An efficient route to highly organized, tunable macroporous-mesoporous alumina

(Figure Presented) Organized macroporous-mesoporous alumina can be obtained via a dual-templating approach. Monodispersed polystyrene beads promote macropore formation, while a P123 surfactant templating agent drives the formation of ordered hexagonal mesopores throughout the alumina framework. These well-defined pore networks coexist over a wide range of temperatures and macropore sizes. © 2009 American Chemical Society.

Synthesis and characterization of dual-functionalized core-shell fluorescent microspheres for bioconjugation and cellular delivery

The efficient transport of micron-sized beads into cells, via a non-endocytosis mediated mechanism, has only recently been described. As such there is considerable scope for optimization and exploitation of this procedure to enable imaging and sensing applications to be realized. Herein, we report the design, synthesis and characterization of fluorescent microsphere-based cellular delivery agents that can also carry biological cargoes. These core-shell polymer microspheres possess two distinct chemical environments; the core is hydrophobic and can be labeled with fluorescent dye, to permit visual tracking of the microsphere during and after cellular delivery, whilst the outer shell renders the external surfaces of the microspheres hydrophilic, thus facilitating both bioconjugation and cellular compatibility. Cross-linked core particles were prepared in a dispersion polymerization reaction employing styrene, divinylbenzene and a thiol-functionalized co-monomer. These core particles were then shelled in a seeded emulsion polymerization reaction, employing styrene, divinylbenzene and methacrylic acid, to generate orthogonally functionalized core-shell microspheres which were internally labeled via the core thiol moieties through reaction with a thiol reactive dye (DY630-maleimide). Following internal labeling, bioconjugation of green fluorescent protein (GFP) to their carboxyl-functionalized surfaces was successfully accomplished using standard coupling protocols. The resultant dual-labeled microspheres were visualized by both of the fully resolvable fluorescence emissions of their cores (DY630) and shells (GFP). In vitro cellular uptake of these microspheres by HeLa cells was demonstrated conventionally by fluorescence-based flow cytometry, whilst MTT assays demonstrated that 92% of HeLa cells remained viable after uptake. Due to their size and surface functionalities, these far-red-labeled microspheres are ideal candidates for in vitro, cellular delivery of proteins, as described in the accompanying paper.

Uncovering changes in the redox protein interactome of PTEN

Phosphatase and tensin homolog (PTEN) is a redox-sensitive, dual-specificity protein phosphatase involved in regulating a number of cellular processes including metabolism, apoptosis, cell proliferation and survival. It acts as a tumor suppressor by negatively regulating the PI3K/Akt pathway. While direct evidence of a redox regulation of PTEN downstream signaling has been reported, the effect of cellular oxidative stress or direct PTEN oxidation on the PTEN interactome is still poorly defined. To investigate this, PTEN-GST fusion protein was prepared in its reduced form and an H2O2-oxidized form that was reversible by DTT treatment, and these were immobilized on a glutathione-sepharose-based support. The immobilized protein was incubated with cell lysate to capture interacting proteins. Captured proteins were eluted from the beads, analyzed by LC-MSMS and comparatively quantified using label-free methods. After subtraction of interactors that were also present in the resin and GST controls, 97 individual protein interactors were identified, including several that are novel. Fourteen interactors that varied significantly with the redox status of PTEN were identified, including thioredoxin and peroxiredoxin-1. Except for one interactor, their binding was higher for oxidized PTEN. Using western blotting, altered binding to PTEN was confirmed for 3 selected interactors (Prdx1, Trx, and Anxa2) and DDB1 was validated as a novel interactor with unaltered binding. Our results suggest that the redox status of PTEN causes a functional variation in the PTEN interactome which is important for the cellular function of PTEN. The resin capture method developed had distinct advantages in that the redox status of PTEN could be directly controlled and measured.

Hierarchical macroporous-mesoporous SBA-15 sulfonic acid catalysts for biodiesel synthesis

Hierarchical macroporous-mesoporous SBA-15 silicas have been synthesised via dual-templating routes employing liquid crystalline surfactants and polystyrene beads. These offer high surface areas and well-defined, interconnecting macro- and mesopore networks with respective narrow size distributions around 300 nm and 3-5 nm for polystyrene:tetraethoxysilane ratios ≥2:1. Subsequent functionalisation with propylsulfonic acid yields the first organized, macro-mesoporous solid acid catalyst. The enhanced mass transport properties of these new bi-modal solid acid architectures confer significant rate enhancements in the transesterification of bulky glyceryl trioctanoate, and esterification of long chain palmitic acid, over pure mesoporous analogues. This paves the way to the wider application of hierarchical catalysts in biofuel synthesis and biomass conversion. © 2010 The Royal Society of Chemistry.

