Creep and shrinkage behavior of ultra high-performance concrete under compressive loading with varying curing regimes

This Ultra High Performance Concrete research involves observing early-age creep and shrinkage under a compressive load throughout multiple thermal curing regimes. The goal was to mimic the conditions that would be expected of a precast/prestressing plant in the United States, where UHPC beams would be produced quickly to maximize a manufacturing plant’s output. The practice of steam curing green concrete to accelerate compressive strengths for early release of the prestressing tendons was utilized (140°F [60°C], 95% RH, 14 hrs), in addition to the full thermal treatment (195°F [90°C], 95% RH, 48 hrs) while the specimens were under compressive loading. Past experimental studies on creep and shrinkage characteristics of UHPC have only looked at applying a creep load after the thermal treatment had been administered to the specimens, or on ambient cured specimens. However, this research looked at mimicking current U.S. precast/prestressed plant procedures, and thus characterized the creep and shrinkage characteristics of UHPC as it is thermally treated under a compressive load. Michigan Tech has three moveable creep frames to accommodate two loading criteria per frame of 0.2f’ci and 0.6f’ci. Specimens were loaded in the creep frames and moved into a custom built curing chamber at different times, mimicking a precast plant producing several beams throughout the week and applying a thermal cure to all of the beams over the weekend. This thesis presents the effects of creep strain due to the varying curing regimes. An ambient cure regime was used as a baseline for the comparison against the varying thermal curing regimes. In all cases of thermally cured specimens, the compressive creep and shrinkage strains are accelerated to a maximum strain value, and remain consistent after the administration of the thermal cure. An average creep coefficient for specimens subjected to a thermal cure was found to be 1.12 and 0.78 for the high and low load levels, respectively. Precast/pressed plants can expect that simultaneously thermally curing UHPC elements that are produced throughout the week does not impact the post-cure creep coefficient.

Life cycle assessment of trayless dining

Universities in the United States are applying more sustainable approaches to their dining service operations. "The increase in social consciousness and environmental stewardship on college campuses has spurred an array of new and innovative sustainability programs"(ARAMARK Higher Education 2008). University residence dining is typically cafeteria style, with students using trays to carry food. Studies report that food served without trays substantially reduces food waste and water and electrical consumption associated with washing trays. Commonly, these reported results are estimates and not measurements taken under actual operating conditions. This study utilizes measurements recorded under actual dining service conditions in student residence halls at Michigan Technological University to develop the following: 1) operational-specific data on the issues and potential savings associated with a conversion to trayless dining and 2) life cycle assessment (LCA) cost and environmental impact analyses comparing dining with and without trays. For the LCA, the entire life cycle of the system is considered, from the manufacturing to the usage and disposal phases. The study shows that trayless dining reduces food waste because diners carry less food. The total savings for the diner shifts when not using trays for the standard academic year (205 days), with an average number of 700 diners, is 7,032 pounds of food waste from the pre-rinse area (33% reduction) and 3,157 pounds of food waste from the pan washing area (39% reduction). In addition, for each day of the study, the diners consumed more food during the trayless portion of the experiment. One possible explanation for the increased food consumption during this short duration study could be that the diners found it more convenient to eat the extra food on their plate rather than carrying it back for disposal. The trayless dining experiment shows a reduction in dishwasher water, steam, and electrical consumption for each day of the study. The average reduction of dishwasher water, steam, and electrical consumption over the duration of the study were 10.7%, 9.5%, and 6.4% respectively. Trayless dining implementation would result in a decrease of 4,305 gallons of consumption and wastewater discharge, 2.87 mm BTU of steam consumption, and 158 kWh of electrical consumption for the dinner shift over the academic year. Results of the LCA indicate a total savings of $190.4 when trays are not used during the dinner shift. Trayless dining requires zero CO2 eq and cumulative energy demand in the manufacturing stage, reductions of 1005 kg CO2 eq and 861 MJ eq in the usage phase, and reductions of 6458 kg CO2 eq and 1821 MJ eq in the end of the life cycle.

EXPERIMENTAL INVESTIGATION OF CERTAIN INTERNAL CONDENSING AND BOILING FLOWS: THEIR SENSITIVITY TO PRESSURE FLUCTUATIONS AND HEAT TRANSFER ENHANCEMENTS

Space-based (satellite, scientific probe, space station, etc.) and millimeter – to – microscale (such as are used in high power electronics cooling, weapons cooling in aircraft, etc.) condensers and boilers are shear/pressure driven. They are of increasing interest to system engineers for thermal management because flow boilers and flow condensers offer both high fluid flow-rate-specific heat transfer capacity and very low thermal resistance between the fluid and the heat exchange surface, so large amounts of heat may be removed using reasonably-sized devices without the need for excessive temperature differences. However, flow stability issues and degradation of performance of shear/pressure driven condensers and boilers due to non-desirable flow morphology over large portions of their lengths have mostly prevented their use in these applications. This research is part of an ongoing investigation seeking to close the gap between science and engineering by analyzing two key innovations which could help address these problems. First, it is recommended that the condenser and boiler be operated in an innovative flow configuration which provides a non-participating core vapor stream to stabilize the annular flow regime throughout the device length, accomplished in an energy-efficient manner by means of ducted vapor re-circulation. This is demonstrated experimentally. Second, suitable pulsations applied to the vapor entering the condenser or boiler (from the re-circulating vapor stream) greatly reduce the thermal resistance of the already effective annular flow regime. For experiments reported here, application of pulsations increased time-averaged heat-flux up to 900 % at a location within the flow condenser and up to 200 % at a location within the flow boiler, measured at the heat-exchange surface. Traditional fully condensing flows, reported here for comparison purposes, show similar heat-flux enhancements due to imposed pulsations over a range of frequencies. Shear/pressure driven condensing and boiling flow experiments are carried out in horizontal mm-scale channels with heat exchange through the bottom surface. The sides and top of the flow channel are insulated. The fluid is FC-72 from 3M Corporation.