Modification of the B2-type matrix of aluminide diffusion coatings on nickel-base superalloys-bulk aluminide analogues

Pack aluminide coating is a useful method for conferring oxidation resistance on nickel-base superalloys. Nominally, these coatings have a matrix composed of a Ni-Al based B2-type phase (commonly denoted as Β). However, following high-temperature exposure in oxidative envi-ronments, aluminum is depleted from the coating. Aluminum depletion in turn, leads to de-stabilization of the Β phase, resulting in the formation of a characteristic lathlike Β-derivative microstructure. This article presents a transmission electron microscopy study of the formation of the lathlike Β-derivative microstructure using bulk nickel aluminides as model alloys. In the bulk nickel aluminides, the lathlike microstructure has been found to correspond to two distinct components: L10-type martensite and a new Β derivative. The new Β derivative is characterized and the conditions associated with the presence of this feature are identified and compared with those leading to the formation of the L10 martensitic phase. © 1995 The Minerals, Metals & Material Society.

Microstructural study of aluminide surface coatings on single crystal nickel base superalloy substrates

Aluminide diffusion coatings are frequently employed to enhance the oxidation resistance of nickel base superalloys. However, there is a concern that the presence of an aluminide coating could influence the properties of the coated superalloy, especially in respect of fatigue behaviour. To understand the nature of the effects of surface coatings on the fatigue properties of superalloys, an understanding of microstructural development within both the coating and the coating/substrate interfacial zone during high temperature fatigue testing is necessary. This paper is concerned with microstructural changes in aluminide diffusion coatings on single crystal γ′ strengthened superalloy substrates during the course of high temperature fatigue testing. The 'edge on' transmission electron microscopy technique is employed to study cross-sections of two stage (aluminization plus diffusion treatment) coated superalloy samples. The paper examines the degradation of the coating produced by phase transformations induced by loss of aluminum from the coating and/or aging of the coating. Aluminum removal both by interdiffusion with the substrate and by oxidation of the coating surface is considered. Microstructural development in the portion of the substrate influenced by interdiffusion with the coating is also discussed.

The icephobic performance of alkyl-grafted aluminum surfaces

This work analyzes the anti-icing performance of flat aluminum surfaces coated with widely used alkyl-group based layers of octadecyltrimethoxysilane, fluorinated alkylsilane and stearic acid as they are subjected to repeated icing/deicing cycles. The wetting properties of the samples upon long-term immersion in water are also evaluated. The results demonstrate that smooth aluminum surfaces grafted with alkyl groups are prone to gradual degradation of their hydrophobic and icephobic properties, which is caused by interactions and reactions with both ice and liquid water. This implies that alkyl-group based monolayers on aluminum surfaces are not likely to be durable icephobic coatings unless their durability in contact with ice and/or water is significantly improved.