Increasing the fracture toughness of silicon by ion implantation

Previous studies have shown that moderate doses of radiation can lead to increased fracture toughness in ceramics. An experimental investigation was conducted to determine the effects of ion implantation on fracture toughness in silicon. Specimens implanted with Ne showed increased fracture toughness, over the entire range of implantations tested. Using ions of various energies to better distribute implantation damage further increased the fracture toughness even though the region of amorphous damage was slightly decreased. The implantation damage accumulated in a predictable manner so that fracture toughness could be optimized.

The relationship between fracture toughness and microstructure in titanium alloys

Linear Elastic Fracture Mechanics has been used to study the microstructural factors controlling the strength and toughness of two alpha-beta, titanium alloys. Fracture toughness was found to be independent of orientation for alloy Ti/6A1/4-V, but orientation dependent for IMI 700, bend and tension specimens giving similar toughness values. Increasing the solution temperature led to the usual inverse relationship between strength and toughness, with toughness becoming a minimum as the beta transus was approached. The production of a double heat treated microstructure led to a 100% increase in toughness in the high strength alloy and a 20% increase in alloy Ti/6A1/4V, with little decrease in strength. The double heat treated microstruoture was produced by cooling from the beta field into the alpha beta field, followed. by conventional solution treatment and ageing. Forging above the beta transus led to an increase in toughness over alpha beta forging in the high strength alloy, but had little effect on the toughness of Ti/6A1/4V. Light and electron microscopy showed that the increased toughness resulted from the alpha phase being changed from mainly continuous to a discontinuous platelet form in a transformed beta matrix. Void formation occurred at the alpha-beta interface and crack propagation was via the interface or across the platelet depending on which process required the least energy. Varying the solution treatment temperature produced a varying interplatelet spacing and platelet thickness. The finest interplatelet spacing was associated with the highest toughness, since a higher applied stress was required to give the necessary stress concentration to initiate void formation. The thickest alpha platelet size gave the highest toughness which could be interpreted in terms of Krafftt's "process zone size" and the critical crack tip displacement criterion by Hahn and Rosenfield from an analysis by Goodier and Field.

The fracture toughness of a range of cast steels

A range of plain carbon, carbon-manganese and low alloy cast steels were tested in order to determine their various fracture toughness values under elastic and elastic-plastic conditions. The main fracture toughness parameters which are considered are (1) Linear Elastic Fracture Mechanics (LEFM), (2) the J-Contour Integral, and (3) Crack Opening Displacement (COD). Results are obtained from fracture toughness specimens of various dimensions and the relevance of the validity criteria to cast steels is considered in some detail. In addition, the effect of casting position on specimen toughness values was noted. Valid KIC results according to LEFM, were obtained for three of the eight cast steels tested. Although KIC values from LEFM were not obtained from the remaining five steels, critical COD and J-integral values were determined. It is postulated that these values and particularly the critical J values can be used, with confidence for material selection or in defect tolerance calculations using these steels. Toughness values were found to vary with casting position in several of the steels tested and the possible reasons for such variations are discussed in the Thesis.

Fracture toughness of a series of high chromium abrasion resistant alloys

The fracture properties of a series of alloys containing 15% chromium and 0.8 to 3.4% carbon are investigated using strain fracture toughness testing techniques. The object of the work is to apply a quantitative method of measuring toughness to abrasion resistant materials, which have previously been assessed on an empirical basis; and to examine the relationship between microstructure and K10 in an attempt to improve the toughness of inherently brittle materials. A review of the relevant literature includes discussion of the background to the alloy series under investigation, a survey of the development of fracture mechanics and the emergence of K10 as a toughness parameter. Metallurgical variables such as composition, heat treatment, grain size, and hot working are ???? to relate microstructure to toughness, and fractographic evidence is used to substantiate the findings. The results are applied to a model correlating ductile fracture with plastic strain instability, and the nucleation of voids. Strain induced martensite formation in austenitic structures is analysed in terms of the plastic energy dissipation mechanisms operating at the crack tip. Emphasis is placed on the lower carbon alloys in the series, and a composition put forward to optimise wear resistance and toughness. The properties of established competitive materials are compared to the proposed alloy on a toughness and cost basis.

Fracture toughness of some high density PM steels

Tensile strengths, impact energies, and fracture toughness data are presented for pure Fe-0.5 C, Astaloy A with 0.2 and 0.6%C, and for Distaloy AB-0.6%C at relative densities of about 0.9, achieved by conventional pressing and sintering, and at close to 1.0, achieved by powder forging. At low relative density, properties are controlled by sizes of sinter necks; it is postulated that toughness scales as (x/a)4, x/a being the ratio of neck diameter to particle diameter. At high relative density, microvoid coalescence and good toughness is observed for low strength microstructures whereas cleavage and poor toughness is a concomitant of high strength.

