Hot-spots during the calcination of MCM-41:a SAXS comparative analysis of a soft mesophase

The phenomenon of microscopic hot-spots, during the calcination of MCM-41, was investigated by quantifying the magnitude of the temperature increase during the calcination of a soft MCM-41 mesophase using a SAXS comparative study. This was performed by thermally treating a soft material that was detemplated via Fenton chemistry followed by equilibrating and drying in a low-surface-tension solvent (n-butanol or N,N-dimethylformamide); these samples have limited structural shrinkage. The resulting samples were thermally treated at increasing temperatures, and the structural shrinkage was compared with that of the directly calcined material. By comparing the structural shrinkage, it was found that the microscopic temperature increase would fall between 190 and 250 C, as deduced from N,N-dimethyl-formamide and n-butanol. The order of magnitude of the temperature increase appears to be consistent with the well-known glow effect. It is, however, substantially higher than the experimentally determined macroscopic temperature increase. Several aspects are discussed to interpret this difference. © 2013 Elsevier B.V.

The tribology of laminated magnetic recording heads

This thesis investigates the mechanisms that lead to pole tip recession (PTR) in laminated magnetic recording heads (also known as "sandwich heads"). These heads provide a platform for the utilisation of advanced soft magnetic thin films in practical recording heads suitable for high frequency helical scan tape recording systems. PTR results from a differential wear of the magnetic pole piece from the tape-bearing surface of the head. It results in a spacing loss of the playback or read signal of 54.6dB per recording wavelength separation of the poles from the tape. PTR depends on the material combination used in the head, on the tape type and the climate - temperature and relative humidity (r.h.). Five head materials were studied: two non-magnetic substrate materials- sintered multi granular CaTi03 and composite CaTi03/ZrTi04/Ti02 and three soft magnetic materials- amorphous CoNbZr, and nanocrystalline FeNbSiN and FeTaN. Single material dummy heads were constructed and their wear rates measured when cycling them in a Hi-8 camcorder against commercially available metal particulate (MP) and metal evaporated (ME) tapes in three different climates: 25°C/20%r.h., 25°C/80%r.h. and 40°C/80%r.h. X-ray photoelectron spectroscopy (XPS) was used to examine changes the head surface chemistry. Atomic force microscopy (AFM) was used to examine changes in head and tape surface topography. PTR versus cycling time of laminated heads of CaTi03/ZrTiO4/Ti02 and FeTaN construction was measured using AFM. The principal wear mechanism observed for all head materials was microabrasion caused by the mating body - the tape surface. The variation in wear rate with climate and tape type was due to a variation in severity in this mechanism, except for tape cycling at 40°C in which gross damage was observed to be occurring to the head surface. Two subsidiary wear mechanisms were found: third body scratching (all materials) and grain pullout (both ceramics and FeNbSiN). No chemical wear was observed, though tribochemical reactions were observed on the metal head surfaces. PTR was found to be caused by two mechanisms - the first differential microabrasion of the metal and substrate materials and which was characterised by a low (~10nm) equilibrium value. The second was by deep ploughing by third body debris particles, thought mainly to be grain pullout particles. This level of PTR caused by this mechanism was often more severe, and of a non-equilibrium nature. It was observed more for ME tape, especially at 40°C/80%r.h. and 25°c/20%r.h. Two other phenomena on the laminated head pole piece were observed and commented upon: staining and ripple texturing.

A study in radiopaque polymeric materials

The problems associated with x-ray-transparent denture base are defined and conventional approaches to their solution are assessed. Consideration of elemental absorption parameters leads to the postulation that atoms such as zinc, and bromine, may be effective radiopacifiers over at least part of the clinical x-ray spectrum. These elements had hitherto been considered too light to be effective. Investigation of copolymers of methylmethacrylate and p-bromostyrene revealed no deleterious effects arising from the aromatically brominated monomer (aliphatic bromination caused UV destabilisation). For effective x-ray absorption a higher level of bromination would be necessary, but the expense of suitable compounds made further study unjustifiable. Incorporation of zinc atoms into the polymer was accomplished by copolymerisation of zinc acrylate with methylmethacrylate in solution. At high zinc levels this produced a powder copolymer convenient for addition to dental polymers in the dough moulding process. The resulting mouldings showed increasing brittleness at high loadings of copolymer. Fracture was shown to be through the powder particles rather than around them, indicating the source of weakness to be in the internal structure of the copolymer. The copolymer was expected to be cross-linked through divalent zinc ions and its insolubility and infusibility supported this. Cleavage of the ionic cross links with formic acid produced a zinc-free linear copolymer of high molecular weight. Addition of low concentrations of acrylic acid to the dough moulding monomer appeared to 'labilise' the cross links producing a more homogeneous moulding with adequate wet strength. Toxicologically the zinc-containing materials are satisfactory and though zinc is extracted at a measurable rate in an aqueous system, this is very small and should be acceptable over the life of a denture. In other respects the composite is quite satisfactory and though a marketable product is not claimed the system is considered worthy of further study.

