Oxidative dehydrogenation of ethylbenzene to styrene over alumina:effect of calcination

Commercially available γ-Al2O3 was calcined at temperatures between 500 and 1200 °C and tested for its performance in the oxidative ethylbenzene dehydrogenation (ODH) over a wide range of industrially-relevant conditions. The original γ-Al2O 3, as well as η- and α-Al2O3, were tested. A calcination temperature around 1000/1050 °C turned out to be optimal for the ODH performance. Upon calcination the number of acid sites (from 637 to 436 μmol g-1) and surface area (from 272 to 119 m 2 g-1) decrease, whereas the acid site density increases (from 1.4 to 2.4 sites per nm2). Less coke, being the active catalyst, is formed during ODH on the Al-1000 sample compared to γ-Al 2O3 (30.8 wt% vs. 21.6 wt%), but the coke surface coverage increases. Compared with γ-Al2O3, the EB conversion increased from 36% to 42% and the ST selectivity increased from 83% to 87%. For an optimal ST selectivity the catalyst should contain enough coke to attain full conversion of the limiting reactant oxygen. The reactivity of the coke is changed due to the higher density and strength of the Lewis acid sites that are formed by the high temperature calcination. The Al-1000 sample and all other investigated catalysts lost ODH activity with time on stream. The loss of selectivity towards more COX formation is directly correlated with the amount of coke. © The Royal Society of Chemistry 2013.

Stabilization of self-assembled alumina mesophases

An efficient route to stabilize alumina mesophases derived from evaporation-induced self-assembly is reported after investigating various aspects in-depth: influence of the solvent (EtOH, s-BuOH, and t-BuOH) on the textural and structural properties of the mesophases based on aluminum tri-sec-butoxide (ATSB), synthesis reproducibility, role of nonvolatile acids, and the crystallization and thermal stability of the crystalline counterparts. Mesophase specific surface area and pore uniformity depend notably on the solvent; s-BuOH yields the highest surface area and pore uniformity. The optimal mesophase synthesis is reproducible with standard deviations in the textural parameters below 5%. The most pore-uniform mesophases from the three solvents were thermally activated at 1023 K to crystallize them into γ-alumina. The s-BuOH mesophase is remarkably thermally stable, retaining the mesoscopic wormhole order with 300 m2/g (0.45 cm3/g) and an increased acidic site density. These features are not obtained with EtOH or t-BuOH, where agglomerated γ-Al2O3 crystallites are formed with lower surface areas and broader pore size distributions. This was rationalized by the increase of the hydrolysis rate using EtOH and t-BuOH. t-BuOH dehydrates under the synthesis conditions or reacts with HCl, situations that increase the water concentration and rate of hydrolysis. It was found that EtOH exchanges rapidly, producing a highly reactive Al-ethoxide, thus enhancing the hydrolysis rate as well. Particle heterogeneity with random packing of fibrous and wormhole morphologies, attributed to the high hydrolysis rate, was observed for mesophases derived from both solvents. Such a low particle coordination favors coarsening with enlargement of the pore size distribution upon thermal treatment, explaining the lower thermal stability. Controlled hydrolysis and formation of low-polymerized Al species in s-BuOH are possibly responsible for the adequate assembly onto the surfactant. This was verified by the formation of a regular distribution of relatively size-uniform nanoparticles in the mesophase; high particle coordination prevents coarsening, favors densification, and maintains a relatively uniform pore size distribution upon thermal treatment. The acid removal in the evaporation is another key factor to promote network condensation in this route. © 2013 American Chemical Society.