Transglutaminase mediated grafting of silk proteins onto wool fabrics leading to improved physical and mechanical properties

Transglutaminases have the ability to incorporate primary amines and to graft peptides (containing glutamine or lysine residues) into proteins. These properties enable transglutaminases to be used in the grafting of a range of compounds including peptides and/or proteins onto wool fibres, altering their functionality. In this paper we investigated the transglutaminase mediated grafting of silk proteins into wool and its effect on wool properties. A commercial hydrolysed silk preparation was compared with silk sericin. The silk sericin protein was labelled with a fluorescent probe which was used to demonstrate the efficiency of the TGase grafting of such proteins into wool fibres. The TGase mediated grafting of these proteins led to a significant effect on the properties of wool yarn and fabric, resulting in increased bursting strength, as well as reduced levels of felting shrinkage and improved fabric softness. Also observed was an accumulation of deposits on the surface of the treated wool fibres when monitored by SEM and alterations in the thermal behaviour of the modified fibres, in particular for mTGase/sericin treated fibres which, with the confocal studies, corroborate the physical changes observed on the treated wool fabric. © 2006 Elsevier Inc. All rights reserved.

Reactive processing of polymers: structural characterization of products by 1H and 13C NMR spectroscopy for glycidyl methacrylate grafting onto EPR in the absence and presence of a reactive comonomer

Grafted GMA on EPR samples were prepared in a Thermo-Haake internal mixer by free radical melt grafting reactions in the absence (conventional system; EPR-g-GMA(CONV)) and presence of the reactive comonomer divinyl benzene, DVB (EPR-g-GMA(DVB)). The GMA-homopolymer (poly-GMA), a major side reaction product in the conventional system, was almost completely absent in the DVB-containing system, the latter also resulted in a much higher level of GMA grafting. A comprehensive microstructure analysis of the formed poly-GMA was performed based on one-dimensional H-1 and C-13 NMR spectroscopy and the complete spectral assignments were supported by two-dimensional NMR techniques based on long range two and three bond order carbon-proton couplings from HMBC (Heteronuclear Multiple Bond Coherence) and that of one bond carbon-proton couplings from HSQC (Heteronuclear Single Quantum Coherence), as well as the use of Distortionless Enhancement by Polarization Transfer (DEPT) NMR spectroscopy. The unambiguous analysis of the stereochemical configuration of poly-GMA was further used to help understand the microstructures of the GMA-grafts obtained in the two different free radical melt grafting reactions, the conventional and comonomer-containing systems. In the grafted GMA, in the conventional system (EPR-g-GMA(CONV)), the methylene protons of the GMA were found to be sensitive to tetrad configurational sequences and the results showed that 56% of the GMA sequence in the graft is in atactic configuration and 42% is in syndiotactic configuration whereas the poly-GMA was predominantly syndiotactic. The differences in the microstructures of the graft in the conventional EPR-g-GMA(CONV) and the DVB-containing (EPR-g-GMA(DVB)) systems is also reported (C) 2009 Elsevier Ltd. All rights reserved.

Reactive processing of polymers:effect of bifunctional and tri-functional comonomers on melt grafting of glycidyl methacrylate onto polypropylene

Two reactive comonomers, divinyl benzene (DVB) and trimethylolpropane triacrylate (TRIS), were evaluated for their role in effecting the melt free radical grafting reaction of the monomer glycidyl methacrylate (GMA) onto polypropylene (PP). The characteristics of the GMA-grafting systems in the presence and absence of DVB or TRIS were examined and compared in terms of the yield of the grafting reaction and the extent of the main side reactions, namely homopolymerisation of GMA (poly-GMA) and polymer degradation, using different chemical compositions of the reactive systems and processing conditions. In the absence of the comonomers, i.e. in a conventional system, high initiator concentrations of peroxides were typically required to achieve the highest possible GMA grafting levels which were found to be generally low. Concomitantly, both poly-GMA and degradation of the polymer by chain scission takes place with increasing initiator amounts. On the other hand, the presence of a small amount of the comonomers, DVB or Tris, in the GMA-grafting system, was shown to bring about a significant increase in the grafting level paralleled by a large reduction in poly-GMA and PP degradation. In the presence of these highly reactive comonomers, the optimum grafting system requires a much lower concentration of the peroxide initiator and, consequently, would lead to the much lower degree of polymer degradation observed in these systems. The differences in the effects of the presence of DVB and that of TRIS in the grafting systems on the rate of the GMA-grafting and homopolymerisation reactions, and the extent of PP degradation (through melt flow changes), were compared and contrasted with a conventional GMA-grafting system.

