Environmental degradation of polyethylene-based plastics

The criteria involved in the degradation of polyethylene-based degradable polymer samples have been investigated, with a view to obtaining a clearer mechanism of photo-biodegradation. The compatibility of degradable polymer samples during materials recycling was also studied. Commercial and laboratory prepared degradable polymer samples were oxidised in different environments and the oxidation products formed were studied using various analytical chromatographic and spectroscopic techniques such as HPLC, FT-IR and NMR. It was found that commercial degradable polymer samples which are based on the ECO systems, degrade predominantly via the Norrish II process, whereas the other degradable systems studied (starch-filled polyethylene systems, transition metal systems, including metal carboxylate based polyethylene systems and the photoantioxidant-activator systems) photodegrade essentially via the Norrish I process. In all cases, the major photoxidation products extracted from the degradable polymer samples were found to be carboxylic acids, although, in the polymer itself a mixture of carbonyl containing products such as esters, lactones, ketones and aldehydes was observed. The study also found that the formation of these hydrophilic carbonyl products causes surface swelling of the polymer, thus making bioerosion possible. It was thus concluded that environmental degradation of LDPE is a two step process, the initiation stage being oxidation of the polymer which gives rise to bioassimilable products, which are consequently bioeroded in the second stage, (the biodegradation step). Recycling of the degradable polymer samples as 10% homogeneous and heterogeneous blends was carried out using a single screw extruder (180°C and 210°C) and an internal mixer (190°C). The study showed that commercial degradable polymer samples may be recycled with a minimal loss in their properties.

Degradation and stabilisation of diisocyanate cured polybutadiene

Hydroxyl terminated polybutadiene (HTPB) has been used as a rocket propellant binder which is required to be stored for at least twenty years. It is found that the excellent stress-strain characteristics of this propellant can be totally lost, during this long storage, due to the deterioration of the polybutadiene chains. As a result, the propellant can not stand the service loads, which may lead to a catastrophe. The study of the HTPB binder degradation, below 80°C, has been carried out by investigating the environmental factors and the changes which occur along the macromolecular chains. Results have shown that oxygen is the main factor which causes the crosslinking and chain scission reactions. The former is the predominant reaction and proceeds rapidly under oxygen sufficient environment. The unsaturation of polymer chain, which provides the desired physical properties to the binder, was lost with the increase in crosslink density. At the same time hydroperoxides were found to form and decompose along the polymer chains. Therefore, the deterioration of the binder results from the oxidation of polymer chains. Since the oxidation reaction occurred at higher rate than oxygen diffusion rate and oxygen diffusion rate is inversely proportional to the crosslink density, the binder, below the surface layer in a thick section container, could be naturally protected under an oxygen deficient condition for a long time. Investigation of the effectiveness of antioxidants in HTPB binder has shown that the efficiency of an antioxidant depends on its ability to scavenge radicals. Generally, aromatic amines are the most effective binder antioxidants. But when a peroxide decomposer is combined with an aromatic amine at the appropriate ratio, a synergistic effect is obtained, which gives the lowest binder gel increase rate.

Cobalt promoted TiO2/GO for the photocatalytic degradation of oxytetracycline and Congo Red

A family of titania derived nanocomposites synthesized via sol-gel and hydrothermal routes exhibit excellent performance for the photocatalytic degradation of two important exemplar water pollutants, oxytetracycline and Congo Red. Low loadings of Co3O4 nanoparticles dispersed over the surfaces of anatase TiO2 confer visible light photoactivity for the aqueous phase decomposition of organics through the resulting heterojunction and reduced band gap. Subsequent modification of these Co3O4/TiO2 composites by trace amounts of graphene oxide nanosheets in the presence of a diamine linker further promotes both oxytetracycline and Congo Red photodegradation under simulated solar and visible irradiation, through a combination of enhanced photoresponse and consequent radical generation. Radical quenching and fluorescence experiments implicate holes and hydroxyl radicals as the respective primary and secondary active species responsible for oxidative photodegradation of pollutants.

Hydroxyl radical generation by cactus-like copper oxide nanoporous carbon catalysts for microcystin-LR environmental remediation

Copper oxide supported on nanoporous activated carbon (CuO-NPAC) is reported for the aqueous phase catalytic degradation of cyanotoxin microcystin-LR (MC-LR). The loading and spatial distribution of CuO throughout the NPAC matrix strongly influence the catalytic efficiency. CuO-NPAC synthesis was optimized with respect to the copper loading and thermal processing, and the physicochemical properties of the resulting materials were characterized by XRD, BET, TEM, SEM, EPR, TGA, XPS and FT-IR spectroscopy. EPR spin trapping and fluorescence spectroscopy showed in situ ˙OH formation via H2O2 over CuO-NPAC as the catalytically relevant oxidant. The impact of reaction conditions, notably CuO-NPAC loading, H2O2 concentration and solution pH, is discussed in relation to the reaction kinetics for MC-LR remediation.