The Effect of the Cu:Fe''' Ratio Upon the Current Efficiency in the Electrolysis of a Copper Sulfate Solution Containing Iron Sulfate

It is a well-known fact that, in the electrolysis of a CuSO4 solution containing iron sulfate, using insoluble anodes, with the depletion of copper, the point is finally reached where the current efficiency becomes zero. This decrease in current efficiency is due to the oxidation of the ferrous sulfate to the ferric condition at the anode, by the oxygen liberated. The resulting ferric sulfate diffuses over to the cathode and there dissolves copper from the cathode according to the chemical equation Cu + Fe2 (SO4)3 = CuSO4 + 2FeSO4. This copper, which has been deposited at the cathode by the electric current, is thus redissolved by the Fe2(SO4)3. The solution of the copper causes at the same time a formation of FeSO4 which in turn diffuses over to the anode and is there oxidized to Fe2(SO4)3; and so the cycle continues, using electric current without rendering useful work. E. H. Larison has noted that a definite amount of ferric salts must be reduced to the ferrous condition before all the copper will remain on the cathode; he does not state, however, just what this point is. L. Addicks has plotted the relation between current efficiency and ferric sulphate content. The existence of the results scattered the points more or less, although the decrease in current efficiency with increased ferric sulphate content is clearly indicated. E. T.Kern has likewise noted that the smaller the amount of copper in the solution, the greater is the reduction of current efficiency. In this work, therefore, it was desired to determine what amount of ferric iron was permissible in a copper sulfate solution of definite concentration before the current efficiency would drop to zero, and what, if any, was the effect of definite Cu:Fe’’’ratio upon the current efficiency of the electrolysis.

The Effect of the Fe2: Fe3 Ratio upon the Current Efficiency in the Electrolysis of a Copper Sulfate Solution Containing Iron Sulfate

In the treatment of copper ores by hydro-electro-metallurgical methods, not only is copper deposited, but other metals are also dissolved. In practice it has been found* that iron, under certain conditions, causes the copper to deposit on the cathode as a nonadherent precipitate and also that the iron in solution causes a great decrease in current efficiency, es­pecially when the electrolysis is conducted by operating with a higher current density at the cathode than at the anode. The present investigation deals with the effects of the two valences of iron on the current efficiency and endeavors to determine whether or not there is a ratio of the two at which point the efficiency becomes zero or approaches it.

The Effect of Impurities on the Electrodeposition of Zinc from Zinc Sulfate Solution Containing Antimony.

It has been proven by research and years of experience, that before electrolytic zinc is possible, the electrolyte, as zinc sulfate solution must be prepared as pure as is economical. In other words, the ideal electrolyte must only be a solution of one metal - zinc. Every other metal and carbon must be excluded if good recovery and a firm deposit is to be obtained.

The Electroplating of Cadmium from Sulfate Solutions

It has been proven that cadmium forms a very satisfactory plate on steel, which has to withstand severe corrosion, especially the corrosion of sea water and spray. The metal is now successfully plated electrolytically from cyanide solutions, but wherever work is carried on with cyanide, there is great danger of poisoning to the workers.

Magnesium - Tellurium by Powder Methods

Today considerable work is being done in the compressed metal powder field which is gradually ob­taining prominence as a valuable branch of metallurgy. The mass of data, however, has led to many different ideas on the results of sintering.

The Age-Hardening of Magnesium with Aluminum and Zinc

Magnesium is one of the most active elements and forms oxides, nitrides, and carbides, but not hydrides. Due to its activity, low melting point, low strength when unalloyed, and the difficulty with which it is worked, magnesium has not been and is not at present well developed.

Zinc Plating Magnesium

Magnesium and magnesium alloys are becoming more and more important in modern industry. Their use in the aviation industry has been greatly curtailed because of their comparatively poor resistance to corrosion especially in moist atmospheres. Many methods have been adopted to improve their resistance to corrosion.

Electroplating of Chromium upon a Nickel Plated Magnesium Alloy

A nickel plating operation for magnesium alloys was investigated and proved successful in plating a small sample of a typical commercial magnesium alloy, Dowmetal J1.

The Effect of Manganese and Magnesium on the Hardening of Copper-Aluminum Alloys

During recent years, duralumin and all aluminum alloys have been made the object of much discussion regarding their hardening mechanism. The commercial success of nearly all of the alloys of aluminum and mag­nesium is dependent on their ability to age or precipitation harden.