Reactive processing of polymers:melt grafting of glycidyl methacrylate on ethylene propylene copolymer in the presence of a coagent

Glycidyl methacrylate (GMA) was grafted on ethylene-propylene copolymer during melt processing with peroxide initiation in the presence and absence of a more reactive comonomer (coagent), trimethylolpropane triacrylate (Tris). The characteristics of the grafting systems in terms of the grafting reaction yield and the nature and extent of the competing side reactions were examined. The homopolymers of GMA (Poly-GMA) and Tris (Poly-Tris) and the GMA-Tris copolymer (GMA-co-Tris) were synthesized and characterized. In the absence of the coagent, high levels of poly-GMA, which constituted the major competing reaction, was formed, giving rise to low GMA grafting levels. Further, this grafting system resulted in a high extent of gel formation and polymer crosslinking due to the high levels of peroxide needed to achieve optimum GMA grafting and a consequent large drop in the melt index (increased viscosity) of the polymer. In the presence of the coagent, however, the grafting system required much lower peroxide concentration, by almost an order of magnitude, to achieve the optimum grafting yield. The coagent-containing GMA-grafting system has also resulted in a drastic reduction in the extent of all competing reactions, and in particular, the GMA homopolymerization, leading to improved GMA grafting efficiency with no detectable gel or crosslinking. The mechanisms of the grafting reactions, in the presence and absence of Tris, are proposed.

Hydrothermal saline promoted grafting:a route to sulfonic acid SBA-15 silica with ultra-high acid site loading for biodiesel synthesis

A simple grafting protocol is reported which affords a ten-fold enhancement in acid site density of mesoporous sulfonic acid silicas compared to conventional syntheses, offering improved process efficiency and new opportunities for tailored supported solid acids in sustainable chemistry. This journal is

Hydrothermal saline promoted grafting of periodic mesoporous organic sulfonic acid silicas for sustainable FAME production

Hydrothermal saline promoted grafting of sulfonic acid groups onto SBA-15 and periodic mesoporous organic silica analogues affords solid acid catalysts with high acid site loadings (>2.5 mmol g-1 H+), ordered mesoporosity and tunable hydrophobicity. The resulting catalysts show excellent activity for fatty acid esterification and tripalmitin transesterification to methyl palmitate, with framework phenyl groups promoting fatty acid methyl esters production. (Chemical Equation Presented)

Grafting functional antioxidants on highly crosslinked polyethylene

The problem of interference of antioxidants, such as hindered phenols, with peroxide-initiated crosslinking of polyethylene was addressed through the use of functional (reactive) graftable antioxidants (g-AO). Reactive derivatives of hindered phenol and hindered amine antioxidants were synthesised, characterised and used to investigate their grafting reactions in high density polyethylene; both non-crosslinked (PE) and highly peroxide-crosslinked (PEXa). Assessment of the extent of in-situ grafting of the antioxidants, their retention after exhaustive solvent extraction in PE and PEXa, and the stabilising performance of the grafted antioxidants (g-AO) in the polymer were examined and benchmarked against conventionally stabilised crosslinked & non-crosslinked polyethylene. It was shown that the functional antioxidants graft to a high extent in PEXa, and that the level of interference of the g-AOs with the polymer crosslinking process was minimal compared to that of conventional antioxidants which bear the same antioxidant function. The much higher level of retention of the g-AOs in PEXa after exhaustive solvent extraction, compared to that of the corresponding conventional antioxidants, accounts for their superior long-term thermal stabilising performance under severe extractive conditions.

Compatibilisation and stabilisation of immiscible polymer blends by reactive processing

