Surface quality of profile extrusion dies manufactured by Selective Laser Melting

The design of plastics profile extrusion dies becomes increasingly more complex so that conventional manufacture processes reach their limit in the die manufacture. A feasible manufacture of arbitrarily designed dies is only possible by additive manufacturing. An especially promising process is hereby the Selective Laser Melting with which metal parts with series identical mechanical properties can be produced without the need for part specific tooling or downstream sintering processes. Disadvantegeous is, however, the relatively rough surface of additively manufactured parts. Against this background, the manufacturing of an profile extrusion die by Selective Laser Melting and the plastics profile surface quality, that can be achieved with such dies, is investigated. For this purpose, profiles are extruded both with an additively manufactured die and a conventionally milled sample of the same die geometry. In case of the additively manufactured die a concept for the surface finishing of the flow channel is required, which can be applied to arbitrarily shaped geometries. Therefore, two different reworking processes are applied only to the die land of the flow channel. The comparison of the surface roughnesses shows that the additively manufactured die with a polished die land delivers the same surface quality as the conventional die.

Prediction of PA12 melt viscosity in Laser Sintering by a Time and Temperature dependent rheological model

Ein auf Basis von Prozessdaten kalibriertes Viskositätsmodell wird vorgeschlagen und zur Vorhersage der Viskosität einer Polyamid 12 (PA12) Kunststoffschmelze als Funktion von Zeit, Temperatur und Schergeschwindigkeit angewandt. Im ersten Schritt wurde das Viskositätsmodell aus experimentellen Daten abgeleitet. Es beruht hauptsächlich auf dem drei-parametrigen Ansatz von Carreau, wobei zwei zusätzliche Verschiebungsfaktoren eingesetzt werden. Die Temperaturabhängigkeit der Viskosität wird mithilfe des Verschiebungsfaktors aT von Arrhenius berücksichtigt. Ein weiterer Verschiebungsfaktor aSC (Structural Change) wird eingeführt, der die Strukturänderung von PA12 als Folge der Prozessbedingungen beim Lasersintern beschreibt. Beobachtet wurde die Strukturänderung in Form einer signifikanten Viskositätserhöhung. Es wurde geschlussfolgert, dass diese Viskositätserhöhung auf einen Molmassenaufbau zurückzuführen ist und als Nachkondensation verstanden werden kann. Abhängig von den Zeit- und Temperaturbedingungen wurde festgestellt, dass die Viskosität als Folge des Molmassenaufbaus exponentiell gegen eine irreversible Grenze strebt. Die Geschwindigkeit dieser Nachkondensation ist zeit- und temperaturabhängig. Es wird angenommen, dass die Pulverbetttemperatur einen Molmassenaufbau verursacht und es damit zur Kettenverlängerung kommt. Dieser fortschreitende Prozess der zunehmenden Kettenlängen setzt molekulare Beweglichkeit herab und unterbindet die weitere Nachkondensation. Der Verschiebungsfaktor aSC drückt diese physikalisch-chemische Modellvorstellung aus und beinhaltet zwei zusätzliche Parameter. Der Parameter aSC,UL entspricht der oberen Viskositätsgrenze, wohingegen k0 die Strukturänderungsrate angibt. Es wurde weiterhin festgestellt, dass es folglich nützlich ist zwischen einer Fließaktivierungsenergie und einer Strukturänderungsaktivierungsenergie für die Berechnung von aT und aSC zu unterscheiden. Die Optimierung der Modellparameter erfolgte mithilfe eines genetischen Algorithmus. Zwischen berechneten und gemessenen Viskositäten wurde eine gute Übereinstimmung gefunden, so dass das Viskositätsmodell in der Lage ist die Viskosität einer PA12 Kunststoffschmelze als Folge eines kombinierten Lasersinter Zeit- und Temperatureinflusses vorherzusagen. Das Modell wurde im zweiten Schritt angewandt, um die Viskosität während des Lasersinter-Prozesses in Abhängigkeit von der Energiedichte zu berechnen. Hierzu wurden Prozessdaten, wie Schmelzetemperatur und Belichtungszeit benutzt, die mithilfe einer High-Speed Thermografiekamera on-line gemessen wurden. Abschließend wurde der Einfluss der Strukturänderung auf das Viskositätsniveau im Prozess aufgezeigt.

