The boundary lubricated friction and wear of low alloy steel

Pin on disc wear machines were used to study the boundary lubricated friction and wear of AISI 52100 steel sliding partners. Boundary conditions were obtained by using speed and load combinations which resulted in friction coefficients in excess of 0.1. Lubrication was achieved using zero, 15 and 1000 ppm concentrations of an organic dimeric acid additive in a hydrocarbon base stock. Experiments were performed for sliding speeds of 0.2, 0.35 and 0.5 m/s for a range of loads up to 220 N. Wear rate, frictional force and pin temperature were continually monitored throughout tests and where possible complementary methods of measurement were used to improve accuracy. A number of analytical techniques were used to examine wear surfaces, debris and lubricants, namely: Scanning Electron Microscopy (SEM), Auger Electron Spectroscopy (AES), Powder X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), optical microscopy, Back scattered Electron Detection (BSED) and several metallographic techniques. Friction forces and wear rates were found to vary linearly with load for any given combination of speed and additive concentration. The additive itself was found to act as a surface oxidation inhibitor and as a lubricity enhancer, particularly in the case of the higher (1000 ppm) concentration. Wear was found to be due to a mild oxidational mechanism at low additive concentrations and a more severe metallic mechanism at higher concentrations with evidence of metallic delamination in the latter case. Scuffing loads were found to increase with increasing additive concentration and decrease with increasing speed as would be predicted by classical models of additive behaviour as an organo-metallic soap film. Heat flow considerations tended to suggest that surface temperature was not the overriding controlling factor in oxidational wear and a model is proposed which suggests oxygen concentration in the lubricant is the controlling factor in oxide growth and wear.

Automobile friction materials: a test instrument and technique for determining dynamic mechanical properties in relation to brake squeal

This study is primarily concerned with the problem of break-squeal in disc brakes, using moulded organic disc pads. Moulded organic friction materials are complex composites and due to this complexity it was thought that they are unlikely to be of uniform composition. Variation in composition would under certain conditions of the braking system, cause slight changes in its vibrational characteristics thus causing resonance in the high audio-frequency range. Dynamic mechanical propertes appear the most likely parameters to be related to a given composition's tendency to promote squeal. Since it was necessary to test under service conditions a review was made of all the available commercial test instruments but as none were suitable it was necessary to design and develop a new instrument. The final instrument design, based on longitudinal resonance, enabled modulus and damping to be determined over a wide range of temperatures and frequencies. This apparatus has commercial value since it is not restricted to friction material testing. Both used and unused pads were tested and although the cause of brake squeal was not definitely established, the results enabled formulation of a tentative theory of the possible conditions for brake squeal. The presence of a temperature of minimum damping was indicated which may be of use to braking design engineers. Some auxilIary testing was also performed to establish the effect of water, oil and brake fluid and also to determine the effect of the various components of friction materials.

The effect of crystallinity upon the friction and wear of graphites

DUE TO COPYRIGHT RESTRICTIONS ONLY AVAILABLE FOR CONSULTATION AT ASTON UNIVERSITY LIBRARY WITH PRIOR ARRANGEMENT

The development of a testing procedure for dry friction brakes

A description of the background to testing friction materials for automotive brakes explains the need for a rapid, inexpensive means of assessing their behaviour in a way which is both accurate and meaningful. Various methods of controlling inertia dynamometers to simulate road vehicles are rejected in favour of programming by means of a commercially available XY plotter. Investigation of brake service conditions is used to set up test schedules, and a dynamometer programming unit built to enable service conditions on vehicles to be simulated on a full scale dynamometer. A technique is developed by which accelerated testing can be achieved without operating under overload conditions, saving time and cost without sacrificing validity. The development of programming by XY plotter is described, with a method of operating one XY plotter to programme the machine, monitor its own behaviour, and plot its own results in logical sequence. Commissioning trials are described and the generation of reproducible results in frictional behaviour and material durability is discussed. Teclmiques are developed to cross check the operation of the machine in retrospect, and retrospectively correct results in the event of malfunctions. Sensitivity errors in the measuring circuits are displayed between calibrations, whilst leaving the recorded results almost unaffected by error. Typical results of brake lining tests are used to demonstrate the range of performance parameters which can be studied by use of the machine. Successful test investigations completed on the machine are reported, including comments on behaviour of cast iron drums and discs. The machine shows that materials can repeat their complex friction/ temperature/speed/pressure relationships at a reproducibility of the order of +-0.003u and +~ 0.0002 in. thickness loss during wear tests. Discussion of practical and academic implications completes the report with recommendations for further work in both fields.

Reconnection dynamics and mutual friction in quantum turbulence

We investigate the behaviour of the mutual friction force in finite temperature quantum turbulence in 4He, paying particular attention to the role of quantized vortex reconnections. Through the use of the vortex filament model, we produce three experimentally relevant types of vortex tangles in steady-state conditions, and examine through statistical analysis, how local properties of the tangle influence the mutual friction force. Finally, by monitoring reconnection events, we present evidence to indicate that vortex reconnections are the dominant mechanism for producing areas of high curvature and velocity leading to regions of high mutual friction, particularly for homogeneous and isotropic vortex tangles.

Some effects of friction and lubrication during hot forging steel.

DUE TO COPYRIGHT RESTRICTIONS ONLY AVAILABLE FOR CONSULTATION AT ASTON UNIVERSITY LIBRARY AND INFORMATION SERVICES WITH PRIOR ARRANGEMENT

Comparative analysis of experimental and modelling of gas-solid flow hydrodynamics:effect of friction and interparticle cohesion forces

The effect of friction and interparticle cohesion forces on the gas-solid flow hydrodynamics was discussed. A proposed interparticle cohesion and frictional force terms have been tested in a continuum fully developed flow model to investigate their effect on the general hydrodynamic features of vertical duct flow. It was observed that both terms have direct effect on lowering the material carryover, which implies a reduced bed expansion in freely bubbling column. The parametric analysis shows that cohesion and frictional forces are high when compared to kinetic stress and hence it can play a major role in describing the hydrodynamics features of the flow.

Rutting-induced permeability loss of open graded friction course mixtures

Functionality of an open graded friction course (OGFC) depends on the high interconnected air voids or pores of the OGFC mixture. The authors' previous study indicated that the pores in the OGFC mixture were easily clogged by rutting deformation. Such a deformation-related clogging can cause a significant rutting-induced permeability loss in the OGFC mixture. The objective of this study was to control and reduce the rutting-induced permeability loss of the OGFC based on mixture design and layer thickness. Eight types of the OGFC mixtures with different air void contents, gradations, and nominal maximum aggregate sizes were fabricated in the laboratory. Wheel-tracking rutting tests were conducted on the OGFC slabs to simulate the deformation-related clogging. Permeability tests after different wheel load applications were performed on the rutted OGFC slabs using a falling head permeameter developed in the authors' previous study. The relationships between permeability loss and rutting depth as well as dynamic stability were developed based on the eight OGFC mixtures' test results. The thickness effects of the single-layer and the two-layer OGFC slabs were also discussed in terms of deformation-related clogging and the rutting-induced permeability loss. Results showed that the permeability coefficient decreases linearly with an increasing rutting depth of the OGFC mixtures. Rutting depth was recommended as a design index to control permeability loss of the OGFC mixture rather than the dynamic stability. Permeability loss due to deformation-related clogging can be effectively reduced by using a thicker single-layer OGFC or two-layer OGFC.