The Leaching of Electrodeposition of Iron

Electrolytic iron as deposited is brittle and therefore must be annealed. After annealing, the material is ductile and closely resembles copper in its behavior under work. It is claimed to be more resistant to corrosion than dead soft iron. It also has the advantage of corroding uniformly ( or­dinary soft iron develops pin holes which shorten its life considerably). The extreme purity of electrolytic iron namely makes it very suitable as a base metal for alloys. Its ductility opens up a field for use in the manufacture of cold rolled strip, seamless tubes, and wire.

Geology of Iron Deposits at Princeton Montana and Economic Aspects of Iron Ore in Montana

The purpose of this paper is to introduce to the reader, an iron deposit in the Princeton district, about 19 miles northeast by highway from Philipsburg, Montana. Heretofore there has been no written literature on this deposit. It is also intended to investigate the economic possibilities of iron ore in general in the State of Montana.

The Electrodeposition of Iron-Manganese Alloys

Various electrolytes were experimented with in an attempt to deposit an iron-manganese alloy. An Alloy was obtained from a solution containing ferrous ammonium sulfate, manganous sulfate, and ammonium sulfate. Further experimentation was done in an effort to determine the optimum conditions of deposition and the highest manganese alloy which could be produced.

Electrolytic Deposition of Iron

In this thesis the purpose was to obtain a good iron deposit from a relatively simple bath. The deposit was to be of good nature and low in Carbon content. Also included is a summary of the uses to which electrolytic iron can be put as well as a summary of work done by other researchers in depositing iron electrolytically.

The Electrodeposition of Iron-Manganese Alloys

An electrodeposition of an iron-manganese alloy was made from the same conditions determined by previous re­search. Various addition agents were experimented with in an attempt to produce better conditions for electro-deposition. It was found advantageous to add small a­mounts of sodium lauryl sulfate and ammonium sulfite to the electrolyte.

Production of Iron-Tin Compacts by Powder Metallurgy and a Synopsis of their Principle Properties

This thesis is concerned primarily with the production of metal powder compacts of iron and tin. In producing these compacts, the effects of process­ing variables on some of the essential properties of the pellets made were investigated.

The Corrosion Resistance of Iron-Tin Compacts as Produced by Powder Metallurgy

The art of Powder Metallurgy deals with the preparation of metal powders and their utilization. As a more pertinent definition, the following has been suggest­ed: "Powder Metallurgy is the art of producing metal powders and shaped objects from individual, mixed, or alloyed metal powders, with or without the inclusion of non-metallic consti­tuents".

Electro-Deposition of Iron from a Chloride Bath

Iron was electro-deposited from a ferrous chloride bath. Studies were made of deposits formed when current density was varied, and fin­ally when both current density and temperature were changed. An attempt was made to lay the ground work for a long range study of the chloride bath, and to determine the most simple conditions possible for obtaining a smooth, even, and thick deposit.

Corrosion Testing of Iron-Tin Alloys by the Salt Spray Method

The purpose of this study was to determine the rela­tive rate of corrosion of iron-tin alloys containing low percentages of tin. Since in the world today, a great deal of work is being done to develop large tin deposits and new methods devised to treat these ores, it is possible that the metal will become abundant and will obtain a more important position in the metal industry.

The Electrodeposition of Iron-Manganese Alloys

Although the alteration of properties resulting from the alloying of metals in their usual commercial forms has been extensively investigated, the field of electrodeposition of alloys is believed generally not to have received the atten­tion that it merits.

The Effect of the Fe2: Fe3 Ratio upon the Current Efficiency in the Electrolysis of a Copper Sulfate Solution Containing Iron Sulfate

In the treatment of copper ores by hydro-electro-metallurgical methods, not only is copper deposited, but other metals are also dissolved. In practice it has been found* that iron, under certain conditions, causes the copper to deposit on the cathode as a nonadherent precipitate and also that the iron in solution causes a great decrease in current efficiency, es­pecially when the electrolysis is conducted by operating with a higher current density at the cathode than at the anode. The present investigation deals with the effects of the two valences of iron on the current efficiency and endeavors to determine whether or not there is a ratio of the two at which point the efficiency becomes zero or approaches it.