Supercritical water gasification of RDF and its components over RuO2/γ-Al2O3 catalyst:new insights into RuO2 catalytic reaction mechanisms

Five samples including a composite refuse derived fuel (RDF) and four combustible components of municipal solid wastes (MSW) have been reacted under supercritical water conditions in a batch reactor. The reactions have been carried out at 450 °C for 60 min reaction time, with or without 20 wt% RuO2/gamma-alumina catalyst. The reactivities of the samples depended on their compositions; with the plastic-rich samples, RDF and mixed waste plastics (MWP), giving similar product yields and compositions, while the biogenic samples including mixed waste wood (MWW) and textile waste (TXT) also gave similar reaction products. The use of the heterogeneous ruthenium-based catalyst gave carbon gasification efficiencies (CGE) of up to 99 wt%, which was up by at least 83% compared to the non-catalytic tests. In the presence of RuO2 catalyst, methane, hydrogen and carbon dioxide became the dominant gas products for all five samples. The higher heating values (HHV) of the gas products increased at least two-fold in the presence of the catalyst compared to non-catalytic tests. Results show that the ruthenium-based catalyst was active in feedstock steam reforming, methanation and possible direct hydrogenolysis of C-C bonds. This work provides new insights into the catalytic mechanisms of RuO2 during SCWG of carbonaceous materials, along with the possibility of producing high yields of methane from MSW fractions.

Studies on the deactivation and reactivation of spent hydroprocessing catalyst

A study is reported on the deactivation of hydroprocessing catalysts and their reactivation by the removal of coke and metal foulants. The literature on hydrotreating catalyst deactivation by coke and metals deposition, the environmental problems associated with spent catalyst disposal, and its reactivation/rejuvenation process were reviewed. Experimental studies on catalyst deactivation involved problem analysis in industrial hydroprocessing operations, through characterization of the spent catalyst, and laboratory coking studies. A comparison was made between the characteristics of spent catalysts from fixed bed and ebullating bed residue hydroprocessing reactor units and the catalyst deactivation pattern in both types of reactor systems was examined. In the laboratory the nature of initial coke deposited on the catalyst surface and its role on catalyst deactivation were studied. The influence of initial coke on catalyst surface area and porosity was significant. Both catalyst acidity and feedstock quality had a remarkable influence on the amount and the nature of the initial coke. The hydroenitrogenation function (HDN) of the catalyst was found to be deactivated more rapidly by the initial coke than the hydrodesulphurization function (HDS). In decoking experiments, special attention was paid to the initial conditions of coke combustion, since the early stages of contact between the coke on the spent catalyst surface and the oxygen are crucial in the decoking process. An increase in initial combustion temperature above 440oC and the oxygen content of the regeneration gas above 5% vanadium led to considerable sintering of the catalyst. At temperatures above 700oC there was a substantial loss of molybdenum from the catalyst, and phase transformations in the alumina support. The preferred leaching route (coked vs decoked form of spent catalyst) and a comparison of different reagents (i.e., oxalic acid and tartaric acid) and promoters (i.e., Hydrogen Peroxide and Ferric Nitrate) for better selectivity in removing the major foulant (vanadium), characterization and performance evaluation of the treated catalysts and modelling of the leaching process were addressed in spent catalyst rejuvenation studies. The surface area and pore volume increased substantially with increasing vanadium extraction from the spent catalyst; the HDS activity showed a parallel increase. The selectivity for leaching of vanadium deposits was better, and activity recovery was higher, for catalyst rejuvenated by metal leaching prior to decoking.

Zirconia and alumina based catalysts for steam reforming of naphthalene

The present paper deals with experimentation of ZrO2 and Al2O3-supported catalysts for conversion of naphthalene, chosen as tar model compound of pyrolysis or gasification syngas. In particular, the reforming capacity of active metals and promoters such as Co, Ni, Fe, Cr, Ce and Pt was tested in a fixed bed reactor at temperature from 400 to 900 °C. As regards ZrO2-supported catalysts, the best results were achieved by the Ni/Fe/Pt catalyst with 96% naphthalene conversion, 78% and 280% as CO and H2 production yield at 800 °C. Regarding Al2O3-supported catalysts, they were more active on average than the zirconia ones, achieving a very good performance even at 500 °C (90–100% naphthalene conversion, 30–40% CO yield and 300–350% H2 yield at 550 °C). Influence of different amounts of alumina, montmorillonite and carbon on carrier composition as well as pellets’ size were also studied. Both zirconia and alumina catalysts showed deactivation at higher temperatures due to coke deposition, resulting in a strong H2 production drop. Regeneration of catalysts by O2 and steam as well as activation by H2 were also studied. The activated catalyst was able to convert more than 99% naphthalene at 450 °C with a CO and H2 production yield of 26% and 420%, respectively.