An X-ray micro-fluorescence study to investigate the distribution of Al, Si, P and Ca ions in the surrounding soft tissue after implantation of a calcium phosphate-mullite ceramic composite in a rabbit animal model

Synthetic calcium phosphates, despite their bioactivity, are brittle. Calcium phosphate-mullite composites have been suggested as potential dental and bone replacement materials which exhibit increased toughness. Aluminium, present in mullite, has however been linked to bone demineralisation and neurotoxicity: it is therefore important to characterise the materials fully in order to understand their in vivo behaviour. The present work reports the compositional mapping of the interfacial region of a calcium phosphate-20 wt% mullite biocomposite/soft tissue interface, obtained from the samples implanted into the long bones of healthy rabbits according to standard protocols (ISO-10993) for up to 12 weeks. X-ray micro-fluorescence was used to map simultaneously the distribution of Al, P, Si and Ca across the ceramic-soft tissue interface. A well defined and sharp interface region was present between the ceramic and the surrounding soft tissue for each time period examined. The concentration of Al in the surrounding tissue was found to fall by two orders of magnitude, to the background level, within similar to 35 mu m of the implanted ceramic.

The effect of care solutions on the bulk and surface properties of soft contact lenses

Purpose: Soft contact lenses for continuous wear require the use of cleaning regimes which utilise hydrogen peroxide systems or multipurpose cleaning solutions (MPS). The compositions of MPS are becoming increasingly complex and often include disinfectants, cleaning agents, preservatives, wetting agents, demulcents, chelating and buffering agents. Recent research on solution–lens interactions has focused on specific ocular parameters such as corneal staining. However the effect of a solution on the lens, particularly silicone hydrogel lenses, itself has received less attention. The purpose of this work was to establish and understand the effects that care solutions have on selected bulk and surface material properties. Methods: Selected bulk and surface properties of each material (etafilcon A, vifilcon A, balafilcon A, senofilcon A, lotrafilcon A and lotrafilcon B, galyfilcon A) were measured after a 24 h soak in a variety of care solutions. Additionally the lenses were soaked for 24 h in hyperosmolar (680 mOsm L-1) and hyposmolar (170 mOsm L-1) PBS. A bulk property parameter the total diameter (TD) was measured using an Optimec contact lens analyser. The surface property related CoF of soaked lenses was measured on a nano-tribometer with conditions of load 30 mN, at a distance of 20 mm and speed 30 mm/min. Results: In terms of bulk properties, change is related to the EWC of the lens, the higher the EWC of the lens the greater the TD changes. Silicone hydrogel lenses have EWCs of <47% and little or no TD changes were observed; lotrafilcon A exhibited no change irrespective of the cleaning solution. Conventional contact lenses have higher EWCs (58% for etafilcon A and 55% for vifilcon A) and the TD was seen to change to a greater extent, for example the etafilcon A material in ReNu MPS had an increase to 14.45± 0.07 mm from the cited 14.2 mm. Other lenses increased or decreased in TD depending on the solution used. The osmolarity of the solution although important is not the only factor governing change in the TD, for example soaking senofilcon A in hyperosmolar PBS (680 mOsm L-1) for 24 h increased the TD of the lens (+0.25 ± 0.07 mm), however when the same lens type was soaked for 24 h in a MPS with a lower osmolarity there was a similar effect. Biotribology measurements demonstrated that some solution–lens combinations can reduce the CoF by 55%, when compared with biotribology with the native packing solution. An increase in the CoF was observed for other solution–lens combinations. Conclusions: There is a dramatic difference in bulk and surface performance of specific lens materials with particular care solutions. Individual components of the care solutions have effects on the bulk and surface properties of contact lenses. The affects are not as great with the silicone hydrogel as compared with conventional hydrogels.

Clinical performance of daily disposable soft contact lenses using sustained release technology

