Role of reinforcement/matrix interfacial strength in fatigue crack propagation in particulate SiC reinforced aluminum alloy 8090

A study has been made of the influence of the reinforcement/matrix interfacial strength on fatigue crack propagation in a powder metallurgy aluminum alloy 8090-SiC particulate composite. The interfacial region has been altered by two separate routes, the first involving aging of the 8090 matrix, with the subsequent formation of precipitate free zones at the boundaries, and the second consisting of oxidizing the surface of the SiC particles before their incorporation into the composite. In the naturally aged condition, oxidation of the SiC leads to a reduction in fatigue crack growth resistance at higher values of stress intensity range ΔK. This is due to a proportion of the crack growth occurring through voids formed in association with many of the weak SiC interfaces which have retained a layer of thick surface oxide after processing. On overaging no difference in crack growth rate is discernible between the oxidized and unoxidized SiC composites. It is proposed that this is due to similar levels of interfacial weakening having occurred in both composites, indicating that this is an important factor in the reduction of the high ΔK crack growth resistance of the unoxidized SiC composite on aging.

Influence of macroscopic residual stress fields on fatigue crack growth measurement in SiC particulate reinforced 8090 aluminium alloy

The effect of residual stresses, induced by cold water quenching, on the morphology of fatigue crack fronts has been investigated in a powder metallurgy 8090 aluminium alloy, with and without reinforcement in the form of 20 wt-%SiC particles. Residual stress measurements reveal that the surface compressive stresses developed in these materials are significantly greater than in conventional metallurgy ingot 8090, because surface yielding occurs on quenching. The yield stresses of the powder route materials are greater than those of ingot produced 8090 and hence greater surface stresses can be maintained. In fatigue, severe crack front bowing is observed in the powder formed materials as a result of the reduction of the R ratio (minimum load/maximum load) by the compressive residual stresses at the sides of the specimen, causing premature crack closure and hence reducing the local driving force for fatigue crack growth ΔKeff. This distortion of the crack fronts introduces large errors into measurements of crack growth rate and threshold values of ΔK.

Fatigue crack propagation in nickel-base superalloys:effects of microstructure, load ratio, and temperature

The current state of knowledge and understanding of the long fatigue crack propagation behavior of nickel-base superalloys are reviewed, with particular emphasis on turbine disk materials. The data are presented in the form of crack growth rate versus stress intensity factor range curves, and the effects of such variables as microstructure, load ratio, and temperature in the near-threshold and Paris regimes of the curves, are discussed.

Microstructural and environmental effects on fatigue crack propagation in duplex stainless steels

Fatigue crack initiation and propagation in duplex stainless steels are strongly affected by microstructure in both inert and aggressive environments. Fatigue crack growth rates in wrought Zeron 100 duplex stainless steel in air were found to vary with orientation depending on the frequency of crack tip retardation at ferrite/austenite grain boundaries. Fatigue crack propagation rates in 3.5% NaCl solution and high purity water are increased by hydrogen assisted transgranular cyclic cleavage of the ferrite. The corrosion fatigue results are interpreted using a model for the cyclic cleavage mechanism.

Fatigue crack propagation mechanisms in a thermally aged duplex stainless steel

Zeron 100 duplex stainless steel is susceptible to embrittlement following ageing at temperatures between 350 °C and 450 °C. The embrittlement is associated with cleavage of the age-hardened ferrite phase, initiated by deformation twinning. This can result in order of magnitude increases in the fatigue crack propagation rate. The effects of ageing on the mechanisms of fatigue crack propagation in Zero 100 are investigated, and a quantitative model is developed, accounting for the effects of hardness, temperature, stress level and microstructure on the fatigue crack growth rate. © 1994.

Short fatigue crack path determinants in polycrystalline Ni-base superalloys

Fifty seven short fatigue cracks in the Ni-base superalloy AP1 have been examined, to ascertain how the paths taken by growing fatigue cracks are determined. The observations were made on the surface of a smooth specimen, and on the exposed fracture surfaces. Three dimensional reconstructions of the vulnerable microstructures in the vicinity of the cracks were produced. Initiation occurred in mode II, with the lines of intersection of the initiation sites with the specimen top surface orientated at approximately 45° to the tensile axis. These initiation sites developed in slip bands which crossed a large grain and at least one other grain via a grain boundary with a low angle of misorientation. 'River markings' on one of the initiation facets, indicated that the crack first opened from the top centre of the initiation grain. Subsequent to initiation, the growth paths of these cracks are related to the misorientations of the grains and the progress of the crack front.