The main objectives of this research were to develop optimised chemical compositions and reactive processing conditions for grafting a functional monomer maleic anhydride (MA) in polypropylene (PP), ethylene propylene diene monomer (EPDM) and mixtures of PP-EPDM, and to optimise synthetic routes for production of PP/EPDM copolymers for the purpose of compatibilisation of PP/EPDM blends. The MA-functionalisation was achieved using an internal mixer in the presence of low concentrations (less than 0.01 molar ratio) of a free radical initiator. Various methods were used to purify MA-functionalised PP and the grafting yield was determined using either FTIR or titrametry. The grafting yield of MA alone, which due to its low free-radical reactivity towards polymer macroradicals, was accompanied by severe degradation in the case of PP and crosslinking for EPDM. In the case of MA-functionalised PP/EPDM, both degradation and crosslinking occurred though not to a great extent. The use of tri-functional coagents e.g. trimethylopropane triacrylates (TRIS) with MA, led to high improvement of the grafting yield of MA on the polymers. This is almost certainly due to high free-radical activity of TRIS leading to copolymerisation of MA and TRIS which was followed by grafting of the copolymer onto the polymer backbone. In the case of PP, the use of coagent was also found to reduce the polymer degradation. PP/EPDM copolymers with optimum tensile properties were synthesised using a 'one-step' continues reactive processing procedure. This was achieved firstly by functionalisation of a mixture of PP (higher w/w ratio) and EPDM (low w/w ratio) with MA, in the presence of the coagent TRIS and a small concentration of a free radical initiator. This was then followed by an imidisation reaction with the interlinking agent hexamethylene diamine (HEMDA). Small amount of copolymers, up to 5 phr, which were interlinked with up to 15 phr of HEMDA, were sufficient to compatibilise PP/EPDM75/25 blends resulting in excellent tensile properties compared to binary PP/EPDM 75/25 blend. Improvement in blend's compatibility and phases-stabilisation (observed through tensile and SEM analysis) was shown in all cases with significant interphases adhesion improvement between PP and EPDM, and reduction in domain size across the fractured surface indicating efficient distribution of the compatibiliser.

Flow field analysis of some mixing and conveying screw element regions, within a closely intermeshing, co-rotating twin-screw extruder.

Grafting of antioxidants and other modifiers onto polymers by reactive extrusion, has been performed successfully by the Polymer Processing and Performance Group at Aston University. Traditionally the optimum conditions for the grafting process have been established within a Brabender internal mixer. Transfer of this batch process to a continuous processor, such as an extruder, has, typically, been empirical. To have more confidence in the success of direct transfer of the process requires knowledge of, and comparison between, residence times, mixing intensities, shear rates and flow regimes in the internal mixer and in the continuous processor.The continuous processor chosen for the current work in the closely intermeshing, co-rotating twin-screw extruder (CICo-TSE). CICo-TSEs contain screw elements that convey material with a self-wiping action and are widely used for polymer compounding and blending. Of the different mixing modules contained within the CICo-TSE, the trilobal elements, which impose intensive mixing, and the mixing discs, which impose extensive mixing, are of importance when establishing the intensity of mixing. In this thesis, the flow patterns within the various regions of the single-flighted conveying screw elements and within both the trilobal element and mixing disc zones of a Betol BTS40 CICo-TSE, have been modelled using the computational fluid dynamics package Polyflow. A major obstacle encountered when solving the flow problem within all of these sets of elements, arises from both the complex geometry and the time-dependent flow boundaries as the elements rotate about their fixed axes. Simulation of the time dependent boundaries was overcome by selecting a number of sequential 2D and 3D geometries, used to represent partial mixing cycles. The flow fields were simulated using the ideal rheological properties of polypropylene and characterised in terms of velocity vectors, shear stresses generated and a parameter known as the mixing efficiency. The majority of the large 3D simulations were performed on the Cray J90 supercomputer situated at the Rutherford-Appleton laboratories, with pre- and postprocessing operations achieved via a Silicon Graphics Indy workstation. A mechanical model was constructed consisting of various CICo-TSE elements rotating within a transparent outer barrel. A technique has been developed using coloured viscous clays whereby the flow patterns and mixing characteristics within the CICo-TSE may be visualised. In order to test and verify the simulated predictions, the patterns observed within the mechanical model were compared with the flow patterns predicted by the computational model. The flow patterns within the single-flighted conveying screw elements in particular, showed good agreement between the experimental and simulated results.

Reactive processing methods for functionalisation of polymers and in-situ compatibilisation of poly(ethylene terephthalate)-based blends