Selective Laser Melting of the Eutectic Silver-Copper Alloy Ag 28 wt % Cu

The aim of this work was to perform a detailed investigation of the use of Selective Laser Melting (SLM) technology to process eutectic silver-copper alloy Ag 28 wt. % Cu (also called AgCu28). The processing occurred with a Realizer SLM 50 desktop machine. The powder analysis (SEM-topography, EDX, particle distribution) was reported as well as the absorption rates for the near-infrared (NIR) spectrum. Microscope imaging showed the surface topography of the manufactured parts. Furthermore, microsections were conducted for the analysis of porosity. The Design of Experiments approach used the response surface method in order to model the statistical relationship between laser power, spot distance and pulse time.

Rapid Manufacturing - auch mit SLM

Rapid Manufacturing (RM) wurde als Schlagwort in der letzten Zeit insbesondere aus dem Bereich des Selective Laser Sintering (SLS) bekannt. In dieser inzwischen über 15-jährigen Technologieentwicklung wurden in den vergangenen Jahren bedeutende Fortschritte erzielt, die die Bauteileigenschaften nahe an die Anforderungen für End-Teile heran brachten. So ist das RM denn auch weniger aus der Sicht grösserer Losgrösse zu verstehen. Viel mehr bedeutet Rapid Manufacturing, dass die Bauteile nach einer generativen Fertigung direkt im Endprodukt resp. der Endanwendung zum Einsatz kommt. Das Selective Laser Melting, mit welchem aus metallischen Pulvermaterialien direkt Metallteile in Standardmaterialien hergestellt werden können, ist aufgrund der guten Materialeigenschaften für RM prädestiniert. In den ersten Anwendungsfeldern des SLM–Verfahrens standen die Herstellung von Werkzeugeinsätzen mit konturnaher Kühlung (Conformal Cooling) im Vordergrund, wobei diese Werkzeuge unter dem Begriff RM verstanden werden müssen, da die Werkzeuge direkt für die Endanwendung - den Spritzgussprozess - verwendet werden. Aktuelle Trends gehen jedoch in Richtung der Fertigung von Funktionsteilen z.B. für den Maschinenbau. Obwohl sich in der Fertigung komplexer Funktionsteile noch Probleme, z.B. mit in Bezug auf die generative Baurichtung überhängender Bauteilstrukturen ergeben, zeigen sich trotzdem erhebliche Vorteile eines RM mittels SLM. Neben klaren Vorteilen durch das mögliche Customizing von Bauteilen können bei kleineren Bauteilgrössen auch erhebliche Kostenvorteile erzielt werden. Allerdings zeigen die Grenzen der aktuellen Möglichkeiten, in welchen Bereichen das SLM-Verfahren weiterer Entwicklung bedarf. Themen wie Produktivität, die Problematik der nach wie vor notwendigen Supportstrukturen wie auch Qualitätssicherung müssen in den nächsten Jahren angegangen werden, wenn dieses Verfahren den Schritt hin zu einem etablierten Produktionsverfahren und damit zu breiterer Akzeptanz und Anwendung finden soll

Selektives Lasersintern von teilkristallinen Thermoplasten

Da eine flexible Fertigung im Bereich von Losgrößen zwischen 1-1000 Stück in vielen Wirtschaftszweigen vermehrt an Bedeutung gewinnt, steigt das Interesse an Verfahren wie dem Selektiven Lasersintern. Dennoch sollen die Eigenschaften von in Serie eingesetzten Werkstoffen erreicht werden. Aufgrund der bestehenden werkstofflichen Restriktionen auf Polyamid 12 wird aktuell an der Verarbeitung anderer teilkristalliner Thermoplaste geforscht. In diesem Beitrag werden die sich in der Markteinführung befindlichen Werkstoffe vorgestellt und basierend auf der Verarbeitung weiterer Thermoplaste die bestehende Modellvorstellung zum Lasersintern erweitert.

