CO-ELECTROPHORETIC DEPOSITION OF LIQUID METAL AND SILICON FOR LITHIUM-ION BATTERY APPLICATION

A low cost electrophoretic deposition (EPD) process was successfully used for liquid metal thin film deposition with a high depositing rate of 0.6 µ/min. Furthermore, silicon nano-powder and liquid metal were then simultaneously deposited as the negative electrode of lithium-ion battery by a technology called co-EPD. The liquid metal was hoping to act as the matrix for silicon particles during lithium ion insertion and distraction. Half-cell testing was performed using as prepared co-EPD sample. An initial discharge capacity of 1500 mAh/g was reported for nano-silicon and galinstan electrode, although the capacity fading issue of these samples was also observed.

Numerical modeling of the failure mechanisms in Si thin film anode for Li-ion batteries

In recent times, the demand for the storage of electrical energy has grown rapidly for both static applications and the portable electronics enforcing the substantial improvement in battery systems, and Li-ion batteries have been proven to have maximum energy storage density in all rechargeable batteries. However, major breakthroughs are required to consummate the requirement of higher energy density with lower cost to penetrate new markets. Graphite anode having limited capacity has become a bottle neck in the process of developing next generation batteries and can be replaced by higher capacity metals such as Silicon. In the present study we are focusing on the mechanical behavior of the Si-thin film anode under various operating conditions. A numerical model is developed to simulate the intercalation induced stress and the failure mechanism of the complex anode structure. Effect of the various physical phenomena such as diffusion induced stress, plasticity and the crack propagation are investigated to predict better performance parameters for improved design.

Faulted Structures in Li Ion Exchanged NaMO2 (M=Ni(0.25)Mn(0.75))

A family of LiMO2 materials (M=Ni0.25Mn0.75) was prepared from Na1.2-xLixMO∂ precursors (0≤x≤0.6) via ion exchange. The resulting IE products were examined via XRD and compared to simulated XRD patterns produced using DIFFax to determine the defect structures resulting from the IE process. For the 0.1≤x≤0.6 materials, it is observed that there are 3 LiMO2 sub-phases with different Li contents present. As the amount of Li in the precursor increases, the amount of each phase changes resulting in a net shift to higher 2-theta; corresponding to an overall decrease in lattice parameter, approaching the theoretical values for LiMO2. Additionally, as x increases, the probability of O3-type shifting increases, most likely due to an increase in the amount O3-Li2MO3 minority phase which acts to weaken bonds in the TM layer, allowing the O3 shift to occur more easily. For the x=0 IE product, it was seen that the product had an ~O2-type structure, but with lattice parameters closer to those expected for a NaMO2 material.

NANOSCALE ELECTROCHEMISTRY BY IN-SITU TRANSMISSION ELECTRON MICROSCOPY

Nanoscale research in energy storage has recently focused on investigating the properties of nanostructures in order to increase energy density, power rate, and capacity. To better understand the intrinsic properties of nanomaterials, a new and advanced in situ system was designed that allows atomic scale observation of materials under external fields. A special holder equipped with a scanning tunneling microscopy (STM) probe inside a transmission electron microscopy (TEM) system was used to perform the in situ studies on mechanical, electrical, and electrochemical properties of nanomaterials. The nanostructures of titanium dioxide (TiO2) nanotubes are characterized by electron imaging, diffraction, and chemical analysis techniques inside TEM. TiO2 nanotube is one of the candidates as anode materials for lithium ion batteries. It is necessary to study their morphological, mechanical, electrical, and electrochemical properties at atomic level. The synthesis of TiO2 nanotubes showed that the aspect ratio of TiO2 could be controlled by processing parameters, such as anodization time and voltage. Ammonium hydroxide (NH4OH) treated TiO2 nanotubes showed unexpected instability. Observation revealed the nanotubes were disintegrated into nanoparticles and the tubular morphology was vanished after annealing. The nitrogen compounds incorporated in surface defects weaken the nanotube and result in the collapse of nanotube into nanoparticles during phase transformation. Next, the electrical and mechanical properties of TiO2 nanotubes were studied by in situ TEM system. Phase transformation of anatase TiO2 nanotubes into rutile nanoparticles was studied by in situ Joule heating. The results showed that single anatase TiO2 nanotubes broke into ultrafine small anatase nanoparticles. On further increasing the bias, the nanoclusters of anatase particles became prone to a solid state reaction and were grown into stable large rutile nanoparticles. The relationship between mechanical and electrical properties of TiO2 nanotubes was also investigated. Initially, both anatase and amorphous TiO2 nanotubes were characterized by using I-V test to demonstrate the semiconductor properties. The observation of mechanical bending on TiO2 nanotubes revealed that the conductivity would increase when bending deformation happened. The defects on the nanotubes created by deformation helped electron transportation to increase the conductivity. Lastly, the electrochemical properties of amorphous TiO2 nanotubes were characterized by in situ TEM system. The direct chemical and imaging evidence of lithium-induced atomic ordering in amorphous TiO2 nanotubes was studied. The results indicated that the lithiation started with the valance reduction of Ti4+ to Ti3+ leading to a LixTiO2 intercalation compound. The continued intercalation of Li ions in TiO2 nanotubes triggered an amorphous to crystalline phase transformation. The crystals were formed as nano islands and identified to be Li2Ti2O4 with cubic structure (a = 8.375 Å). This phase transformation is associated with local inhomogeneities in Li distribution. Based on these observations, a new reaction mechanism is proposed to explain the first cycle lithiation behavior in amorphous TiO2 nanotubes.