One of the main objectives of this study was to functionalise various rubbers (i.e. ethylene propylene copolymer (EP), ethylene propylene diene terpolymer (EPDM), and natural rubber (NR)) using functional monomers, maleic anhydride (MA) and glycidyl methacrylate (GMA), via reactive processing routes. The functionalisation of the rubber was carried out via different reactive processing methods in an internal mixer. GMA was free-radically grafted onto EP and EPDM in the melt state in the absence and presence of a comonomer, trimethylolpropane triacrylate (TRlS). To optinuse the grafting conditions and the compositions, the effects of various paranleters on the grafting yields and the extent of side reactions were investigated. Precipitation method and Soxhlet extraction method was established to purifY the GMA modified rubbers and the grafting degree was determined by FTIR and titration. It was found that without TRlS the grafting degree of GMA increased with increasing peroxide concentration. However, grafting was low and the homopolymerisation of GMA and crosslinking of the polymers were identified as the main side reactions competing with the desired grafting reaction for EP and EPDM, respectively. The use of the tri-functional comonomer, TRlS, was shown to greatly enhance the GMA grafting and reduce the side reactions in terms of the higher GMA grafting degree, less alteration of the rheological properties of the polymer substrates and very little formation of polyGMA. The grafting mechanisms were investigated. MA was grafted onto NR using both thermal initiation and peroxide initiation. The results showed clearly that the reaction of MA with NR could be thermally initiated above 140°C in the absence of peroxide. At a preferable temperature of 200°C, the grafting degree was increased with increasing MA concentration. The grafting reaction could also be initiated with peroxide. It was found that 2,5-dimethyl-2,5-bis(ter-butylproxy) hexane (TIOI) was a suitable peroxide to initiate the reaction efficiently above I50°C. The second objective of the work was to utilize the functionalised rubbers in a second step to achieve an in-situ compatibilisation of blends based on poly(ethylene terephthalate) (PET), in particular, with GMA-grafted-EP and -EPDM and the reactive blending was carried out in an internal mixer. The effects of GMA grafting degree, viscosities of GMAgrafted- EP and -EPDM and the presence of polyGMA in the rubber samples on the compatibilisation of PET blends in terms of morphology, dynamical mechanical properties and tensile properties were investigated. It was found that the GMA modified rubbers were very efficient in compatibilising the PET blends and this was supported by the much finer morphology and the better tensile properties. The evidence obtained from the analysis of the PET blends strongly supports the existence of the copolymers through the interfacial reactions between the grafted epoxy group in the GMA modified rubber and the terminal groups of PET in the blends.

Compatibilisation of heterogeneous polymer blends by reactive processing

Functionalisation of polystyrene, PS, and ethylene-co-propylene-co-cyclopentadiene terpolymer, EPDM, with acrylic acid, AA, in a melt reactive processing procedure, in the presence of peroxide, trigonox 101, and coagents, Divinyl benzene, DVB (for PS), and trimethylolpropane triacrylate, TRIS (for EPDM), were successfully carried out. The level of grafting of the AA, as determined by infrared analysis, was significantly enhanced by the coagents. The grafting reaction of AA takes place simultaneously with homopolymerisation of the monomers, melt degradation and crosslinking reactions of the polymers. The extent of these competing reactions were inferred from measurements of melt flow index and insoluble gel content. Through a judicious use of both the peroxide and the coagent, particularly TRIS, unwanted side reactions were minimized. Five different processing methods were investigated for both functionalisation experiments; the direct addition of the pre-mixed polymer with peroxide and reactive modifiers was found to give optimum condition for grafting. The functionalised PS, F-PS, and EPDM, F-EPD, and maleinised polypropylene carrying a potential antioxidant, N-(4-anilinophenyl maleimide), F-PP were melt blended in binary mixtures of F-PS/F-EPD and F-PP/F-EPD in the presence (or absence) of organic diamines which act as an interlinking agent, e.g, Ethylene Diamine, EDA, and Hexamethylene Diamine, HEMDA. The presence of an interlinking agent, particularly HEMDA shows significant enhancement in the mechanical properties of the blend, suggesting that the copolymer formed has acted as compatibiliser to the otherwise incompatible polymer pairs. The functionalised and amidised blends, F and A-PSIEPDM (SPOI) and F and A-PPIEPDM (SPD2) were subsequently used as compatibiliser concentrates in the corresponding PSIEPDM and PPIEPDM blends containing various weight propotion of the homopolymers. The SPD1 caused general decreased in tensile strength, albeit increased in drop impact strength particularly in blend containing high PS content (80%). The SPD2 was particularly effective in enhancing impact strength in blends containing low weight ratio of PP (<70%). The SPD2 was also a good thermal antioxidant albeit less effective than commercial antioxidant. In all blends the evidence of compatibility was examined by scanning electron microscopy.