Trends and Expertise Exchange within Rapid Manufacturing in Europe

Rapid Manufacturing (RM) umfasst den Begriff der direkten und wirtschaftlichen Bauteilherstellung des Serienprodukts aus 3D-Daten. Die Hauptvorteile sind u.a. das Wegfallen von Werkzeugen und eine Designfreiheit in der Produktentwicklung, die noch vor wenigen Jahren undenkbar war. Wenngleich heute eine Vielzahl von Werkstoffen im Kunststoff- und Metallbereich einsetzbar sind, konzentriert sich die Verbreitung des RM allerdings auf besondere Technologie- und Wirtschaftszweige, aufgrund mangelnder Erfahrungswerte, teilweise abweichender Werkstoffeigenschaften, fehlender Standards und ungeeigneter Testmethoden. In der Praxis sind Ingenieure und Techniker stark darauf bedacht, auf etablierte Abläufe und Standards zurückzugreifen. Es ist daher schwer einen geeigneten RM-Prozess aufzubauen, wo wichtige Eingangsgrößen meist unbekannt sind. In diesem Bericht wird beschrieben, welche Informationskanäle es innerhalb Europas zum Thema RM gibt und welche Hochschulen und Forschungszentren Aktivitäten aufweisen. Darüber hinaus werden Anwendungsfelder des RM aufgeführt, die über die bekannten Anwendungsfelder hinaus gehen. Dazu gehören Anwendungen im Bereich der Elektrotechnik, Raumfahrtinstrumentation und der Mode. Obwohl nicht alle Anwendungen des RM in diesem Bericht aufgeführt werden, sind einige Schlüsselinformationen im Bereich innovativer Anwendungen von RM enthalten.

Properties comparison of Injected and SLS material

Most of the plastic injection companies are focused in the production of some products with a high exigency standard levels. That is why, to compete and gain some market share in front of the concurrency of companies from other countries, they need to be able to introduce new rapid prototyping techniques and product development.

Selektives Lasersintern von teilkristallinen Thermoplasten

Da eine flexible Fertigung im Bereich von Losgrößen zwischen 1-1000 Stück in vielen Wirtschaftszweigen vermehrt an Bedeutung gewinnt, steigt das Interesse an Verfahren wie dem Selektiven Lasersintern. Dennoch sollen die Eigenschaften von in Serie eingesetzten Werkstoffen erreicht werden. Aufgrund der bestehenden werkstofflichen Restriktionen auf Polyamid 12 wird aktuell an der Verarbeitung anderer teilkristalliner Thermoplaste geforscht. In diesem Beitrag werden die sich in der Markteinführung befindlichen Werkstoffe vorgestellt und basierend auf der Verarbeitung weiterer Thermoplaste die bestehende Modellvorstellung zum Lasersintern erweitert.

Untersuchung der Materialalterung bei pulverbasierten Schichtbauverfahren

Additive, pulverbasierte Schichtbauverfahren, wie das Selektive Masken- oder La-sersintern, ermöglichen die Fertigung von komplexen Bauteilen ohne Werkzeug und Form. Aufgrund der hohen, verarbeitungsbedingten Bauraumtemperaturen kommt es während der Verarbeitung zu physikalischem und thermisch-oxidativem Abbau der eingesetzten Kunststoffpulver. Das im Bauraum nicht aufgeschmolzene Material, der so genannte Partcake, kann nach dem Bauprozess vom fertigen Bauteil entfernt und für weitere Bauprozesse verwendet werden. Zur Realisierung reproduzierbarer Bau-teileigenschaften ist jedoch eine Aufbereitung („Refreshen“) des Partcake-Pulvers notwendig. Im Rahmen des Beitrags werden Erkenntnisse zum Alterungsverhalten von Kunst-stoffpulvern vorgestellt. In einem Modellversuch wurde der Verarbeitungsprozess für PA12-Pulver nachgestellt und somit verschiedene Alterungsstufen generiert. Beson-deres Augenmerk wurde auf den Einfluss einer Materialvorbehandlung gelegt. Die gealterten Pulver wurden physikalisch und thermoanalytisch hinsichtlich ihrer verar-beitungsrelevanten Materialeigenschaften untersucht.

