Catalytic supercritical water gasification of plastics with supported RuO2:a potential solution to hydrocarbons-water pollution problem

Here we report on a potential catalytic process for efficient clean-up of plastic pollution in waters, such as the Great Pacific Garbage Patch (CPGP). Detailed catalytic mechanisms of RuO2 during supercritical water gasification of common polyolefin plastics including low-density polyethylene (LDPE), high-density polyethylene (HDPE), polypropylene (PP) and polystyrene (PP), have been investigated in a batch reactor at 450 °C, 60 min. All four plastics gave very high carbon gasification efficiencies (CGE) and hydrogen gasification efficiencies (HGE). Methane was the highest gas component, with a yield of up to 37 mol kg−1LDPE using the 20 wt% RuO2 catalyst. Evaluation of the gas yields, CGE and HGE revealed that the conversion of PS involved thermal degradation, steam reforming and methanation; whereas hydrogenolysis was a possible additional mechanism during the conversion of aliphatic plastics. The process has the benefits of producing a clean-pressurized methane-rich fuel gas as well as cleaning up hydrocarbons-polluted waters.

Supercritical water gasification of RDF and its components over RuO2/γ-Al2O3 catalyst:new insights into RuO2 catalytic reaction mechanisms

Five samples including a composite refuse derived fuel (RDF) and four combustible components of municipal solid wastes (MSW) have been reacted under supercritical water conditions in a batch reactor. The reactions have been carried out at 450 °C for 60 min reaction time, with or without 20 wt% RuO2/gamma-alumina catalyst. The reactivities of the samples depended on their compositions; with the plastic-rich samples, RDF and mixed waste plastics (MWP), giving similar product yields and compositions, while the biogenic samples including mixed waste wood (MWW) and textile waste (TXT) also gave similar reaction products. The use of the heterogeneous ruthenium-based catalyst gave carbon gasification efficiencies (CGE) of up to 99 wt%, which was up by at least 83% compared to the non-catalytic tests. In the presence of RuO2 catalyst, methane, hydrogen and carbon dioxide became the dominant gas products for all five samples. The higher heating values (HHV) of the gas products increased at least two-fold in the presence of the catalyst compared to non-catalytic tests. Results show that the ruthenium-based catalyst was active in feedstock steam reforming, methanation and possible direct hydrogenolysis of C-C bonds. This work provides new insights into the catalytic mechanisms of RuO2 during SCWG of carbonaceous materials, along with the possibility of producing high yields of methane from MSW fractions.

Supercritical carbonation of lime based sustainable structural ceramics

Abstract Structural ceramics were manufactured from industrial byproducts and lime by a compression moulding/vacuum dewatering technique. Treatment of these ceramics with supercritical carbon dioxide was found to both significantly increase their flexural strength and activate cementation in the industrial byproducts at least as efficiently as heat curing. Flexural strengths of up to 10 MPa were achieved. Strength improvements were associated with decreased porosity and conversion of calcium hydroxide to calcium carbonate. Life cycle assessment of proposed products made from such materials indicated that the total reduction in embodied carbon dioxide achieved, as a result of combining use of byproducts with recombination of carbon dioxide, was up to 70%. © 2010 Institute of Materials, Minerals and Mining.