The effect of zinc and titanium on the structure of calcium-sodium phosphate based glass

An array of different structural probes has been used to define the effect of adding Zn and Ti to a sodium-calcium phosphate glass. X-ray absorption spectroscopy at the Zn K-edge suggests that the Zn atoms occupy mixed (4- and 6-fold) sites within the glass matrix. X-ray diffraction reveals a feature at 2.03 angstrom that develops with the addition of Zn and Ti and is consistent with Zn-O and Ti-O near-neighbour distances. Neutron diffraction is used to resolve two distinct P-O distances and highlights the decrease in P center dot center dot center dot P coordination number from 2.0 to 1.7 as the Ti metal concentration rises, which is attributed to the O/P fraction moving away from the metaphosphate value of 3.0 to 3.1 with the addition of Ti. Other correlations, such as those associated with CaO(x) and NaO(x) polyhedra, remain largely unaffected. These results suggest that the network forming P center dot center dot center dot P correlation is most disrupted, with the disorder parameter rising from 0.07 to 0.10 angstrom with the additional modifiers. Zn appears to be introduced into the network as a direct replacement for Ca and causes no structural variation over the composition range studied.

A comparative study of the structure of sodium borophosphates made by sol-gel and melt-quench methods

The atomic scale structure of sodium borophosphates made by the sol-gel method is compared to those made by the melt-quench method. It is found that although the sol-gel generated materials have a higher tendency towards crystallization, they nevertheless show a qualitatively similar crystallization trend with composition to their melt-quench analogues; the progressive introduction of boron oxide into the phosphate network initially inhibits then promotes crystallization. At the composition associated with the most stable amorphous sodium borophosphate (20 mol% boron oxide), it is found that the atomic scale structure of the sol-gel synthesized network glass is almost identical to that of the corresponding melt-quenched one.

Structure of rare-earth phosphate glasses by neutron diffraction

Neutron diffraction was used to measure the structure of the phosphate glasses RAl0.30P3.05O9.62, where R denotes Dy or Ho, and RAl0.34P3.20O10.04, where R denotes La or Ce. For each glass, isomorphic structures were assumed and difference function methods were employed to separate, essentially, those correlations involving the rare-earth ion, R3+, from the remainder. The ratio of bridging oxygen, OB, to terminal oxygen, OT, atoms in the PO4 tetrahedra was quantified and in both materials R3+ and Al3+ are found to act as network modifying cations which bind to the OT. The R–OT coordination number is 6.7(1) and 7.5(2) for the Dy/Ho and La/Ce glasses respectively.

Probing crystallisation of a fluoro-apatite - mullite system using neutron diffraction

Real-time small angle neutron scattering and wide angle neutron scattering studies were undertaken concurrently on a glass ionomer of nominal composition 4.5(SiO2)-3(Al2O3)-1.5(P2O5)-3(CaO)-2(CaF2). Neutron studies were conducted as a function of temperature to investigate the crystallisation process. No amorphous phase separation was observed at room temperature and the onset of crystallisation was found to occur at 650°C, which is 90°C lower than previously reported. The first crystalline phase observed corresponded to fluorapatite; it was only upon further heating was the mullite phase became present. The crystallite size at 650°C was found to be ~115Å and the result was consistent across all measurements.