Thermographie zur Temperaturmessung beim Laser-Sintern – ein Beitrag zur Qualitätssicherung?

Beim Laser-Sintern wird das Pulverbett durch Heizstrahler vorgeheizt, um an der Pulveroberfläche eine Temperatur knapp unterhalb des Materialschmelzpunktes zu erzielen. Dabei soll die Temperaturverteilung auf der Oberfläche möglichst homogen sein, um gleiche Bauteileigenschaften im gesamten Bauraum zu erzielen und den Bauteilverzug gering zu halten. Erfahrungen zeigen jedoch sehr inhomogene Temperaturverteilungen, weshalb oftmals die Integration von neuen oder optimierten Prozessüberwachungssystemen in die Anlagen gefordert wird. Ein potentiell einsetzbares System sind Thermographiekameras, welche die flächige Aufnahme von Oberflächentemperaturen und somit Aussagen über die Temperaturen an der Pulverbettoberfläche erlauben. Dadurch lassen sich kalte Bereiche auf der Oberfläche identifizieren und bei der Prozessvorbereitung berücksichtigen. Gleichzeitig ermöglicht die Thermografie eine Beobachtung der Temperaturen beim Lasereingriff und somit das Ableiten von Zusammenhängen zwischen Prozessparametern und Schmelzetemperaturen. Im Rahmen der durchgeführten Untersuchungen wurde ein IR-Kamerasystem erfolgreich als Festeinbau in eine Laser-Sinteranlage integriert und Lösungen für die hierbei auftretenden Probleme erarbeitet. Anschließend wurden Untersuchungen zur Temperaturverteilung auf der Pulverbettoberfläche sowie zu den Einflussfaktoren auf deren Homogenität durchgeführt. In weiteren Untersuchungen wurden die Schmelzetemperaturen in Abhängigkeit verschiedener Prozessparameter ermittelt. Auf Basis dieser Messergebnisse wurden Aussagen über erforderliche Optimierungen getroffen und die Nutzbarkeit der Thermografie beim Laser-Sintern zur Prozessüberwachung, -regelung sowie zur Anlagenwartung als erster Zwischenstand der Untersuchungen bewertet.

Ursachen für eine mangelnde Reproduzierbarkeit beim Laser-Sintern von Kunststoffbauteilen

Das Laser-Sintern hat sich in den letzten Jahren zunehmend als Kleinserienfertigungsverfahren für Kunststoffbauteile etabliert. Dennoch entspricht die Bauteilqualität aufgrund von Verzug oder mangelnder Reproduzierbarkeit der Eigenschaften oftmals nicht den Anforderungen. Ein Grund hierfür ist die inhomogene Temperaturführung während des Prozesses. So ergeben sich aufgrund einer inhomogenen Temperaturverteilung auf der Pulverbettoberfläche sowie durch unterschiedliche Abkühlgeschwindigkeiten im Pulverbett zum Teil deutliche lokale Unterschiede im Temperatur-Zeit-Verhalten. Grundlegende Untersuchungen zu diesen Effekten fehlen jedoch bislang. Im Rahmen der dargestellten Untersuchungen gilt es daher zum einen die Reproduzierbarkeit verschiedener Laser-Sinter-Anlagen in Bezug auf die mechanischen Eigenschaften, die Maßhaltigkeit und die Bauteildichte zu analysieren und zum anderen diese Ergebnisse mit den lokalen Temperatur- und Abkühlbedingungen im Pulverbett zu korrelieren. Dabei werden durch thermografische Untersuchungen die Temperaturverteilung an der Pulverbett-oberfläche charakterisiert sowie durch Einsatz entsprechender Funk-Temperatur-messsensorik die lokalen Abkühlbedingungen von Bauteilen innerhalb des Pulverbettes analysiert. Diese lokalen Temperatur- und Abkühlbedingungen sollen anschließend mit positionsabhängigen Analysen zum Bauteilschrumpf korreliert werden. Abschließend werden Optimierungspotentiale für ein neuentwickeltes Temperaturführungssystem mit homogeneren Temperatur- und Abkühlbedingungen abgeleitet.

