Nano-indentation measurement of oxide layers formed in LBE on F/M steels

Ferritic/martensitic (F/M) steels (T91, HT-9, EP 823) are candidate materials for future liquid lead or lead bismuth eutectic (LBE) cooled nuclear reactors. To understand the corrosion of these materials in LBE, samples of each material were exposed at 535 °C for 600 h and 200 h at an oxygen content of 10 wt%. After the corrosion tests, the samples were analyzed using SEM, WDX and nano-indentation in cross section. Multi-layered oxide scales were found on the sample surfaces. The compositions of these oxide layers are not entirely in agreement with the literature. The nano-indentation results showed that the E-modulus and hardness of the oxide layers are significantly lower than the values for dense bulk oxide materials. It is assumed that the low values stem from high porosity in the oxide layers. Comparison with in-air oxidized steels show that the E-modulus decreases with increasing oxide layer thickness. © 2008 Elsevier B.V. All rights reserved.

Fundamental mechanisms affecting service performance of electroplated plastics

Ten grades of ABS and four grades of polypropylene have been plated with various copper + nickel + chromium coatings and subjected to a variety of tests. In corrosion studies the pre-electroplating sequence and plastics type have been shown to influence performance. One ABS pre-electroplating sequence was consistently associated with better corrosion performance; two factors were responsible for this, namely the more severe nature of the etch and the relatively more noble electroless nickel. Statistical analysis has indicated that order of severity of the corrosion tests was static-mobile-CASS, the latter being the least severe. In mechanical tests two properties of ABS and polypropJylene, ductility and impact strength, have been shown to be adversely affected when electrodeposited layers were applied. The cause of this is due to a complex of factors, the most important of which is the notch sensitivity of the plastics. Peel adhesion has been studied on flat panels and also on ones which had a ridge and a valley moulded into one face. High adhesion peaks occurred on the flat face at regions associated with the ridge and valley. The local moulding conditions induced by the features were responsible for this phenonemon. In the main programme the thermal cycling test was shown to be more likely than the peel adhesion test to give an indication of the service performance of electroplated plastics.

Influence of pretreatment on corrosion behaviour of duplex zinc/polymer coatings on steel substrates

An investigation has been undertaken to determine the major factors influencing the corrosion resistance of duplex-zinc coatings on steel substrates.Premature failure of these systems has been attributed to the presence of defects such as craters and pinholes in the polymer film and debonding of the polymer film from the zinc substrate.Defects found on commercially produced samples have been carefully characterised using metallographic and scanning electron microscopy techniques. The influence of zinc substrate surface roughness, polymer film thickness and degassing of conversion coatings films on the incidence of defects has been determined.Pretreatments of the chromate, chromate-phosphate, non chromate, and alkali-oxide types were applied and the conversion coatings produced characterised with respect to their nature and composition. The effect of degassing on the properties of the films was also investigated. Electrochemical investigations were carried out to determine the effect of the presence of the eta or zeta phase as the outermost layer of the galvanized coating.Flow characteristics of polyester on zinc electroplated hot-dip continuous and batch galvanized and zinc sprayed samples were investigated using hot-stage microscopy. The effects of different pretreatments and degassing after conversion coating formation on flow characteristics were determined.Duplex coatings were subjected to the acetic acid salt spray test. The effect on adhesion was determined using an indentation debonding test and the results compared with those obtained using cross-cut/peel and pull-off tests. The locus of failure was determined using scanning electron microscopy and X-ray photoelectron spectroscopy techniques.