SOLUTE-DERIVED THERMAL STABILITY OF NANOCRYSTALLINE ALUMINUM AND PROCESSING FACTOR INFLUENCE ON THE FORMATION OF AL6MN QUASICRYSTALS IN MELT-SPINNING

Thermal stability of nanograined metals can be difficult to attain due to the large driving force for grain growth that arises from the significant boundary area constituted by the nanostructure. Kinetic approaches for stabilization of the nanostructure effective at low homologous temperatures often fail at higher homologous temperatures. Thermodynamic approaches for thermal stabilization may offer higher temperature stability. In this research, modest alloying of aluminum with solute (1 at.% Sc, Yb, or Sr) was examined as a means to thermodynamically stabilize a bulk nanostructure at elevated temperatures. After using melt-spinning and ball-milling to create an extended solid-solution and nanostructure with average grain size on the order of 30-45 nm, 1 h annealing treatments at 673 K (0.72 Tm) , 773 K (0.83 Tm) , and 873 K (0.94 Tm) were applied. The alloys remain nanocrystalline (<100 nm) as measured by Warren-Averbach Fourier analysis of x-ray diffraction peaks and direct observation of TEM dark field micrographs, with the efficacy of stabilization: Sr>Yb>Sc. Disappearance of intermetallic phases in the Sr and Yb alloys in the x-ray diffraction spectra are observed to occur coincident with the stabilization after annealing, suggesting that precipitates dissolve and the boundaries are enriched with solute. Melt-spinning has also been shown to be an effective process to produce a class of ordered, but non-periodic crystals called quasicrystals. However, many of the factors related to the creation of the quasicrystals through melt-spinning are not optimized for specific chemistries and alloy systems. In a related but separate aspect of this research, meltspinning was utilized to create metastable quasicrystalline Al6Mn in an α-Al matrix through rapid solidification of Al-8Mn (by mol) and Al-10Mn (by mol) alloys. Wheel speed of the melt-spinning wheel and orifice diameter of the tube reservoir were varied to determine their effect on the resulting volume proportions of the resultant phases using integrated areas of collected x-ray diffraction spectra. The data were then used to extrapolate parameters for the Al-10Mn alloy which consistently produced Al6Mn quasicrystal with almost complete suppression of the equilibrium Al6Mn orthorhombic phase.

THE FANNED FLAMES OF DISCONTENT: A SOLIDARITY-INSPIRED HISTORY OF THE IDENTITY/IDEOLOGY, CULTURAL HISTORY, AND RHETORICAL STRATEGIES OF THE WOBBLIES DURING THE 1916 MINNESOTA IRON ORE STRIKE

Rooted in critical scholarship this dissertation is an interdisciplinary study, which contends that having a history is a basic human right. Advocating a newly conceived and termed, Solidarity-inspired History framework/practice perspective, the dissertation argues for and then delivers a restorative voice to working-class historical actors during the 1916 Minnesota Iron Ore Strike. Utilizing an interdisciplinary methodological framework the dissertation combines research methods from the Humanities and the Social Sciences to form a working-class history that is a corrective to standardized studies of labor in the late 19th and early 20th centuries. Oftentimes class interests and power relationships determine the dominant perspectives or voices established in history and disregard people and organizations that run counter to, or in the face of, customary or traditional American themes of patriotism, the Protestant work ethic, adherence to capitalist dogma, or United States exceptionalism. This dissertation counteracts these traditional narratives with a unique, perhaps even revolutionary, examination of the 1916 Minnesota Iron Ore Strike. The intention of this dissertation's critical perspective is to poke, prod, and prompt academics, historians, and the general public to rethink, and then think again, about the place of those who have been dislocated from or altogether forgotten, misplaced, or underrepresented in the historical record. Thus, the purpose of the dissertation is to give voice to historical actors in the dismembered past. Historical actors who have run counter to traditional American narratives often have their body of "evidence" disjointed or completely dislocated from the story of our nation. This type of disremembering creates an artificial recollection of our collective past, which de-articulates past struggles from contemporary groups seeking solidarity and social justice in the present. Class-conscious actors, immigrants, women, the GLBTQ community, and people of color have the right to be remembered on their own terms using primary sources and resources they produced. Therefore, similar to the Wobblies industrial union and its rank-and-file, this dissertation seeks to fan the flames of discontented historical memory by offering a working-class perspective of the 1916 Strike that seeks to interpret the actions, events, people, and places of the strike anew, thus restoring the voices of these marginalized historical actors.