Crack closure and residual stress effects in fatigue of a particle-reinforced metal matrix composite

A study of the influence of macroscopic quenching stresses on long fatigue crack growth in an aluminium alloy-SiC composite has been made. Direct comparison between quenched plate, where high residual stresses are present, and quenched and stretched plate, where they have been eliminated, has highlighted their rôle in crack closure. Despite similar strength levels and identical crack growth mechanisms, the stretched composite displays faster crack growth rates over the complete range of ΔK, measured at R = 0.1, with threshold being displaced to a lower nominal ΔK value. Closure levels are dependent upon crack length, but are greater in the unstretched composite, due to the effect of surface compressive stresses acting to close the crack tip. These result in lower values of ΔKeff in the unstretched material, explaining the slower crack growth rates. Effective ΔKth values are measured at 1.7 MPa√m, confirmed by constant Kmax testing. In the absence of residual stress, closure levels of approximately 2.5 MPa√m are measured and this is attributed to a roughness mechanism.

Fatigue crack propagation in some PM steels

Mechanisms of fatigue crack growth have been studied for a range of PM steels at relative densities of 0.90 and 1.0, for which strength, fracture toughness, and microstructural information was also available. It is shown that the Paris exponents for steady state crack growth are between 8 and 18 when ρr is approximately 0.9 but when ρr is approximately 1.0 the exponents are between 2.6 and 4.0, i.e in the range typical of wrought steels (2-4). At both densities, threshold stress intensities are between 5.5 and 10.8 MPa m1/2 when R = 0.1. Combinations of these thresholds and yield strengths are comparable with those for wrought steels. When R = 0.8, reductions in threshold to between 2.7 and 5 MPa m1/2 are attributed to crack closure effects. At ρr = 0.90, Fe-0.5C fails by progressive rupture of sinter necks. Astaloy A, with 0.2%C and 0.6%C, and Distaloy AB-0.6C have smaller plastic zone sizes and the cracks follow more difficult paths through particles as well as necks. When ρr is approximately 1.0, fracture is partially by true fatigue modes and partly by cleavage, the bursts of cleavage being more noticeable when Kmax is high.

Effect of thermal residual stresses on fatigue crack opening and propagation behavior in an Al/SiCp metal matrix composite

The effects of a thermal residual stress field on fatigue crack growth in a silicon carbide particle-reinforced aluminum alloy have been measured. Stress fields were introduced into plates of material by means of a quench from a solution heat-treatment temperature. Measurements using neutron diffraction have shown that this introduces an approximately parabolic stress field into the plates, varying from compressive at the surfaces to tensile in the center. Long fatigue cracks were grown in specimens cut from as-quenched plates and in specimens which were given a stress-relieving overaging heat treatment prior to testing. Crack closure levels for these cracks were determined as a function of the position of the crack tip in the residual stress field, and these are shown to differ between as-quenched and stress-relieved samples. By monitoring the compliance of the specimens during fatigue cycling, the degree to which the residual stresses close the crack has been evaluated. © 1995 The Minerals, Metals & Material Society.

Influence of macroscopic residual stress fields on fatigue crack growth measurement in SiC particulate reinforced 8090 aluminium alloy

The effect of residual stresses, induced by cold water quenching, on the morphology of fatigue crack fronts has been investigated in a powder metallurgy 8090 aluminium alloy, with and without reinforcement in the form of 20 wt-%SiC particles. Residual stress measurements reveal that the surface compressive stresses developed in these materials are significantly greater than in conventional metallurgy ingot 8090, because surface yielding occurs on quenching. The yield stresses of the powder route materials are greater than those of ingot produced 8090 and hence greater surface stresses can be maintained. In fatigue, severe crack front bowing is observed in the powder formed materials as a result of the reduction of the R ratio (minimum load/maximum load) by the compressive residual stresses at the sides of the specimen, causing premature crack closure and hence reducing the local driving force for fatigue crack growth ΔKeff. This distortion of the crack fronts introduces large errors into measurements of crack growth rate and threshold values of ΔK.

Temperature effects on fatigue thresholds and structure sensitive crack growth in a nickel-base superalloy

Fatigue thresholds and slow crack growth rates have been measured in a powder formed nickel-base superalloy from room temperature to 600°C. Two grain sizes were investigated: 5-12 μm and 50 μm. It is shown that the threshold increases with grain size, and the difference is most pronounced at room temperature. Although crack growth rates increase with temperature in both microstructures, the threshold is only temperature dependent in the material with the larger grain size. It is also only in the latter that the room temperature threshold falls when the load ratio is increased from 0.1 to 0.5. At 600°C the higher load ratio causes a 20% reduction in the threshold irrespective of grain size. The results are discussed in terms of surface roughness and oxide-induced crack closure, the former being critically related to the type of crystallographic crack growth, which is in turn shown to be both temperature and stress intensity dependent. © 1983.