Facile route to conformal hydrotalcite coatings over complex architectures:a hierarchically ordered nanoporous base catalyst for FAME production

An alkali- and nitrate-free hydrotalcite coating has been grafted onto the surface of a hierarchically ordered macroporous-mesoporous SBA-15 template via stepwise growth of conformal alumina adlayers and their subsequent reaction with magnesium methoxide. The resulting low dimensional hydrotalcite crystallites exhibit excellent per site activity for the base catalysed transesterification of glyceryl triolein with methanol for FAME production.

Alumina-grafted SBA-15 as a high performance support for Pd-catalysed cinnamyl alcohol selective oxidation

Ultrathin alumina monolayers grafted onto an ordered mesoporous SBA-15 silica framework afford a composite catalyst support with unique structural properties and surface chemistry. Palladium nanoparticles deposited onto Al-SBA-15 via wet impregnation exhibit the high dispersion and surface oxidation characteristic of pure aluminas, in conjunction with the high active site densities characteristic of thermally stable, high-area mesoporous silicas. This combination confers significant rate enhancements in the aerobic selective oxidation (selox) of cinnamyl alcohol over Pd/Al-SBA-15 compared to mesoporous alumina or silica supports. Operando, liquid-phase XAS highlights the interplay between dissolved oxygen and the oxidation state of palladium nanoparticles dispersed over Al-SBA-15 towards on-stream reduction: ambient pressures of flowing oxygen are sufficient to hinder palladium oxide reduction to metal, enabling a high selox activity to be maintained, whereas rapid PdO reduction and concomitant catalyst deactivation occurs under static oxygen. Selectivity to the desired cinnamaldehyde product mirrors these trends in activity, with flowing oxygen minimising CO cleavage of the cinnamyl alcohol reactant to trans-β-methylstyrene, and of cinnamaldehyde decarbonylation to styrene. © 2013 Elsevier B.V.

Propene combustion over a model Pt/Al2O3/NiAl{110} catalyst

The genesis of a catalytically active model Pt/Al2O3/NiAl{110} oxidation catalyst is described. An ultrathin, crystalline γ-Al2O3 film was prepared via direct oxidation of a NiAl{110} single-crystal substrate. The room-temperature deposition of Pt clusters over the γ-Al2O3 film was characterised by LEED, AES and CO titration and follows a Stranski–Krastanov growth mode. Surface sulfation was attempted via SO2/O2 adsorption and thermal processing over bare and Pt promoted Al2O3/NiAl{110}. Platinum greatly enhances the saturation SOx coverage over that of bare alumina. Over clean Pt/γ-Al2O3 surfaces some adsorbed propene desorbs molecularly [similar]250 K while the remainder decomposes liberating hydrogen. Coadsorbed oxygen or sulfate promote propene combustion, with adsorbed sulfoxy species the most efficient oxidant. The chemistry of these alumina-supported Pt clusters shows a general evolution from small polycrystalline clusters to larger clusters with properties akin to low-index, Pt single-crystal surfaces.

Stabilization of catalyst particles against sintering on oxide supports with high oxygen ion lability exemplified by Ir-catalyzed decomposition of N2O

Iridium nanoparticles deposited on a variety of surfaces exhibited thermal sintering characteristics that were very strongly correlated with the lability of lattice oxygen in the supporting oxide materials. Specifically, the higher the lability of oxygen ions in the support, the greater the resistance of the nanoparticles to sintering in an oxidative environment. Thus with γ-Al2O3 as the support, rapid and extensive sintering occurred. In striking contrast, when supported on gadolinia-ceria and alumina-ceria-zirconia composite, the Ir nanoparticles underwent negligible sintering. In keeping with this trend, the behavior found with yttria-stabilized zirconia was an intermediate between the two extremes. This resistance, or lack of resistance, to sintering is considered in terms of oxygen spillover from support to nanoparticles and discussed with respect to the alternative mechanisms of Ostwald ripening versus nanoparticle diffusion. Activity towards the decomposition of N2O, a reaction that displays pronounced sensitivity to catalyst particle size (large particles more active than small particles), was used to confirm that catalytic behavior was consistent with the independently measured sintering characteristics. It was found that the nanoparticle active phase was Ir oxide, which is metallic, possibly present as a capping layer. Moreover, observed turnover frequencies indicated that catalyst-support interactions were important in the cases of the sinter-resistant systems, an effect that may itself be linked to the phenomena that gave rise to materials with a strong resistance to nanoparticle sintering.

