Fatigue crack propagation in some PM steels

Mechanisms of fatigue crack growth have been studied for a range of PM steels at relative densities of 0.90 and 1.0, for which strength, fracture toughness, and microstructural information was also available. It is shown that the Paris exponents for steady state crack growth are between 8 and 18 when ρr is approximately 0.9 but when ρr is approximately 1.0 the exponents are between 2.6 and 4.0, i.e in the range typical of wrought steels (2-4). At both densities, threshold stress intensities are between 5.5 and 10.8 MPa m1/2 when R = 0.1. Combinations of these thresholds and yield strengths are comparable with those for wrought steels. When R = 0.8, reductions in threshold to between 2.7 and 5 MPa m1/2 are attributed to crack closure effects. At ρr = 0.90, Fe-0.5C fails by progressive rupture of sinter necks. Astaloy A, with 0.2%C and 0.6%C, and Distaloy AB-0.6C have smaller plastic zone sizes and the cracks follow more difficult paths through particles as well as necks. When ρr is approximately 1.0, fracture is partially by true fatigue modes and partly by cleavage, the bursts of cleavage being more noticeable when Kmax is high.

The effect of frequency and microstructure on corrosion fatigue crack propagation in high strength aluminium alloys

Fatigue crack growth in high strength aluminium alloy 7150 commercial plate material has been studied in both laboratory air and acidified aqueous salt solution. The aggressive aqueous environment enhanced fatigue crack growth rates by up to an order in magnitude compared to laboratory air. The enhancement in fatigue crack growth rate was accompanied by evidence of embrittlement in the crack path, involving both brittle intergranular and transgranular failure modes. Both the enhancement of fatigue crack growth rates and the extent of intergranular growth modes are dependent on cyclic frequency which, along with the absence of a similar frequency effect in a spray-formed version of the material with a significantly different grain structure, supports a mechanism of grain boundary hydrogen diffusion for intergranular corrosion fatigue crack growth. The convergence of corrosion fatigue crack growth rates at high ΔK in both spray-formed and conventional plate materials coincides with the operation of identical transgranular corrosion fatigue modes dependent on strain-controlled hydrogen diffusion ahead of the crack tip. © 1997 Acta Metallurgica Inc.

Role of reinforcement/matrix interfacial strength in fatigue crack propagation in particulate SiC reinforced aluminum alloy 8090

A study has been made of the influence of the reinforcement/matrix interfacial strength on fatigue crack propagation in a powder metallurgy aluminum alloy 8090-SiC particulate composite. The interfacial region has been altered by two separate routes, the first involving aging of the 8090 matrix, with the subsequent formation of precipitate free zones at the boundaries, and the second consisting of oxidizing the surface of the SiC particles before their incorporation into the composite. In the naturally aged condition, oxidation of the SiC leads to a reduction in fatigue crack growth resistance at higher values of stress intensity range ΔK. This is due to a proportion of the crack growth occurring through voids formed in association with many of the weak SiC interfaces which have retained a layer of thick surface oxide after processing. On overaging no difference in crack growth rate is discernible between the oxidized and unoxidized SiC composites. It is proposed that this is due to similar levels of interfacial weakening having occurred in both composites, indicating that this is an important factor in the reduction of the high ΔK crack growth resistance of the unoxidized SiC composite on aging.

Fatigue crack propagation in nickel-base superalloys:effects of microstructure, load ratio, and temperature

The current state of knowledge and understanding of the long fatigue crack propagation behavior of nickel-base superalloys are reviewed, with particular emphasis on turbine disk materials. The data are presented in the form of crack growth rate versus stress intensity factor range curves, and the effects of such variables as microstructure, load ratio, and temperature in the near-threshold and Paris regimes of the curves, are discussed.

Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels

Fatigue crack initiation and propagation in duplex stainless steels are strongly affected by microstructure in both inert and aggressive environments. Fatigue crack growth rates in wrought Zeron 100 duplex stainless steel in air were found to vary with orientation depending on the frequency of crack tip retardation at ferrite/austenite grain boundaries. Fatigue crack propagation rates in 3.5% NaCl solution and high purity water are increased by hydrogen assisted transgranular cyclic cleavage of the ferrite. The corrosion fatigue results are interpreted using a model for the cyclic cleavage mechanism.

