Fracture behaviour of an aluminide coating on a single crystal nickel base superalloy

Measurement of the coating fracture strain of an aluminide coating on a single crystal nickel base superalloy has been performed both in three-point bending and using variable wall thickness testpieces. As-aged specimens, 28 to 33 μm in thickness, were tested at room temperature, 600, 700 and 750 °C; specimens pre-exposed for 140 h at 850 and 1100 °C in air and vacuum were tested at room temperature. Fracture strains varied from 0.52 to 0.70% for as-aged specimens tested at temperatures up to 700 °C and specimens exposed at 850 °C and tested at room temperature. The crack path for these conditions was intergranular or transgranular in the main coating, along carbide-matrix interfaces in the coating transition zone, and at an angle of 30-45° to the original crack path in the substrate. The as-aged coating tested at 750 °C was ductile; a ductile-brittle transition occurs between 700 and 750 °C for the strain rate used (1 × 10-5 s-1). Following 1100 °C pre-exposure, specimens were ductile at room temperature with fractures strains of several percent. In this condition the crack morphology changed to one of subsurface nucleation in β grains and at β-γ′ interfaces. © 1993.

Precipitation of chromium containing phases in aluminide coated nickel-base superalloy single crystals

The precipitation of chromium-containing phases, in both the B2 type β-phase coating matrix (nominally NiAl) and the substrate of high-activity-pack-aluminized single crystals of a nickel-base superalloy, is considered in this paper. An ‘edge-on’ transmission electron microscopy (TEM) technique is employed to examine the precipitation of M23X6, σ, α-Cr and other phases after coating and diffusion treatment and subsequent post-coating treatment at 850 and 950 °C. Initial precipitation is dominated by the formation of M23X6 in both the coating and substrate, however, in the case of single-crystal substrates the formation of this carbon-rich phase is not sustained. M23X6 precipitation is superceded by the formation of coherent precipitates of the α-Cr phase which effectively retains the basis but removes the superlattice of the β-matrix. Extensive precipitation of α-Cr has the effect of changing the balance of chromium to molybdenum in solution in the β-phase and further precipitation is dominated by Σ-phase intermetallics and other Cr-Mo-containing phases.

Temperature effects on fatigue thresholds and structure sensitive crack growth in a nickel-base superalloy

Fatigue thresholds and slow crack growth rates have been measured in a powder formed nickel-base superalloy from room temperature to 600°C. Two grain sizes were investigated: 5-12 μm and 50 μm. It is shown that the threshold increases with grain size, and the difference is most pronounced at room temperature. Although crack growth rates increase with temperature in both microstructures, the threshold is only temperature dependent in the material with the larger grain size. It is also only in the latter that the room temperature threshold falls when the load ratio is increased from 0.1 to 0.5. At 600°C the higher load ratio causes a 20% reduction in the threshold irrespective of grain size. The results are discussed in terms of surface roughness and oxide-induced crack closure, the former being critically related to the type of crystallographic crack growth, which is in turn shown to be both temperature and stress intensity dependent. © 1983.

Microstructural development in aluminide diffusion coatings on nickel-base superalloy single crystals

An investigation has been made of the microstructural stability of aluminide diffusion coatings during post-coating thermal exposure. This study has employed edge-on transmission electron microscopy to examine high-activity pack aluminised single crystals of a gamma prime strengthened nickel-base superalloy. The influence of exposure temperature, duration and atmosphere as well as the initial coating thickness has been assessed. Two major processes have been found to contribute to microstructural changes in the coating. These are, firstly, the transformation of the coating matrix (β-phase, nominally NiAl) to other Ni-Al based phases, especially γ' (nominally Ni3(Al, Ti)) and, secondly, the precipitation of chromium containing phases. The work has enabled the roles of three processes contributing to γ formation, namely: oxidation of the coating surface, interdiffusion with the substrate and ageing of the coating, to be understood. In addition, the factors leading to the formation of a sequence of chromium-containing phases have been identified.

Modelling short crack growth behaviour in nickel-base superalloys

This paper provides a description of the features and mechanisms of facetted short crack growth in Ni-base superalloys, and briefly reviews existing short crack growth models in terms of their application to Ni-base alloys. The concept of “soft barriers” is introduced to produce a new two-phase model for local microstructural effects on short crack growth in Waspaloy. This is derived from detailed observations of crack growth through individual grains. The model differs from all previous approaches in highlighting the importance of crack path perturbations within grains. Potential applications of the model in alloy development are discussed.

Effects of microstructure on long and short crack growth in nickel base superalloys

The use of engineering materials in critical applications necessitates the accurate prediction of component lifetime for inspection and renewal purposes. In fatigue limited situations, it is necessary to be able to predict the growth rates of cracks from initiation at a defect through to final fracture. To this end, fatigue crack growth data are presented for different microstructures of typical nickel base superalloys used in gas turbine engines. Crack growth behaviour throughout the life history of the crack, i.e. from the short crack through to the long crack propagation regime, is described for each microstructural condition and discussed in terms of current theories of fatigue crack propagation.