The Age-Hardening of Duralumin

The development of wrought alloys of aluminum to which high strength and ductility can be imparted by heat treatment began with the work of Wilm and Claesser in Germany, 1905­-1911. During this time an alloy was developed which was later commercially produced in that country under the tradename of duralumin. The need for strong, light alloys for aircraft during the World War greatly hastened the development of duralumin.

Age Hardening of Silver-Platinum Alloys

The alloy system selected for study was the binary alloy of platinum and silver. An examination of the various silver alloy diagrams revealed that of several possible alloys, the silver platinum was the most suit­able with regard to solubility.

The Age Hardening of Copper with Manganese Silicide.

The increase in hardness is attributed to the manganese silicide being precipitated from solid solution and deposited between crystal planes. The subsequent softening which occurs on prolonging the period of reheating is believed to be due to an agglomeration of the dispersed hardening agent.

The Age Hardening of Silver with Copper-Silicide

The successful application of the phenomenon of pre­cipitation hardening to aluminum and copper has indicated the possibility of hardening all metals in the same way. The phenomenon of age hardening was discoveredin 1911, and since that time much research has been car­ried on in all parts of the world on various alloy sys­tems.

The Age-Hardening of Magnesium with Aluminum and Zinc

Magnesium is one of the most active elements and forms oxides, nitrides, and carbides, but not hydrides. Due to its activity, low melting point, low strength when unalloyed, and the difficulty with which it is worked, magnesium has not been and is not at present well developed.

The Age-Hardening of Aluminum with MgZn2

The purpose of this thesis is to investigate the age-hardening of aluminum with magnesium and zinc in such proportions as to conform to the compound MgZn2. Because of a lack of time and proper equipment, the only property investigated was the hardness as indicated by the Rockwell Superficial Hardness Tester.

An Experimental Investigation of the Age Hardening of Copper with Manganese Silicide

The subject of the thesis was based upon the theory of precipitation or age hardening of the copper by the compound formed by the Manganese and silicon present in the ternary Cu-Mn-Si alloy. The effect of the heat treat­ment to such an alloy was to be studied and the best aging time and temperature was to be determined.

An Experimental Investigation of the Age Hardening of Nickel with Boron

Since 1911, at which time, the age hardening phenomenon of duralumin was discovered by Film, much re­search has been carried on investigating the various alloy systems. The successful application of age hardening to the copper aluminum system (duralumin) has indicated the possibility of hardening practically all the metals in the same way.

An Investigation of the Age-Hardening of Copper with Nickel-Boron Compounds

Boron is an element whose metallurgical possibil­ities have never been fully investigated. The principal reason for this fact seems to lie in the difficulties encountered in preparing elemental boron and its various intermetallic compounds.

Age Hardening of Copper-Aluminum Alloy Castings

Age hardening occurs in alloys of the solid solution type containing a hardening constituent, be it metal or metallic compound, which is more soluble in the solvent phase at higher temperatures than at lower ones.

Age Hardening of Copper Antimony Alloys

A large number of alloys of varying percentages of copper and antimony were prepared. These alloys were treated in various ways which might be expected to produce age hardening. The effect of cold working was studied in the range where the alloys were malleable.

The Effect of Manganese and Magnesium on the Hardening of Copper-Aluminum Alloys

During recent years, duralumin and all aluminum alloys have been made the object of much discussion regarding their hardening mechanism. The commercial success of nearly all of the alloys of aluminum and mag­nesium is dependent on their ability to age or precipitation harden.

An Investigation of Age-Hardening in a Commercial Copper-Beryllium Alloy

This investigation is concerned with the age-hardening process as exemplified by the aging of a commercial Cu-Be alloy and, in particular, with this pro­cess as determined by X-ray methods. The amount of infor­mation available on age-hardening of commercial alloys is scanty and what information there is, is inaccurate.