Fatigue crack growth behaviour in molten-metal processed SiC particle-reinforced aluminium alloys

Fatigue crack initiation and subsequent short crack growth behaviour of 2014-5wt%SiC aluminium alloy composites has been examined in 4-point bend loading using smooth bar specimens. The growth rates of long fatigue cracks have also been measured at different stress ratios using pre-cracked specimens. The distributions of SiC particles and of coarse constituent particles in the matrix (which arise as a result of the molten-metal processing and relatively slow cooling rate) have been investigated. Preferential crack initiation sites were found to be SiC-matrix interfaces, SiC particles associated with constituent particles and the coarse constituent particles themselves. For microstructurally short cracks the dispersed SiC particles also act as temporary crack arresters. In the long crack growth tests, higher fatigue crack growth rates were obtained than for monolithic alloys. This effect is attributed to the contribution of void formation, due to the decohesion of SiC particles, to the fatigue crack growth process in the composite. Above crack depths of about 200 μm 'short' crack growth rates were in good agreement with the long crack data, showing a Pris exponent, m = 4 in both cases. For the long crack and short crack growth tests little effect of specimen orientation and grain size was observed on fatigue crack growth rates, but, specimen orientation affected the toughness. No effect of stress ratio in the range R = 0.2-0.5 was seen for long crack data in the Paris region.

Effects of dynamic strain ageing on fatigue crack propagation and threshold behaviour in a Ni-base superalloy

In the temperature range 200-400 degree C the Ni-base superalloy, N901, develops marked dynamic strain ageing effects in its tensile behavior. These include inverse strain rate sensitivity, especially in UTS values, strongly serrated stress-strain curves and a heavily sheared failure mode at the higher test-temperatures. As for steels these effects seem to be due to interactions between the dislocations and the interstitial carbon atoms present. The results of tensile and fatigue threshold tests carried out between 20 degree C and 420 degree C are reported and the fatigue behavior is discussed in terms of the effects of surface roughness induced closure, temperature and strain aging interactions.

Interfacial effects on fatigue and fracture in discontinuously reinforced metal matrix composites

Interfaces in conventional monolithic alloys exert an important influence on fatigue and fracture behavior. In discontinuously reinforced metal matrix composites (MMCs), the role of interface is even more dominant. The interfacial is higher in MMCs and the interfaces are generally of high energy and chemically unstable. This paper reviews the factors which can affect interfacial strength in discontinuously reinforced MMCs, and the ways in which interfacial strength can be controlled. The effects of interfacial strength on fatigue crack propagation and fracture behavior are then illustrated.

Crack closure and residual stress effects in fatigue of a particle-reinforced metal matrix composite

A study of the influence of macroscopic quenching stresses on long fatigue crack growth in an aluminium alloy-SiC composite has been made. Direct comparison between quenched plate, where high residual stresses are present, and quenched and stretched plate, where they have been eliminated, has highlighted their rôle in crack closure. Despite similar strength levels and identical crack growth mechanisms, the stretched composite displays faster crack growth rates over the complete range of ΔK, measured at R = 0.1, with threshold being displaced to a lower nominal ΔK value. Closure levels are dependent upon crack length, but are greater in the unstretched composite, due to the effect of surface compressive stresses acting to close the crack tip. These result in lower values of ΔKeff in the unstretched material, explaining the slower crack growth rates. Effective ΔKth values are measured at 1.7 MPa√m, confirmed by constant Kmax testing. In the absence of residual stress, closure levels of approximately 2.5 MPa√m are measured and this is attributed to a roughness mechanism.

