Bio-inspired carbon electro-catalysis for the oxygen reduction reaction

We report the synthesis, characterisation and catalytic performance of two nature-inspired biomass-derived electro-catalysts for the oxygen reduction reaction in fuel cells. The catalysts were prepared via pyrolysis of a real food waste (lobster shells) or by mimicking the composition of lobster shells using chitin and CaCO3 particles followed by acid washing. The simplified model of artificial lobster was prepared for better reproducibility. The calcium carbonate in both samples acts as a pore agent, creating increased surface area and pore volume, though considerably higher in artificial lobster samples due to the better homogeneity of the components. Various characterisation techniques revealed the presence of a considerable amount of hydroxyapatite left in the real lobster samples after acid washing and a low content of carbon (23%), nitrogen and sulphur (<1%), limiting the surface area to 23 m2/g, and consequently resulting in rather poor catalytic activity. However, artificial lobster samples, with a surface area of ≈200 m2/g and a nitrogen doping of 2%, showed a promising onset potential, very similar to a commercially available platinum catalyst, with better methanol tolerance, though with lower stability in long time testing over 10,000 s.

All-fiber polarization locked vector soliton laser using carbon nanotubes

We report an all-fiber mode-locked erbium-doped fiber laser (EDFL) employing carbon nanotube (CNT) polymer composite film. By using only standard telecom grade components, without any complex polarization control elements in the laser cavity, we have demonstrated polarization locked vector solitons generation with duration of ~583fs , average power of ~3 mW (pulse energy of 118pJ ) at the repetition rate of ~25.7 MHz.

Catalytic systems based on carbon fiber materials for the low-temperature oxidation of carbon monoxide

New heterogenized catalytic systems for the low-temperature oxidation of CO were synthesized by supporting solutions of Pd, Cu, and Fe salts on carbon fibrous materials (carbopon and busofit). The carbon supports were studied by elemental analysis, SEM, TGA, and TPD. The effects of the nature of the support, the concentration and composition of the active component, and the conditions of preparation on the efficiency of the catalytic system were studied. It was ascertained that attenuation of hydrophilic properties of the support led to the decrease in system activity. The investigation of the catalysts by XPS showed that sample treatment in the reaction medium results in redistribution of the components of the active phase in the near-surface layer of the catalyst. The catalytic system based on carbon fibrous material carbopon prepared by supporting active components (Pd, Cu, and Fe salts) in three stages with intermediate activation in the reaction medium ensures 95% conversion of CO under respiratory conditions, and is promising for the design of the main element of breathing masks on its basis.

Supercritical water gasification of RDF and its components over RuO2/γ-Al2O3 catalyst:new insights into RuO2 catalytic reaction mechanisms

Five samples including a composite refuse derived fuel (RDF) and four combustible components of municipal solid wastes (MSW) have been reacted under supercritical water conditions in a batch reactor. The reactions have been carried out at 450 °C for 60 min reaction time, with or without 20 wt% RuO2/gamma-alumina catalyst. The reactivities of the samples depended on their compositions; with the plastic-rich samples, RDF and mixed waste plastics (MWP), giving similar product yields and compositions, while the biogenic samples including mixed waste wood (MWW) and textile waste (TXT) also gave similar reaction products. The use of the heterogeneous ruthenium-based catalyst gave carbon gasification efficiencies (CGE) of up to 99 wt%, which was up by at least 83% compared to the non-catalytic tests. In the presence of RuO2 catalyst, methane, hydrogen and carbon dioxide became the dominant gas products for all five samples. The higher heating values (HHV) of the gas products increased at least two-fold in the presence of the catalyst compared to non-catalytic tests. Results show that the ruthenium-based catalyst was active in feedstock steam reforming, methanation and possible direct hydrogenolysis of C-C bonds. This work provides new insights into the catalytic mechanisms of RuO2 during SCWG of carbonaceous materials, along with the possibility of producing high yields of methane from MSW fractions.

Passive mode locking in erbium-doped fibre laser by carbon nanotubes

Passively mode locked fibre lasers have a variety of applications ranging from telecommunication to medical photonics. Carbon nanotubes (CNTs) have attracted recently a great deal of attention as a promising solution for saturable absorber elements required for laser mode locking (see e.g. [1-3] and references therein). CNTs can be used as a saturable absorber in passively mode locked fibre laser directly [1,2] or as a CNTs polymer composites [3]. An attractive feature of CNT-based solutions in fibre lasers is a possibility to maintain the compactness, robustness of all-fibre format and low cost through using all standard telecom compatible components. The two important technical challenges in such type of lasers are: (i) to achieve stable polarization properties of the generated radiation without using complex control elements, and, (ii) to avoid low frequency instabilities of the mode-locked pulse train. In this paper we report results of the experiments on mode-locked soliton fibre laser using the following standard components: 1m of highly doped erbium fibre (Liekki Er80-8/125) serves as the gain medium with nominal absorption of 80 dB/m at 1530 nm; a 976 nm laser diode providing up to 310mW power is used to pump the laser via a 980/1550 wavelength division multiplexing; an isolator is employed to ensure single direction oscillation; SMF-28 is used to create necessary amount of anomalous dispersion to form soliton pulse making the total cavity length around 7.83 m; the CNT-polyvinyl alcohol polymer saturable absorber sandwiched in the FC/PC connector is used as a mode-locker device (see [3] for details). © 2011 IEEE.