Application of the finite element method to problems in fracture mechanics

Numerical techniques have been finding increasing use in all aspects of fracture mechanics, and often provide the only means for analyzing fracture problems. The work presented here, is concerned with the application of the finite element method to cracked structures. The present work was directed towards the establishment of a comprehensive two-dimensional finite element, linear elastic, fracture analysis package. Significant progress has been made to this end, and features which can now be studied include multi-crack tip mixed-mode problems, involving partial crack closure. The crack tip core element was refined and special local crack tip elements were employed to reduce the element density in the neighbourhood of the core region. The work builds upon experience gained by previous research workers and, as part of the general development, the program was modified to incorporate the eight-node isoparametric quadrilateral element. Also. a more flexible solving routine was developed, and provided a very compact method of solving large sets of simultaneous equations, stored in a segmented form. To complement the finite element analysis programs, an automatic mesh generation program has been developed, which enables complex problems. involving fine element detail, to be investigated with a minimum of input data. The scheme has proven to be versati Ie and reasonably easy to implement. Numerous examples are given to demonstrate the accuracy and flexibility of the finite element technique.

Isothermal fatigue of an aluminide-coated single-crystal superalloy:Part II. Effects of brittle precracking

The effect of brittle coating precracking on the fatigue behavior of a high-activity aluminide-coated single-crystal nickel-base superalloy has been studied using hollow cylindrical specimens at test temperatures of 600 °C, 800 °C, and 1000 °C. Three types of precrack were studied: narrow precracks formed at room temperature, wide precracks formed at room temperature, and narrow precracks formed at elevated temperature. The effect of precracking on fatigue life at 600 °C was found to depend strongly on the type of precrack. No failure was observed for specimens with narrow room-temperature precracks because of crack arrest via an oxidation-induced crack closure mechanism, while the behavior of wide precracks and precracks formed at elevated temperature mirrored the non-precracked behavior. Crack retardation also occurred for narrow room-temperature precracks tested at 800 °C - in this case, fatigue cracks leading to failure initiated in a layer of recrystallized grains on the inside surface of the specimen. A significant reduction in fatigue life at 800 °C relative to non-precracked specimens was observed for wide precracks and elevated temperature precracks. The presence of precracks bypassed the initiation and growth of coating fatigue cracks necessary for failure in non-precracked material. No effect of precracking was observed at 1000 °C.

Effects of dynamic strain ageing on fatigue crack propagation and threshold behaviour in a Ni-base superalloy

In the temperature range 200-400 degree C the Ni-base superalloy, N901, develops marked dynamic strain ageing effects in its tensile behavior. These include inverse strain rate sensitivity, especially in UTS values, strongly serrated stress-strain curves and a heavily sheared failure mode at the higher test-temperatures. As for steels these effects seem to be due to interactions between the dislocations and the interstitial carbon atoms present. The results of tensile and fatigue threshold tests carried out between 20 degree C and 420 degree C are reported and the fatigue behavior is discussed in terms of the effects of surface roughness induced closure, temperature and strain aging interactions.

The role of primary carbides in fatigue crack propagation in aeroengine bearing steels

Fatigue crack propagation, tensile and fracture toughness data for four aeroengine bearing steels are reported. The steels involved are the through-hardened tool steels 18-4-1 (T1) and M50, and two similar carburized steels, RBD and Volvic. Crack growth data have been obtained at 20 °C and 280 °C to cover the range of oil temperatures experienced in aeroengine bearing operations. At 20 °C threshold ΔK values (ΔKth) ranged between 3.5 and 4.5 MPa √m with Paris exponents (m) of between 2.0 and 3.5. The lowest m-values were seen in the carburizing steels, which also exhibited lower Paris regime crack growth rates than M50 and 18-4-1. For all the steels, growth rates were higher at 280 °C,than 20 °C, although there was a slight tendency for ΔKth to increase, probably associated with oxide-induced closure at 280 °C. The effects of primary carbides, strength and toughness on fatigue crack growth behaviour are discussed, in relation to the importance of static-mode cracking. © 1990.

