The Rate of Precipitation of Copper Aluminide in the Silver Rich Silver-Copper-Aluminum Alloys

In order to determine the best annealing temperature at which to age-harden the alloys, hardness tests on speci­men annealed for different lengths of time at different temperatures were made.

The Electrical Conductivity of the Copper-Aluminum Alloys.

Among the many aluminum alloys which have been studied are the binary copper-aluminum alloys. These have proven to be among the most useful of the alumi­num alloys thus far worked upon.

Age Hardening of Copper Antimony Alloys

A large number of alloys of varying percentages of copper and antimony were prepared. These alloys were treated in various ways which might be expected to produce age hardening. The effect of cold working was studied in the range where the alloys were malleable.

The Electrodeposition of Copper-Cobalt Alloys

An attempt was made to deposit a 50:50 copper-cobalt alloy from various sulfate electrolytes. No true 50:50 alloy was obtained but various mixtures of cobalt and copper rich crystals were deposited.

The Effect of Manganese and Magnesium on the Hardening of Copper-Aluminum Alloys

During recent years, duralumin and all aluminum alloys have been made the object of much discussion regarding their hardening mechanism. The commercial success of nearly all of the alloys of aluminum and mag­nesium is dependent on their ability to age or precipitation harden.

The Effects of Some Percentages of Nickel on the Annealing of Cartridge Brass

The most important element in the alloying of steels, has also been used quite extensively as a third constituent in copper-zinc alloys. The chief characteristics of nickel which make it desirable as an alloying element are its toughness, high strength, and resistance to corrosion.

The Electrical Resistance of Metals and Alloys in Their Hard and Soft States

It is known that the electrical resistance of annealed metals is usually smaller than that of metals in their cold worked state. The curve showing the relation between electrical resistance and annealing temperature reaches a minimum; continued annealing at higher temperature produces an increase in the electrical resistance. In the case of alloys it has been noted that a second decrease occurs at higher annealing temperature. The following work corroborates the observance of previous investigations. The electrical resistance of cold worked copper, gold, nickel, and iron decreased with annealing and then increased, the minimum being around 300° C. or 400° C. Monel metal showed a minimum resistance followed by an increase which in turn was followed by a second decrease.

Alloys of Lead and Tellurium

Prior to the last few years little practical use was made of the element tellurium, which is obtained from gold and silver tellurides and from the slimes of electro­lytic copper refineries. Lately, however, more study has been made of its properties when alloyed with other metals. It was the purpose of this thesis to study the effects of the addition of tellurium to lead, particularly in small amounts.

An Experimental Investigation of the Age Hardening of Copper with Manganese Silicide

The subject of the thesis was based upon the theory of precipitation or age hardening of the copper by the compound formed by the Manganese and silicon present in the ternary Cu-Mn-Si alloy. The effect of the heat treat­ment to such an alloy was to be studied and the best aging time and temperature was to be determined.

Some Effects of the Addition of Tellurium to Lead Alloys

From the standpoint of its practical useful­ness, the most important characteristics of metallic lead are its cheapness, resistance to corrosion, plas­ticity, high specific gravity, low melting point, and its ability to form alloys in which some properties are modified by the addition of other elements, while other properties remain the same.

Age Hardening of Copper-Aluminum Alloy Castings

Age hardening occurs in alloys of the solid solution type containing a hardening constituent, be it metal or metallic compound, which is more soluble in the solvent phase at higher temperatures than at lower ones.

The Electrodeposition of Iron-Manganese Alloys

Various electrolytes were experimented with in an attempt to deposit an iron-manganese alloy. An Alloy was obtained from a solution containing ferrous ammonium sulfate, manganous sulfate, and ammonium sulfate. Further experimentation was done in an effort to determine the optimum conditions of deposition and the highest manganese alloy which could be produced.

The Electrodeposition of Iron-Manganese Alloys

An electrodeposition of an iron-manganese alloy was made from the same conditions determined by previous re­search. Various addition agents were experimented with in an attempt to produce better conditions for electro-deposition. It was found advantageous to add small a­mounts of sodium lauryl sulfate and ammonium sulfite to the electrolyte.

Hardness and Electrical Resistivity of Copper-Iron Powder Metal Compacts

Although powder metallurgical methods have been used for years to fabricate tungsten and platinum, very little scientific data have been recorded until the beginning of this century. A large percentage of all commercial production at present is based upon past practice rather than upon scientific knowledge.

An Investigation of Age-Hardening in a Commercial Copper-Beryllium Alloy

This investigation is concerned with the age-hardening process as exemplified by the aging of a commercial Cu-Be alloy and, in particular, with this pro­cess as determined by X-ray methods. The amount of infor­mation available on age-hardening of commercial alloys is scanty and what information there is, is inaccurate.