Fracture toughness of SIC, Si3N4, and sialon ceramics using controlled surface flaws

Knoop and Vickers indentation cracks have frequently been used as model 'precracks' in ceramic bend specimens for fracture toughness (K1c) determination. Indentation residual stress reduces the measured K1c but can be removed or accounted for by grinding, annealing, or modelling. Values of K1c are obtained for four materials using Vickers indentations and an improved stress intensity factor. Methods for residual stress removal or incorporation are compared, and the most reliable stress removal alternative is identified for each material. © 1996 The Institute of Materials.

The effect of microstructure on the fracture toughness of a metal-matrix composite

The fracture behaviour and plane strain fracture toughness, KIC, of four 8090-based metal-matrix composites containing 20 weight % SiC particles, 3, 6 and 23 μm in diameter, has been evaluated as a function of matrix ageing condition. Toughness values are found to be almost independent of reinforcement size. Ageing at 170°C results in a monotonic decrease in toughness with increasing strength up to the peak condition, with no subsequent recovery in toughness on overageing. However, unlike reinforced 8090, the composites are not found to be susceptible to intergranular embrittlement on overageing. The observed trends are found to be independent of reinforcement size. These findings are explained in terms of the strength, work hardening behaviour and nature and distribution of void-nucleating particles in the matrix. © 1993.

Effects of crack length and shape on the fracture toughness of a high strength steel 300m

The results of fracture toughness tests on a high strength steel 300m are presented. These results show (i) that in the presence of through-thickness cracks the toughness remains constant down to (a/W)-ratios as low as 0.01 and failure loads up to 0.85σy, and (ii) that the material is more resistant to crack growth when the cracks are semi-elliptical in shape, giving a toughness value which is almost 25 per cent higher than the through-thickness one. Three independent stress analyses are used to obtain stress intensity values for the semi-elliptical cracks and additional confirmation of the increase in toughness comes from stretch zone measurements.

Effect of dopants on the fracture toughness of silicon

Fracture experiments were conducted on p-type and n-type Si in the presence and absence of hydrogen. It was found that fracture toughness is slightly less than the fracture toughness of n-type silicon. Annealing silicon in an Ar/H atmosphere gave a hydrogen concentration of less than 0.1 ppm, which did not have any measurable effect on fracture toughness. Likewise, the exposure of pre-cracked specimens to H did not cause any measurable change in fracture toughness.

The effects of metallurgical variables on the mechanical properties of high-chromium cast irons

The.use of high-chromium cast irons for abrasive wear resistance is restricted due to their poor fracture toughness properties. An.attempt was made to improve the fracture characteristics by altering the distribution, size and.shape of the eutectic carbide phase without sacrificing their excellent wear resistance. This was achieved by additions of molybdenum or tungsten followed by high temperature heat treatments. The absence of these alloying elements or replacement of them with vanadium or manganese did not show any significant effect and the continuous eutectic carbide morphology remained the same after application of high temperature heat treatments. The fracture characteristics of the alloys with these metallurgical variables were evaluated for both sharp-cracks and blunt notches. The results were used in conjunction with metallographic and fractographic observations to establish possible failure mechanisms. The fracture mechanism of the austenitic alloys was found to be controlled not only by the volume percent but was also greatly influenced by the size and distribution of the eutectic carbides. On the other hand, the fracture mechanism of martensitic alloys was independent of the eutectic carbide morphology. The uniformity of the secondary carbide precipitation during hardening heat treatments was shown to be a reason for consistant fracture toughness results being obtained with this series of alloys although their eutectic carbide morphologies were different. The collected data were applied to a model which incorporated the microstructural parameters and correlated them with the experimentally obtained valid stress intensity factors. The stress intensity coefficients of different short-bar fracture toughness test specimens were evaluated from analytical and experimental compliance studies. The.validity and applicability of this non-standard testing technique for determination of the fracture toughness of high-chromium cast irons were investigated. The results obtained correlated well with the valid results obtained from standard fracture toughness tests.

Ductile fracture mechanisms in a structural steel

Microstructural fracture processes in a BS4360 Grade 50D structural steel with lower sulphur content were studied in smooth tensile specimen tests and Charpy-size bend bar tests. Based on the experimental analysis, an experimental void growth relation with the plastic strain and stress triaxiality and multiplying factor on void growth were determined. Experimental results show that the void growth relation can be reasonably used to estimate the constraint in the specimens containing the notch or crack, also they can be used to evaluate the variations of the stress triaxiality in front of the notch and crack tip under general yielding condition. Side-grooves obviously increase the constraint of the CVN specimens. Strain hardening leads to increasing the stress triaxiality, and decelerating the net void growth. This is especially true for the values of stress triaxiality more than about one. Additionally, the effect of the stress triaxiality on the critical void growth corresponding to the onset of ductile tearing was preliminarily investigated. In this work, a large number of smaller specimens were tested to investigate the ductile-brittle transition behaviour of the structural steel. A void growth rate explanation was suggested for evaluating the temperature transition behaviour. The elastic-plastic fracture tough-ness values based on small specimen tests, such as pre-cracked side-grooved bending specimen and short bar tensile specimen, may give large overestimates of the plane strain fracture toughness.