A hydrothermally stable transition alumina by condensation-enhanced self-assembly and pyrolysis crystallization:application in the steam reforming of methane

The preparation of a steam-based hydrothermally stable transition alumina is reported. The gel was derived from a synthetic sol-gel route where Al-tri-sec-butoxide is hydrolysed in the presence of a non-ionic surfactant (EO20PO70EO20), HCl as the catalyst and water (H2O/Al = 6); the condensation was enhanced by treating the hydrolysed gel with tetrabutylammonium hydroxide (TBAOH), after which it was dried at 60 °C by solvent evaporation. The so-obtained mesophase was crystallized under argon at 1200 °C (1 h) producing a transition alumina containing δ/α, and possibly θ, alumina phases. Due to its surface acidity, the pyrolysis conditions transform the block copolymer into a cross-linked char structure that embeds the alumina crystallites. Calcination at 650 °C generates a fully porous material by burning the char; a residual carbon of 0.2 wt.% was found, attributed to the formation of surface (oxy)carbides. As a result, this route produces a transition alumina formed by nanoparticles of about 30 nm in size on average, having surface areas in the range of 59-76 m2 g-1 with well-defined mesopores centered at 14 nm. The material withstands steam at 900 °C with a relative surface area rate loss lower than those reported for δ-aluminas, the state-of-the-art MSU-X γ-alumina and other pure γ-aluminas. The hydrothermal stability was confirmed under relevant CH4 steam reforming conditions after adding Ni; a much lower surface area decay and higher CH4 conversion compared to a state-of-the-art MSU-X based Ni catalyst were observed. Two effects are important in explaining the properties of such an alumina: the char protects the particles against sintering, however, the dominant effect is provided by the TBAOH treatment that makes the mesophase more resistant to coarsening and sintering. This journal is © the Partner Organisations 2014.

Making coke a more efficient catalyst in the oxidative dehydrogenation of ethylbenzene using wide-pore transitional aluminas

The thermal activation of a silica-stabilized γ-Alumina impacts positively on the oxidative dehydrogenation of ethylbenzene (EB) to styrene (ST). A systematic thermal study reveals that the transition from γ-alumina into transitional phases at 1050C leads to an optimal enhancement of both conversion and selectivity under pseudo-steady state conditions; where active and selective coke have been deposited. The effect is observed in the reaction temperature range of 450-475C at given operation conditions resulting in the highest ST yield, while at 425C this effect is lost due to incomplete O2 conversion. The conversion increase is ascribed to the ST selectivity improvement that makes more O2 available for the main ODH reaction. The fresh aluminas and catalytically active carbon deposits on the spent catalysts were characterized by gas adsorption (N 2 and Ar), acidity evaluation by NH3-TPD and pyridine adsorption monitored by FTIR, thermal and elemental analyses, solubility in CH2Cl2 and MALDI-TOF to correlate the properties of both phases with the ST selectivity enhancement. Such an increase in selectivity was interpreted by the lower reactivity of the carbon deposits that diminished the COx formation. The site requirements of the optimal catalyst to create the more selective coke is related to the higher density of Lewis sites per surface area, no mixed Si-Al Brønsted sites are formed while the acid strength of the formed Lewis sites is relatively weaker than those of the bare alumina. © 2013 Elsevier B.V. All rights reserved.

Oxidative dehydrogenation of ethylbenzene to styrene over alumina:effect of calcination

Commercially available γ-Al2O3 was calcined at temperatures between 500 and 1200 °C and tested for its performance in the oxidative ethylbenzene dehydrogenation (ODH) over a wide range of industrially-relevant conditions. The original γ-Al2O 3, as well as η- and α-Al2O3, were tested. A calcination temperature around 1000/1050 °C turned out to be optimal for the ODH performance. Upon calcination the number of acid sites (from 637 to 436 μmol g-1) and surface area (from 272 to 119 m 2 g-1) decrease, whereas the acid site density increases (from 1.4 to 2.4 sites per nm2). Less coke, being the active catalyst, is formed during ODH on the Al-1000 sample compared to γ-Al 2O3 (30.8 wt% vs. 21.6 wt%), but the coke surface coverage increases. Compared with γ-Al2O3, the EB conversion increased from 36% to 42% and the ST selectivity increased from 83% to 87%. For an optimal ST selectivity the catalyst should contain enough coke to attain full conversion of the limiting reactant oxygen. The reactivity of the coke is changed due to the higher density and strength of the Lewis acid sites that are formed by the high temperature calcination. The Al-1000 sample and all other investigated catalysts lost ODH activity with time on stream. The loss of selectivity towards more COX formation is directly correlated with the amount of coke. © The Royal Society of Chemistry 2013.