Facility closure management:the case of Vauxhall Motors Luton

Purpose – The purpose of the paper is to present the findings of a study of factory closure management. It details the sequence and the results of the key strategic manufacturing management decisions made from the time of the announcement of the plant closure to the cessation of operations. The paper also includes an analysis of the human resource management (HRM) actions taken during this same time period and their consequences upon all those involved in the closure management process. Design/methodology/approach – The case study methodology consisted of two initial site visits to monitor closure management effectiveness (adherence to plan and the types and frequency of closure management communications). During these visits, documentary evidence of the impact of the closure decision upon production performance was also collected (manufacturing output and quality performance data). Following plant closure, interviews were held with senior business, production and HRM managers and production personnel. A total of 12 interviews were carried out. Findings – The case study findings have informed the development of a conceptual model of facility closure management. Information obtained from the interviews suggests that the facility closure management process consists of five key management activities. The unexpected announcement of a factory closure can cause behavioural changes similar to those of bereavement, particularly by those employees who are its survivors. In addition, similar reactions to the closure announcement may be displayed by those who choose to remain employed by the factory owner throughout the phased closure of the plant. Originality/value – Facility closure management is an insufficiently researched strategic operations management activity. This paper details a recommended procedure for its management. A conceptual model has also been developed to illustrate the links between the key facility closure management tasks and the range of employee changes of behaviour that can be induced by their execution.

Achieving closure through knowledge management strategy

Case studies of knowledge management practices are often conducted in organizations where the aim is to manage knowledge for future operational improvements. What about knowledge management for organizations with limited life-spans that are preparing for closure? Such organizations are not common but can benefit from knowledge management strategy. This case study concerns the knowledge management strategy of an organization that is preparing for its final phase of operations. We facilitated two group workshops with senior managers to scope a strategy, following which the organization initiated a set of projects to implement the resulting actions. This paper reviews their implemented actions against those designed in the workshop to shed light on knowledge management in this uncommon situation.

Employment outcomes and plant closure in a post-industrial city:an analysis of the labour market studies of MG Rover workers three years on

This paper examines how the loss of 6300 jobs from the closure of MG Rover (MGR) in the city of Birmingham (UK) in April 2005 affected the employment trajectories of ex-workers, in the context of wider structural change and efforts at urban renewal. The paper presents an analysis of a longitudinal survey of 300 ex-MGR workers, and examines to what extent the state of local labour markets and workers’ geographical mobility—as well as the effectiveness of the immediate policy response and longer-term local economic strategies—may have helped to balance the impacts of personal attributes associated with workers’ employability and their reabsorption into the labour markets. It is found that the relative buoyancy of the local economy, the success of longer-run efforts at diversification and a strong policy response and retraining initiative helped many disadvantaged workers to find new jobs in the medium term. However, the paper also highlights the unequal employment outcomes and trajectories that many lesser-skilled workers faced. It explores the policy issues arising from such closures and their aftermath, such as the need to co-ordinate responses, to retain institutional capacity, to offer high-quality training and education resources to workers and, where possible, to slow down such closure processes to enable skills to be retained and reused within the local economy.

"Crack down on the celebrity junkies": does media coverage of celebrity drug use pose a risk to young people?

This study analysed news media content to examine the role played by celebrity drug use in young people's perceptions of drug use. We know that young people have access to discourses of drug use through music and other media which may emphasise short term gains (of pleasure or sexual success) over longer term health and social problems. This study goes beyond a simple modelling approach by using Media Framing Analysis (MFA) to take an in-depth look at the messages themselves and how they are 'framed'. New stories about Amy Winehouse's drug use were used and we conducted focus groups with young people asking them questions about drugs, celebrity and the media. Frames identified include: 'troubled genius', 'losing patience' and 'glamorization or gritty realism'. Initially, the press championed Winehouse's musical talent but soon began to tire of her recklessness; the participants tended to be unimpressed with Winehouse's drug use, characterising her as a promising artist who had 'gone off the rails'. Young people were far more critical of Winehouse than might be expected, demonstrating that concerns about the influence of celebrity drug use and its impact on future health risk behaviour among young people may have been over-simplified and exaggerated. This study illustrates the need to understand young people and their frames of reference within popular culture when designing drug awareness information relevant to them. Furthermore, it indicates that critical media skills analysis may contribute to health risk education programmes related to drug use.

Fatigue crack initiation and propagation from defects in aluminium welds

Fatigue crack initiation and propagation in aluminium butt welds has been investigated. It is shown that the initiation of cracks from both buried defects and. from the weld reinforcement may be quantified by predictive laws based on either linear elastic fracture mechanics, or on Neuber's rule of stress and strain ooncentrations. The former is preferable on the grounds of theoretical models of crack tip plasticity, although either may be used as the basis of an effeotive design criteria against crack initiation. Fatigue lives fol1owing initiation were found to follow predictions based on the integration of a Paris type power law. The effect of residual stresses from the welding operation on both initiation and propagation was accounted for by a Forman type equation. This incorporated the notional stress ratio produced by the residual stresses after various heat treatments. A fracture mechanics analysis was found to be useful in describing the fatigue behaviour of the weldments at increased temperatures up to 300°C. It is pointed out, however, that the complex interaction of residual stresses, frequency, and changes in fracture mode necessitate great caution in the application of any general design criteria against crack initiation and growth at elevated. temperatures.