Vom Metallpulver zum Gesenk Bauteil

Zur schnellen Herstellung von Metallteilen eignen sich die schichtweise Rapid Prototyping Verfahren. Zum einen ist die direkte Herstellung aus Zweikomponenten-Metallpulver möglich, zum anderen lassen sich aus Kunststoffüberzogenen Metallpulvern durch Infiltration komplexe Metallteile fertigen. Der Vortrag beschreibt die Prozessketten der beiden Verfahren und stellt ihre besonderen Eigenschaften gegenüber. Anhand von Praxisbeispielen wird die tatsächliche Leistungsfähigkeit beider Verfahren aufgeführt. Es werden die beiden Verfahren “Direct Metal Laser Sintering“ (DMLS) und “Indirect Metal Laser Sintering“ (IMLS) zur Herstellung von Gesenken und Bauteilen vorgestellt. Das “Direct Metal Laser Sintering“ wird in Zusammenarbeit mit der Fa. Daimler-Chrysler vorgestellt, die mit ihrer EOS Sinteranlage ein Benchmarkwerkzeug mit konturnaher Kühlung gefertigt haben. Das “Indirect Metal Laser Sintering“ wird an der Universität Duisburg-Essen angewandt. Hier wurden diverse Bauteile bzw. Gesenke in Zusammenarbeit mit der Fa. Powercut oder dem ZBT hergestellt.

SLM von Polylactiden zur Herstellung von resorbierbaren Implantaten

Rapid Manufacturing von individuellen Implantaten mittels Selective Laser Melting (SLM) wurde für metallische Standardwerkstoffe in der Medizintechnik (Titanlegierungen, Kobalt-Chrom-Legierungen, Stahl) realisiert. Dies sind permanente Implantate, die entweder dauerhaft im Körper verbleiben oder in einer zweiten Operation entfernt werden. Eine vom ILT mittels SLM hergestellte Hüftpfanne aus TiAl6V4 konnte bereits erfolgreich im Patienten implantiert werden. Die regenerative Therapie ist jedoch die klinisch bevorzugte Strategie. Das bedeutet, dass der Selbstheilungsprozess des menschlichen Körpers für die Heilung von großen Knochendefekten genutzt wird. Ein neuer Ansatz zur Implantatfertigung folgt dieser Strategie. Der SLM-Prozess wird für die Verarbeitung von bioresorbierbaren Werkstoffen entwickelt um individuelle Implantate zu fertigen, die im Körper abgebaut und durch körpereigenes Knochengewebe ersetzt werden. Diese Arbeit beschreibt die Qualifizierung des SLM Verfahrens für die Verarbeitung von einem Kompositmaterial aus Polylactid / β-Tricalciumphosphat (PDLLA/β-TCP).

Funktionalisierte Bauteile durch Selektives Maskensintern

Das Selektive Maskensintern ist ein neues, pulverbasiertes Additives Fertigungsverfahren. Das schichtweise aufgebrachte Kunststoffpulver wird hier flächig über einen Infrarotstrahler belichtet und aufgeschmolzen. Das Verfahren bietet ein großes Potential dreidimensionale, wärmeleitfähige Bauteile mit beliebiger Geometrie herzustellen. In diesem Beitrag wird darauf eingegangen, wie kommerziell erhältliches Polyamid 12-Pulver mit thermisch leitfähigen Füllstoffen, wie Aluminiumgrieß und Kupferkugeln, modifiziert und funktionalisierte Bauteile hergestellt werden können. Prozessrelevante Materialeigenschaften werden mittels Differential Scanning Kalorimetrie, Rotationsviskosimetrie und der Wärmeleitfähigkeit der modifizierten Pulver bestimmt. An den gefertigten Bauteilen wird die ausgebildete Morphologie, die mechanischen Eigenschaften als auch die Bauteilwärmeleitfähigkeit untersucht.