3D culture of bone-derived cells immobilised in alginate following light-triggered gelation

Photoreactive liposomes have been exploited as a means of developing 3D tissue constructs. Liposomes formulated using the photosensitive lipid 1,2-bis(4-(n-butyl)phenylazo-4′-phenylbutyroyl)phosphatidylcholine (Bis Azo PC), which undergoes conformational change on stimulation with long wavelength ultraviolet light, were prepared with entrapped CaCl2 before being incorporated into a 4% alginate solution. It was shown that stimulation of the photosensitive lipid using a light emitting diode (LED) (peak emission at 385 nm, dose equivalent to 9 mJ/cm2) caused the release of liposome-entrapped CaCl2, resulting in cross-linking of the alginate solution and immobilisation of bone-derived cells over a range of seeding densities, approximately 97% of which remained viable for periods of up to 14 days in culture. Entrapment volumes of a variety of liposome types were evaluated and interdigitating fusion vesicles were identified as having the highest payload (24%), however the inclusion of cholesterol as a means of shifting Bis Azo PC sensitivity into the visible light wavelengths resulted in an approximately 10-fold reduction in calcium entrapment. This application of light-sensitised liposomes offers the potential to create complex tissue engineering substrates containing cells immobilised in precise locations, in contrast with substrates onto which cells are seeded post-production. © 2007 Elsevier B.V. All rights reserved.

In situ mineralization by the release of calcium and phosphate ions from nanogels

Biomimetic hydroxyapatite was synthesized by the controlled release of calcium and phosphate ions from poly(N-isopropylacrylamide-co-acrylic acid) (poly(NIPAAm-co-AA)) nanogels. Mixing nanogels containing calcium chloride (CaCl2 ·2H2O) and nanogels containing sodium hydrogen phosphate (Na2HPO4·2H2O) in simulated body fluid (SBF) at physiological conditions of 37 °C and pH 7.4, biomimetic hydroxyapatite was obtained. By studying separately the loading and controlled release of the salts from the nanogels, adequate conditions were chosen to synthesize the hydroxyapatite: Calcium loaded (Ca-loaded) nanogels (1000 mg/ml; 400:3) and inorganic phosphate loaded (Pi-loaded) nanogels (90 mg/ml; 12:1) in a ratio of 2:1 were placed in SBF solution. The obtained powders characterization showed that a low crystalline and substituted hydroxyapatite similar to bone apatite was formed. Such a strategy could be used in medical and dental procedures to induce rapid inorganic mineral formation from a nanogel-containing biomaterial. © 2012 American Scientific Publishers. All rights reserved.