Temperature effects on the mechanism of time independent hydrogen assisted fatigue crack propagation in steels

The effects of temperature on hydrogen assisted fatigue crack propagation are investigated in three steels in the low-to-medium strength range; a low alloy structural steel, a super duplex stainless steel, and a super ferritic stainless steel. Significant enhancement of crack growth rates is observed in hydrogen gas at atmospheric pressure in all three materials. Failure occurs via a mechanism of time independent, transgranular, cyclic cleavage over a frequency range of 0.1-5 Hz. Increasing the temperature in hydrogen up to 80°C markedly reduces the degree of embrittlement in the structural and super ferritic steels. No such effect is observed in the duplex stainless steel until the temperature exceeds 120°C. The temperature response may be understood by considering the interaction between absorbed hydrogen and micro-structural traps, which are generated in the zone of intense plastic deformation ahead of the fatigue crack tip. © 1992.

The influence of ageing on fatigue crack growth in SiC-particulate reinforced 8090

A study of the influence of SiC-particulate reinforcement on ageing and subsequent fatigue crack growth resistance in a powder metallurgy 8090 aluminium alloy-SiC composite has been made. Macroscopic hardness measurements revealed that ageing at 170°C in the composite is accelerated with respect to the unreinforced alloy, though TEM studies indicate that this is not due to the enhanced precipitation of S′. Fatigue crack growth rates in the naturally aged condition of the composite and unreinforced matrix are similar at low to medium values of ΔK, but diverge above ≈ 8 MPa√m owing to the lower fracture toughness of the composite. As a result of the presence of the reinforcement, planar slip in the composite is suppressed and facetted crack growth is not observed. Ageing at or above 170°C has a deleterious effect on fatigue crack growth. Increased ageing time decreases the roughness of the fracture path at higher growth rates. These effect are though to be due to microstructural changes occurring at or near to the SiC/matrix interfaces, providing sites for static mode failure mechanisms to operate. This suggestion is supported by the observation that as ΔK increases, crack growth rates become Kmax dependent, implying the crack growth rate is strongly influenced by static modes.

Fatigue in SiC-particulate-reinforced aluminium alloy composites

The fatigue behaviour in SiC-particulate-reinforced aluminium alloy composites has been briefly reviewed. The improved fatigue life reported in stress-controlled test results from the higher stiffness of the composites; therefore it is generally inferior to monolithic alloys at a constant strain level. The role of SiC particulate reinforcement has been examined for fatigue crack initiation, short-crack growth and long-crack growth. Crack initiation is observed to occur at matrix-SiC interface in cast composites and either at or near the matrix-SiC interface or at cracked SiC particles in powder metallurgy processed composites depending on particle size and morphology. The da/dN vs ΔK relationship in the composites is characterized by crack growth rates existing within a narrow range of ΔK and this is because of the lower fracture toughness and relatively high threshold values in composites compared with those in monolithic alloys. An enhanced Paris region slope attributed to the monotonic fracture contribution are reported and the extent of this contribution is found to depend on particle size. The effects of the aging condition on crack growth rates and particle size dependence of threshold values are also treated in this paper. © 1991.

The influence of a coal gasifier atmosphere on fatigue crack growth rates in BS 4360 steel

Fatigue crack growth tests have been carried out in a number of gaseous environments in order to assess their effects on the crack propagation resistance of BS 4360 grade 50EE, a weldable structural steel. Crack growth rates at 25 °C are up to 20 times higher in hydrogen than in air, but there is no effect when hydrogen is present as a 30% constituent of a simplified product gas (SPG). Indeed, crack growth rates in such a mixture are slightly lower than those measured in air, being comparable with those observed in an inert environment. The other gases present in the SPG are CO, CO2 and CH4, and it is probable that the carbon monoxide is responsible for nullifying the embrittling effects of hydrogen, by preferentially adsorbing on to the surface of the steel and thus blocking hydrogen entry. Experimental observations suggest that oxygen has the same effect when small quantities are allowed to diffuse into a non-flowing hydrogen environment around a propagating crack. The results are encouraging in terms of the suitability of conventional structural steels such as BS 4360 for gas plant applications. The gas mixtures present in such an environment would not have the severe detrimental effects on fatigue crack growth resistance which result from the presence of 'pure' hydrogen. © 1993.