Fatigue crack propagation mechanisms in a thermally aged duplex stainless steel

Zeron 100 duplex stainless steel is susceptible to embrittlement following ageing at temperatures between 350 °C and 450 °C. The embrittlement is associated with cleavage of the age-hardened ferrite phase, initiated by deformation twinning. This can result in order of magnitude increases in the fatigue crack propagation rate. The effects of ageing on the mechanisms of fatigue crack propagation in Zero 100 are investigated, and a quantitative model is developed, accounting for the effects of hardness, temperature, stress level and microstructure on the fatigue crack growth rate. © 1994.

Effects of dynamic strain ageing on fatigue crack propagation and threshold behaviour in a Ni-base superalloy

In the temperature range 200-400 degree C the Ni-base superalloy, N901, develops marked dynamic strain ageing effects in its tensile behavior. These include inverse strain rate sensitivity, especially in UTS values, strongly serrated stress-strain curves and a heavily sheared failure mode at the higher test-temperatures. As for steels these effects seem to be due to interactions between the dislocations and the interstitial carbon atoms present. The results of tensile and fatigue threshold tests carried out between 20 degree C and 420 degree C are reported and the fatigue behavior is discussed in terms of the effects of surface roughness induced closure, temperature and strain aging interactions.

Effect of mean stress on hydrogen assisted fatique crack propagation in duplex stainless steel

Hydrogen assisted subcritical cleavage of the ferrite matrix occurs during fatigue of a duplex stainless steel in gaseous hydrogen. The ferrite fails by a cyclic cleavage mechanism and fatigue crack growth rates are independent of frequency between 0.1 and 5 Hz. Macroscopic crack growth rates are controlled by the fraction of ferrite grains cleaving along the crack front, which can be related to the maximum stress intensity, Kmax. A superposition model is developed to predict simultaneously the effects of stress intensity range (ΔK) and K ratio (Kmin/Kmax). The effect of Kmax is rationalised by a local cleavage criterion which requires a critical tensile stress, normal to the {001} cleavage plane, acting over a critical distance within an embrittled zone at the crack tip. © 1991.

Temperature effects on the mechanism of time independent hydrogen assisted fatigue crack propagation in steels

The effects of temperature on hydrogen assisted fatigue crack propagation are investigated in three steels in the low-to-medium strength range; a low alloy structural steel, a super duplex stainless steel, and a super ferritic stainless steel. Significant enhancement of crack growth rates is observed in hydrogen gas at atmospheric pressure in all three materials. Failure occurs via a mechanism of time independent, transgranular, cyclic cleavage over a frequency range of 0.1-5 Hz. Increasing the temperature in hydrogen up to 80°C markedly reduces the degree of embrittlement in the structural and super ferritic steels. No such effect is observed in the duplex stainless steel until the temperature exceeds 120°C. The temperature response may be understood by considering the interaction between absorbed hydrogen and micro-structural traps, which are generated in the zone of intense plastic deformation ahead of the fatigue crack tip. © 1992.

The role of primary carbides in fatigue crack propagation in aeroengine bearing steels

Fatigue crack propagation, tensile and fracture toughness data for four aeroengine bearing steels are reported. The steels involved are the through-hardened tool steels 18-4-1 (T1) and M50, and two similar carburized steels, RBD and Volvic. Crack growth data have been obtained at 20 °C and 280 °C to cover the range of oil temperatures experienced in aeroengine bearing operations. At 20 °C threshold ΔK values (ΔKth) ranged between 3.5 and 4.5 MPa √m with Paris exponents (m) of between 2.0 and 3.5. The lowest m-values were seen in the carburizing steels, which also exhibited lower Paris regime crack growth rates than M50 and 18-4-1. For all the steels, growth rates were higher at 280 °C,than 20 °C, although there was a slight tendency for ΔKth to increase, probably associated with oxide-induced closure at 280 °C. The effects of primary carbides, strength and toughness on fatigue crack growth behaviour are discussed, in relation to the importance of static-mode cracking. © 1990.

