The Effect of the Cu:Fe''' Ratio Upon the Current Efficiency in the Electrolysis of a Copper Sulfate Solution Containing Iron Sulfate

It is a well-known fact that, in the electrolysis of a CuSO4 solution containing iron sulfate, using insoluble anodes, with the depletion of copper, the point is finally reached where the current efficiency becomes zero. This decrease in current efficiency is due to the oxidation of the ferrous sulfate to the ferric condition at the anode, by the oxygen liberated. The resulting ferric sulfate diffuses over to the cathode and there dissolves copper from the cathode according to the chemical equation Cu + Fe2 (SO4)3 = CuSO4 + 2FeSO4. This copper, which has been deposited at the cathode by the electric current, is thus redissolved by the Fe2(SO4)3. The solution of the copper causes at the same time a formation of FeSO4 which in turn diffuses over to the anode and is there oxidized to Fe2(SO4)3; and so the cycle continues, using electric current without rendering useful work. E. H. Larison has noted that a definite amount of ferric salts must be reduced to the ferrous condition before all the copper will remain on the cathode; he does not state, however, just what this point is. L. Addicks has plotted the relation between current efficiency and ferric sulphate content. The existence of the results scattered the points more or less, although the decrease in current efficiency with increased ferric sulphate content is clearly indicated. E. T.Kern has likewise noted that the smaller the amount of copper in the solution, the greater is the reduction of current efficiency. In this work, therefore, it was desired to determine what amount of ferric iron was permissible in a copper sulfate solution of definite concentration before the current efficiency would drop to zero, and what, if any, was the effect of definite Cu:Fe’’’ratio upon the current efficiency of the electrolysis.

The Effect of the Fe2: Fe3 Ratio upon the Current Efficiency in the Electrolysis of a Copper Sulfate Solution Containing Iron Sulfate

In the treatment of copper ores by hydro-electro-metallurgical methods, not only is copper deposited, but other metals are also dissolved. In practice it has been found* that iron, under certain conditions, causes the copper to deposit on the cathode as a nonadherent precipitate and also that the iron in solution causes a great decrease in current efficiency, es­pecially when the electrolysis is conducted by operating with a higher current density at the cathode than at the anode. The present investigation deals with the effects of the two valences of iron on the current efficiency and endeavors to determine whether or not there is a ratio of the two at which point the efficiency becomes zero or approaches it.

The Effects of Zinc Sulphate, Manganese Sulphate, and Iron Sulphate on the Lead Storage Cell.

The lead storage battery as it is used today is made up of the pasted type plates of lead dioxide, the anode, and sponge lead, the cathode, and wooden or hard rubber separators, which serve to insulate these from one another. In manufacturing these, it is desirable to keep them free from impurities.

Refining of Low Grade Zinc-Gold Precipitates

The purpose of this investigation was to ascertain if advantage could be taken of the copper in the precipitates as a collecting agent of the precious metals in the direct smelting furnace.The products produced to be low grade anode bullion and a slag low in precious metals, high in zinc and lead.

An Investigation of the Anodic Oxidation of Aluminum in a Sulfuric Acid Electrolyte

When aluminum is allowed to stand in air or is heated in air, a thin oxide film is produced on the metal. If aluminum is made the anode in a suitable electrolyte and a current applied, a coating is obtained which is similar to that produced in air, but may be effected much quicker. This film is thicker, harder, more resistant to corrosion and abrasion, and more adhesive than the natural oxide. The film is porous and makes an excellent adsorptive for dyes and pigments.