SYNTHESIS OF GRAPHENE AND ITS APPLICATIONS FOR DYE-SENSITIZED SOLAR CELLS

Graphene, which is a two-dimensional carbon material, exhibits unique properties that promise its potential applications in photovoltaic devices. Dye-sensitized solar cell (DSSC) is a representative of the third generation photovoltaic devices. Therefore, it is important to synthesize graphene with special structures, which possess excellent properties for dye-sensitized solar cells. This dissertation research was focused on (1) the effect of oxygen content on the structure of graphite oxide, (2) the stability of graphene oxide solution, (3) the application of graphene precipitate from graphene oxide solution as counter electrode for DSSCs, (4) the development of a novel synthesis method for the three-dimensional graphene with honeycomb-like structure, and (5) the exploration of honeycomb structured graphene (HSG) as counter electrodes for DSSCs. Graphite oxide is a crucial precursor to synthesize graphene sheets via chemical exfoliation method. The relationship between the oxygen content and the structures of graphite oxides was still not explored. In this research, the oxygen content of graphite oxide is tuned by changing the oxidation time and the effect of oxygen content on the structure of graphite oxide was evaluated. It has been found that the saturated ratio of oxygen to carbon is 0.47. The types of functional groups in graphite oxides, which are epoxy, hydroxyl, and carboxylgroups, are independent of oxygen content. However, the interplanar space and BET surface area of graphite oxide linearly increases with increasing O/C ratio. Graphene oxide (GO) can easily dissolve in water to form a stable homogeneous solution, which can be used to fabricate graphene films and graphene based composites. This work is the first research to evaluate the stability of graphene oxide solution. It has been found that the introduction of strong electrolytes (HCl, LiOH, LiCl) into GO solution can cause GO precipitation. This indicates that the electrostatic repulsion plays a critical role in stabilizing aqueous GO solution. Furthermore, the HCl-induced GO precipitation is a feasible approach to deposit GO sheets on a substrate as a Pt-free counter electrode for a dye-sensitized solar cell (DSSC), which exhibited 1.65% of power conversion efficiency. To explore broad and practical applications, large-scale synthesis with controllable integration of individual graphene sheets is essential. A novel strategy for the synthesis of graphene sheets with three-dimensional (3D) Honeycomb-like structure has been invented in this project based on a simple and novel chemical reaction (Li2O and CO to graphene and Li2CO3). The simultaneous formation of Li2CO3 with graphene not only can isolate graphene sheets from each other to prevent graphite formation during the process, but also determine the locally curved shape of graphene sheets. After removing Li2CO3, 3D graphene sheets with a honeycomb-like structure were obtained. This would be the first approach to synthesize 3D graphene sheets with a controllable shape. Furthermore, it has been demonstrated that the 3D Honeycomb-Structured Graphene (HSG) possesses excellent electrical conductivity and high catalytic activity. As a result, DSSCs with HSG counter electrodes exhibit energy conversion efficiency as high as 7.8%, which is comparable to that of an expensive noble Pt electrode.