A highly emissive inorganic hexamolybdenum cluster complex as a handy precursor for the preparation of new luminescent materials

The synthesis and characterisation of a new, highly luminescent inorganic cluster complex, (Bu4N)2[Mo6I 8(NO3)6], are described. The complex possesses labile nitrato ligands and is therefore a useful precursor for the design of new luminescent materials. To exemplify this, functionalised polystyrene beads have been utilised as "polymeric ligands" to immobilise the molybdenum cluster complex. This journal is © the Partner Organisations 2014.

Self-assembly-driven electrospinning:the transition from fibers to intact beaded morphologies

Polymer beads have attracted considerable interest for use in catalysis, drug delivery, and photo­nics due to their particular shape and surface morphology. Electrospinning, typically used for producing nanofibers, can also be used to fabricate polymer beads if the solution has a sufficiently low concentration. In this work, a novel approach for producing more uniform, intact beads is presented by electrospinning self-assembled block copolymer (BCP) solutions. This approach allows a relatively high polymer concentration to be used, yet with a low degree of entanglement between polymer chains due to microphase separation of the BCP in a selective solvent system. Herein, to demonstrate the technology, a well-studied polystyrene-poly(ethylene butylene)–polystyrene triblock copolymer is dissolved in a co-solvent system. The effect of solvent composition on the characteristics of the fibers and beads is intensively studied, and the mechanism of this fiber-to-bead is found to be dependent on microphase separation of the BCP.

Synthesis and characterisation of polyacrylonitrile and its derived carbon materials

Carbon is a versatile material which is composed of different allotropes, and also come in with different structures. Carbon nanofibres (CNFs) is one dimensional carbon nanomaterials, which have exhibited superior mechanical properties, great specific area, good electrical conductivity, good biocompatibility, and ease of modification. In addition to the lower cost associated to compare with carbon nanotubes (CNTs), CNFs have been attracted in numerous applications, such as reinforcement materials, filtrations, Li-ion battery, supercapacitor as well as tissue engineering, just to list a few. Therefore, it is a great deal to understand the relationship between the fabrication conditions and the characteristics of the resulted CNFs. In this project, electrospun PAN NFs were used as precursor material to fabricate carbon nanofibres. In order to produce CNFs with good morphology, the processing parameters of PAN nanofibres by electrospinning was optimized toward to the morphology at solution concentration of 12 wt%. The optimized processing parameters at given concentration were 16 kV, 14 cm and 1.5 mL/h, which led to the formation of PAN NFs with average fibre diameter of approximately 260 nm. Along with the effect of processing parameter study, the effect of concentration on the morphology was also carried out at optimized processing parameters. It was found that by increasing concentration of PAN solution from 2 to 16%, the resulted PAN transformed from beads only, to beaded fibres and finally to smooth fibres. With further increasing concentration the morphology of smooth fibres remain with increase in the fibre diameter. Electrospun PAN NFs with average fibre of 306 nm was selected to be converted into CNFs by using standard heating procedures, stabilisation in air at 280 °C and carbonization in N2. The effect of carbonization temperature ranging from 500 to 1000 °C was investigated, by using SEM, FTIR, Raman, and Impedance spectroscopy. With increasing carbonization temperature from 500 to 1000 °C, the diameter of NFs was decreased from 260 to 187, associated with loss of almost all functional groups of NFs. It was indicated by Raman results, that the graphitic crystallite size was increased from 2.62 to 5.24 nm, and the activation energy obtained for this growth was 7570 J/mol. Furthermore, impedance results (i.e. Cole-Cole plot) revealed that the electrical characteristic of CNFs transitioned from being insulating to electrically conducting in nature, suggested by the different electrical circuits extracted from Cole-Cole plots with carbonization temperature from 500 to 800 °C. The carbonization on PAN NFs with diameter of ~431nm was carried out by using novel route, microwave plasma enhance chemical vapour deposition (MPECVD) process. To compare with carbonized PAN NFs by using conventional route, MPECVD was not only able to facilitate carbonization process, but more interestingly can form carbon nanowalls (CNWs) grown on the surfaces of carbonized PAN NFs. Suggested by the unique morphology, the potential applications for the resulted carbon fibrous hybrid materials are supercapacitor electrode material, filtrations, and etc., The method developed in this project required one step less, compared with other literature. Therefore, using MPECVD on stabilised PAN NFs is proposed as economical, and straightforward approach towards mass production of carbon fibrous hybrid materials containing CNWs.