of randomly distributed two dimensional graphene layers. For the same material, the thermal conductivity is found to decrease almost linearly with decreasing temperature, similar to that of a single multi-walled carbon nanotube. Magnetic fields applied perpendicularly to the sample cause the thermal conductivity to decrease significantly, but the influence of the magnetic fields becomes weak when temperature increases.