Expansion of mortar bars in the presence of potassium acetate deicer

Carboxylate-based deicing and anti-icing chemicals became widely used in the mid 1990s, replacing more environmentally burdensome chemicals. Within a few years of their adoption, distress of portland cement concrete runways was reported by a few airports using the new chemicals. Distress manifested characteristics identical to that of alkali silica reactivity (ASR), but onset occurred early in the pavement’s operating life and with pavements thought to contain innocuous aggregate. The carboxylate-based deicing chemicals were suspected of exacerbating ASR-like expansion. Innocuous, moderately, and highly reactive aggregates were tested using modified ASTM C1260 and ASTM C1567 procedures with soak solutions containing deicer solutions and sodium hydroxide or potassium hydroxide. ASR-like expansion is exacerbated in the presence of potassium acetate. The expansion rate produced by a given aggregate is also a function of the alkali hydroxide used. Petrographic analyses were performed on thin sections prepared from mortar bars used in the experiments. Expansion occurred via two mechanisms; rupture of aggregate grains and expansion of paste.

Nanomechanics of cellulose crystals and cellulose-based polymer composites

Cellulose-polymer composites have potential applications in aerospace and transportation areas where lightweight materials with high mechanical properties are needed. In addition, these economical and biodegradable composites have been shown to be useful as polymer electrolytes, packaging structures, optoelectronic devices, and medical implants such as wound dressing and bone scaffolds. In spite of the above mentioned advantages and potential applications, due to the difficulties associated with synthesis and processing techniques, application of cellulose crystals (micro and nano sized) for preparation of new composite systems is limited. Cellulose is hydrophilic and polar as opposed to most of common thermoplastics, which are non-polar. This results in complications in addition of cellulose crystals to polymer matrices, and as a result in achieving sufficient dispersion levels, which directly affects the mechanical properties of the composites. As in other composite materials, the properties of cellulose-polymer composites depend on the volume fraction and the properties of individual phases (the reinforcement and the polymer matrix), the dispersion quality of the reinforcement through the matrix and the interaction between CNCs themselves and CNC and the matrix (interphase). In order to develop economical cellulose-polymer composites with superior qualities, the properties of individual cellulose crystals, as well as the effect of dispersion of reinforcements and the interphase on the properties of the final composites should be understood. In this research, the mechanical properties of CNC polymer composites were characterized at the macro and nano scales. A direct correlation was made between: Dispersion quality and macro-mechanical properties Nanomechanical properties at the surface and tensile properties CNC diameter and interphase thickness Lastly, individual CNCs from different sources were characterized and for the first time size-scale effect on their nanomechanical properties were reported. Then the effect of CNC surface modification on the mechanical properties was studied and correlated to the crystalline structure of these materials.