Purpose: Polyvinyl alcohol (PVA) is a successful tear film stabiliser and is widely used in comfort drops and some soft contact lens materials. A PVA-containing lens, nelfilcon A has been modified to include additional (non-functional) PVA in order to provide improved comfort. This study aims to examine the clinical performance of this nelfilcon A lens with AquaRelease™ (AquaRelease). Methods: Two contralateral, investigator masked, open label, subjective and objective evaluations were conducted. The first examined the effect of adding increased molecular weight PVA to nelfilcon A (n = 5), and the second compared this AquaRelease lens to ocufilcon B (n = 34). The principal measures were non-invasive break-up time (NIBUT) and subjective comfort, which were assessed at the beginning and end of a week of daily wear, and three times throughout 1 day at 8, 12 and 16 h. Results: All subjects successfully completed the daily wearing schedule of 16 h. On initial insertion, subjective comfort and NIBUT improved for AquaRelease than original nelfilcon A lenses (p < 0.05). Initial comfort was better for AquaRelease compared to ocufilcon B lenses (p = 0.01); however, NIBUT was not statistically different (11.7 ± 15.6 s versus 8.4 ± 6.8 s; p = 0.26). Subjective comfort decreased with time (p < 0.001), but there was no significant difference between AquaRelease and ocufilcon B lenses (p = 0.16). NIBUT was not significantly affected by time (p = 0.56) or between lenses (p = 0.33). At the end of a weeks' wear, subjective initial, end-of-day, overall comfort and vision were rated significantly better with AquaRelease than ocufilcon B (p < 0.01). Conclusions: Release of additional non-functionalised PVA from the nelfilcon A lenses appears to enhance comfortable contact lens wear. © 2006 British Contact Lens Association.

Physical and biological properties of a novel siloxane adhesive for soft tissue applications

The aim of this study was to investigate the adhesive properties of an in-house amino-propyltrimethoxysilane-methylenebisacrylamide (APTMS-MBA) siloxane system and compare them with a commercially available adhesive, n-butyl cyanoacrylate (nBCA). The ability of the material to perform as a soft tissue adhesive was established by measuring the physical (bond strength, curing time) and biological (cytotoxicity) properties of the adhesives on cartilage. Complementary physical techniques, X-ray photoelectron spectroscopy, Raman and infrared imaging, enabled the mode of action of the adhesive to the cartilage surface to be determined. Adhesion strength to cartilage was measured using a simple butt joint test after storage in phosphate-buffered saline solution at 37°C for periods up to 1 month. The adhesives were also characterised using two in vitro biological techniques. A live/dead stain assay enabled a measure of the viability of chondrocytes attached to the two adhesives to be made. A water-soluble tetrazolium assay was carried out using two different cell types, human dermal fibroblasts and ovine meniscal chondrocytes, in order to measure material cytotoxicity as a function of both supernatant concentration and time. IR imaging of the surface of cartilage treated with APTMS-MBA siloxane adhesive indicated that the adhesive penetrated the tissue surface marginally compared to nBCA which showed a greater depth of penetration. The curing time and adhesion strength values for APTMS-MBA siloxane and nBCA adhesives were measured to be 60 s/0.23 MPa and 38 min/0.62 MPa, respectively. These materials were found to be significantly stronger than either commercially available fibrin (0.02 MPa) or gelatin resorcinol formaldehyde (GRF) adhesives (0.1 MPa) (P <0.01). Cell culture experiments revealed that APTMS-MBA siloxane adhesive induced 2% cell death compared to 95% for the nBCA adhesive, which extended to a depth of approximately 100-150 μm into the cartilage surface. The WST-1 assay demonstrated that APTMS-MBA siloxane was significantly less cytotoxic than nBCA adhesive as an undiluted conditioned supernatant (P <0.001). These results suggest that the APTMS-MBA siloxane may be a useful adhesive for medical applications. © VSP 2005.

Injectable biomimetic hydrogels for soft tissue repair

This chapter discusses recent developments of injectable biomimetic hydrogel systems found in soft tissue repair applications. It begins by introducing how biomimesis and biomaterials are related, and how tissue repair systems can be considered biomimetic. We introduce hydrogels by discussing their classification, synthesis and applications, then discuss how injectable biomimetic hydrogels have been investigated for use in soft tissue repair. Different approaches to the use of biomimetic hydrogels for soft tissue repair are covered, focusing on synthetic, non-biodegrable polymers. We include so-called conventional polymers and more biomimetic polymers. The chapter concludes with the likely future trends and highlights further reading materials. © 2013 Woodhead Publishing Limited. All rights reserved.

Detemplation of soft mesoporous silica nanoparticles with structural preservation

A mild protocol that allows the template removal of soft un-aged silica nanoparticles was investigated. After oxidizing the organic template by Fenton chemistry, a good structural preservation is only achieved when the material is equilibrated and dried in a low-surface tension solvent. This avoids excessive capillary stress induced by the high surface tension of water, a major component in the Fenton reaction medium. The Fenton reaction should be carried out under mild conditions as well; otherwise the sample deteriorates by extensive hydrolysis, and capillary stress, and the structural ordering diminishes severely. We propose employing 10 ppm Fe concentration at 70 °C for 24 h for the cetyltrimethylammonium bromide template. The proposed protocol involves 2 steps resulting in an overall significantly higher pore volume attributed to the wider pores and limited particle agglomeration, while the calcined counterpart evidences aggregation and loss of the hexagonal ordering. n-BuOH exchange is unnecessary when the mesophase is stabilized by ageing, as the structure resists the water capillary stress. © The Royal Society of Chemistry 2013.