The role of stable nitroxyl radical precursors as antioxidants in polyolefins

Various 2,2,6,6-tetramethyl piperidines and their N-alkyl derivatives of stable nitroxyl radical precursors containing acrylic(s) and methacrylic(s) groups were reactively processed in the presence of a peroxide as bound-antioxidant masterbatches for polyolefin stabilisation. It was found that grafting of the antioxidant monomers onto the polymer backbone was inevitably in competition with homopolymerisation of the monomers as well as melt degradation of the polymer and other side reactions. As previously reported, binding efficiency of bisacrylic nitroxyl precursor was maximum due to formation of unextractable homopolymer of the antioxidant. On the other hand, the binding efficiency of monoacrylic derivatives was low and the homopolymers were found extractable, which suggests that the bound monoacrylic derivatives are entirely grafted onto the polyolefin backbone. Application of bis and tri-functional coagents gave improved binding efficiency of the monoacrylic monomers. This may be due to copolymerisation of the antioxidants with the coagents and grafting of the copolymers onto the polymer backbone. Comparison of photostabilising activity of the fully extracted bound antioxidants to those of the corresponding unbound analogous showed lower results for the former. However, thermal stabilising activity of the bound antioxidants was higher than that of the unbound analogous due to better substantivity. Analysis using physical techniques and GPC for molecular weight distribution of masterbatches containing the bound monoacrylic antioxidants showed formation of high molecular weight products. Model reaction of a secondary amine derivative in liquid hydrocarbon and analysis of the product using FTIR and NMR spectroscopy indicated a possibility of side reaction, i.e. involvement of the amine active group (>N-H) of the antioxidant in the binding process to form the high molecular weight product. Implementation of various N-alkylated derivatives did not inhibit the side reaction. The photostabilising activity of the bound-antioxidants can be improved when applied in conjunction with small amounts of a benzophenone uv-stabiliser. The synergistic stabilising activity, however, was diminished when the uv-stabiliser was removed from the system during the service time. Nitroxyl precursors containing methacrylic group(s) gave lower binding efficiency than the corresponding acrylic derivatives. Reversible deploymerisation of the grafted methacrylic antioxidants may be responsible for this. Bis and tris-acrylic coagents improved the binding efficiency, and the presence of methacrylic group improved stabilising activity of the antioxidants. N-methyl derivatives were found to exhibit better stabilising activity than their parent secondary amine derivatives.

Mechanisms of antifatigue agents used in natural rubber

A large number of compounds containing quinonoid or hindered phenol functions were examined for their roles as antifatigue agents. Among the evaluated quinones and phenols expected to have macroalkyl radical scavenging ability, BQ, αTOC, γTOC and GM showed relatively good performance for fatigue resistance (although their performance was slightly less effective than the commercial aromatic amine antioxidants, IPPD and 6PPD). The compounds which were shown to have higher reactivity with alkyl radicals (via calculated reactivity indices) showed better fatigue resistance. This fact supports the suggestion that strong alkyl radical scavengers should be also effective antifatigue agents. Evidence produced based on calculation of reactivity indices suggests that the quinones examined react with alkyl radicals on the meta position of the quinone rings producing phenoxyl radicals. The phenoxyl radicals are expected either to disproportionate, to recombine with a further alkyl radical, or to abstract a hydrogen from another alkyl radical producing an olefine. The regeneration of quinones and formation of the corresponding phenols is expected to occur during the antifatigue activity. The phenol antioxidant, HBA is expected to produce a quinonoid compound and this is also expected to function in a similar way to other quinones. Another phenol, GM, which is also known to scavenge alkyl radicals showed good antifatigue performance. Tocopherols had effective antifatigue activity and are expected to have different antifatigue mechanisms from that of other quinones, hence αTOC was examined for its mechanisms during rubber fatiguing using HPLC analysis. Trimers of αTOC which were produced during vulcanisation are suggested to contribute to the fatigue activity observed. The evidence suggests that the trimers reproduce αTOC and a mechanism was proposed. Although antifatigue agents evaluated showed antifatigue activity, most of them had poor thermoxidative resistance, hence it was necessary to compensate for this by using a combination of antioxidants with the antifatigue agents. Reactive antioxidants which have the potential to graft on the polymer chains during reactive processing were used for this purpose. APMA was the most effective antioxidant among other evaluated reactive antioxidants. Although high ratio of grafting was achieved after optimisation of grafting conditions, it is suggested that this was achieved by long branches of APMA due to large extent of polymerisation. This is expected to cause maldistribution of APMA leading to reducing the effect of CB-D activity (while CB-A activity showed clear advantages for grafting). Further optimisation of grafting conditions is required in order to use APMA more effectively. Moreover, although synergistic effects between APMA and antifatigue agents were expected, none of the evaluated antifatigue agents, BQ, αTOC, γTOC and TMQ, showed significant synergism both in fatigue and thermoxidative resistance. They performed just as additives.

