Osteoarthritis (OA) is a debilitating disease that is becoming more prevalent in today’s society. OA affects approximately 28 million adults in the United States alone and when present in the knee joint, usually leads to a total knee replacement. Numerous studies have been conducted to determine possible methods to halt the initiation of OA, but the structural integrity of the menisci has been shown have a direct effect on the progression of OA. Menisci are two C-shaped structures that are attached to the tibial plateau and aid in facilitating proper load transmission within the knee. The meniscal cross-section is wedge-like to fit the contour of the femoral condyles and help attenuate stresses on the tibial plateau. While meniscal tears are common, only the outer 1/3 of the meniscus is vascularized and has the capacity to heal, hence tears of the inner 2/3rds are generally treated via meniscectomy, leading to OA. To help combat this OA epidemic, an effective biomimetric meniscal replacement is needed. Numerous mechanical and biochemical studies have been conducted on the human meniscus, but very little is known about the mechanical properties on the nano-scale and how meniscal constituents are distributed in the meniscal cross-section. The regional (anterior, central and posterior) nano-mechanical properties of the meniscal superficial layers (both tibial and femoral contacting) and meniscal deep zone were investigated via nanoindentation to examine the regional inhomogeneity of both the lateral and medial menisci. Additionally, these results were compared to quantitative histological values to better formulate a structure-function relationship on the nano-scale. These data will prove imperative for further advancements of a tissue engineered meniscal replacement.

Processing and mechanical properties of cast aluminum containing scandium, zirconium, and ytterbium

A series of aluminum alloys containing additions of scandium, zirconium, and ytterbium were cast to evaluate the effect of partial ytterbium substitution for scandium on tensile behavior. Due to the high price of scandium, a crucible-melt interaction study was performed to ensure no scandium was lost in graphite, alumina, magnesia, or zirconia crucibles after holding a liquid Al-Sc master alloy for 8 hours at 900 °C in an argon atmosphere. The alloys were subjected to an isochronal aging treatment and tested for conductivity and Vickers microhardness after each increment. For scandium-containing alloys, peak hardnesses of 520-790 MPa, and peak tensile stresses of 138-234 MPa were observed after aging from 150-350 °C for 3 hours in increments of 50 °C, and for alloys without scandium, peak hardnesses of 217-335 MPa and peak tensile stresses of 45-63 MPa were observed after a 3 hour, 150 °C aging treatment. The hardness and tensile strength of the ytterbium containing alloy was found to be lower than in the alloy with no ytterbium substitution.