Effects of microstructure, temperature and R-ratio on fatigue crack propagation and threshold behaviour in two Ni-base alloys

Fatigue crack propagation and threshold data for two Ni-base alloys, Astroloy and Nimonic 901, are reported. At room temperature the effect which altering the load ratio (R-ratio) has on fatigue behaviour is strongly dependent on grain size. In the coarse grained microstructures crack growth rates increase and threshold values decrease markedly as R rises from 0. 1 to 0. 8, whereas only small changes in behaviour occur in fine grained material. In Astroloy, when strength level and gamma grain size are kept constant, there is very little effect of processing route and gamma prime distribution on room temperature threshold and crack propagation results. The dominant microstructural effect on this type of fatigue behaviour is the matrix ( gamma ) grain size itself.

The mechanics of creep crack growth in a Magnox alloy

Magnox AL80 has been used for a study of creep crack propagation. A number of variables have been considered such as specimen geometry,notch root radius, material thickness, creep prestrain and stress level.The work has covered the material behaving under two values of the creep exponent, n=3.5 and n=7, according to the stress level. As well as observing initiation times and crack growth rates, scribed grids have been used to examine the near crack tip strain levels and distributions. It was shown that estimations of COD from notch flank opening can give misleading indications of material behaviour and that a more informative method was to monitor displacements in the material surrounding the crack tip. Strong evidence was found for crack advance being displacement controlled, however it was shown that the COD approach should be considered geometry dependant. The summation of ∈xx and ∈yy provided the most successful description of crack advance as it produced a single value that described propagation in all the cases concidered. The strain distributions indicates that σyy was related to distance from a point ahead of the crack tip by the exponent - (l/n+l) and that σxx is proportional to σyy. The constraint stresses arising in the DEN and CN specimens were evaluated. Initiation time was found to be principally affected by the stress level but was modified by the constraints arising from specimen geometry. Crack growth was found not to obey either the empirical K or σpett relationships but was reviewed in context of the observed strain behaviour.

H-induced platelet and crack formation in hydrogenated epitaxial Si/Si0.98 B0.02 /Si structures

An approach to transfer a high-quality Si layer for the fabrication of silicon-on-insulator wafers has been proposed based on the investigation of platelet and crack formation in hydrogenated epitaxialSi/Si0.98B0.02/Si structures grown by molecular-beam epitaxy. H-related defect formation during hydrogenation was found to be very sensitive to the thickness of the buried Si0.98B0.02 layer. For hydrogenated Si containing a 130nm thick Si0.98B0.02 layer, no platelets or cracking were observed in the B-doped region. Upon reducing the thickness of the buried Si0.98B0.02 layer to 3nm, localized continuous cracking was observed along the interface between the Si and the B-doped layers. In the latter case, the strains at the interface are believed to facilitate the (100)-oriented platelet formation and (100)-oriented crack propagation.

The influence of a coal gasifier atmosphere on fatigue crack growth rates in BS 4360 steel

Fatigue crack growth tests have been carried out in a number of gaseous environments in order to assess their effects on the crack propagation resistance of BS 4360 grade 50EE, a weldable structural steel. Crack growth rates at 25 °C are up to 20 times higher in hydrogen than in air, but there is no effect when hydrogen is present as a 30% constituent of a simplified product gas (SPG). Indeed, crack growth rates in such a mixture are slightly lower than those measured in air, being comparable with those observed in an inert environment. The other gases present in the SPG are CO, CO2 and CH4, and it is probable that the carbon monoxide is responsible for nullifying the embrittling effects of hydrogen, by preferentially adsorbing on to the surface of the steel and thus blocking hydrogen entry. Experimental observations suggest that oxygen has the same effect when small quantities are allowed to diffuse into a non-flowing hydrogen environment around a propagating crack. The results are encouraging in terms of the suitability of conventional structural steels such as BS 4360 for gas plant applications. The gas mixtures present in such an environment would not have the severe detrimental effects on fatigue crack growth resistance which result from the presence of 'pure' hydrogen. © 1993.