Reactive processing of polyolefins using antioxidant systems

Various monoacrylic compounds containing a hindered phenol function (e.g.3,5-di-tert.-butyl-4-hydroxy benzyl alcohol, DBBA and vinyl-3-[3',5'-di-tert.-butyl-4-hydroxy phenyl] propionate, VDBP), and a benzophenone function (2-hydroxy-4-[beta hydroxy ethoxy] benzophenone, HAEB) were synthesised and used as reactive antioxidants (AO's) for polypropylene (PP). These compounds were reacted with PP melt in the presence of low concentration of a free radical generator such a peroxide (reactive processing) to produce bound-antioxidant concentrates. The binding reaction of these AO's onto PP was found to be low and this was shown to be mainly due to competing reactions such as homopolymerisation of the antioxidant. At high concentrations of peroxide, higher binding efficiency resulted, but, this was accompanied by melt degradation of the polymer. In a special reactive processing procedure, a di- or a trifunctional reactant (referred to as coagent), e.g.tri-methylol propane tri-acrylate, Tris, and Divinyl benzene, DVB, were used with the antioxidant and this has led to an enhanced efficiency of the grating reaction of antioxidants on the polymer in the melt. The evidence suggests that this is due to copolymerisation of the antioxidants with the coagent as well as grafting of the copolymers onto the polymer backbone. Although the 'bound' AO's containing a UV stabilising function showed lower overall stabilisation effect than the unbound analogues before extraction, they were still much more effective when subjected to exhaustive solvent extraction. Furthermore, a very effective synergistic stabilising activity when two reactive AO's containing thermal and UV stabilising functions e.g. DBBA and HAEB, were reactively processed with PP in the presence of a coagent. The stabilising effectiveness of such a synergist was much higher than that of the unbound analogues both before and after extraction. Analysis using the GPC technique of concentrates containing bound-DBBA processed in the presence of Tris coagent showed higher molecular weight (Mn), compared to that of a polymer processed without the coagent, but was still lower than that of the control processed PP with no additives. This indicates that Tris coagent may inhibit further melt degradation of the polymer. Model reactions of DBBA in liquid hydrocarbon (decalin) and analysis of the products using FTIR and NMR spectroscopy showed the formation of grafted DBBA onto decalin molecules as well as homopolymerisation of the AO. In the presence of Tris coagent, copolymerisation of DBBA with the Tris inevitably occured; which was followed by grafting of the copolymer onto the decalin, FTIR and NMR results of the polymer concentrates containing bound-DBBA processed with and without Tris, showed similar behaviour as the above model reactions. This evidence supports the effect of Tris in enhancing the efficiency of the reaction of DBBA in the polymer melt. Reactive procesing of HAEB in polymer melts exhibited crosslinking formation In the early stages of the reaction, however, in the final stage, the crosslinked structure was 'broken down' or rearranged to give an almost gel free polymer with high antioxidant binding efficiency.

The study and characterisation of water-based latices used for can coating interiors

Water-based latices, used in the production of internal liners for beer/beverage cans, were investigated using a number of analytical techniques. The epoxy-graft-acrylic polymers, used to prepare the latices, and films, produced from those latices, were also examined. It was confirmed that acrylic polymer preferentially grafts onto higher molecular weight portions of the epoxy polymer. The amount of epoxy remaining ungrafted was determined to be 80%. This figure is higher than was previously thought. Molecular weight distribution studies were carried out on the epoxy and epoxy-g-acrylic resins. A quantitative method for determining copolymer composition using GPC was evaluated. The GPC method was also used to determine polymer composition as a function of molecular weight. IR spectroscopy was used to determine the total level of acrylic modification of the polymers and NMR was used to determine the level of grafting. Particle size determinations were carried out using transmission electron microscopy and dynamic light scattering. Levels of stabilising amine greatly affected the viscosity of the latex, particle size and amount of soluble polymer but the core particle size, as determined using TEM, was unaffected. NMR spectra of the latices produced spectra only from solvents and amine modifiers. Using solid-state CP/MAS/freezing techniques spectra from the epoxy component could be observed. FT-IR spectra of the latices were obtained after special subtraction of water. The only difference between the spectra of the latices and those of the dry film were due to the presence of the solvents in the former. A distinctive morphology in the films produced from the latices was observed. This suggested that the micelle structure of the latex survives the film forming process. If insufficient acrylic is present, large epoxy domains are produced which gives rise to poor film characteristics. Casting the polymers from organic solutions failed to produce similar morphology.