Investigation into the impact of grain boundaries, film interface, and crystallographic orientation on the ionic conductivity of thin film gadolinium-doped ceria

The research reported in this dissertation investigates the impact of grain boundaries, film interface, and crystallographic orientation on the ionic conductivity of thin film Gd-doped CeO2 (GDC). Chapter 2 of this work addresses claims in the literature that submicron grain boundaries have the potential to dramatically increase the ionic conductivity of GDC films. Unambiguous testing of this claim requires directly comparing the ionic conductivity of single-crystal GDC films to films that are identical except for the presence of submicron grain boundaries. In this work techniques have been developed to grow GDC films by RF magnetron sputtering from a GDC target on single crystal r plane sapphire substrates. These techniques allow the growth of films that are single crystals or polycrystalline with 80 nm diameter grains. The ionic conductivities of these films have been measured and the data shows that the ionic conductivity of single crystal GDC is greater than that of the polycrystalline films by more than a factor of 4 over the 400-700°C temperature range. Chapter 3 of this work investigates the ionic conductivity of surface and interface regions of thin film Gd-doped CeO2. In this study, single crystal GDC films have been grown to thicknesses varying from 20 to 500 nm and their conductivities have been measured in the 500-700°C temperature range. Decreasing conductivity with decreasing film thickness was observed. Analysis of the conductivity data is consistent with the presence of an approximately 50 nm layer of less conductive material in every film. This study concludes that the surface and interface regions of thin film GDC are less conductive than the bulk single crystal regions, rather than being highly conductive paths. Chapter 4 of this work investigates the ionic conductivity of thin film Gd-doped CeO2 (GDC) as a function of crystallographic orientation. A theoretical expression has been developed for the ionic conductivity of the [100] and [110] directions in single crystal GDC. This relationship is compared to experimental data collected from a single crystal GDC film. The film was grown to a thickness of _300 nm and its conductivity measured along the [100] and [110] orientations in the 500-700°C temperature range. The experimental data shows no statistically significant difference in the conductivities of the [100] and [110] directions in single crystal GDC. This result agrees with the theoretical model which predicts no difference between the conductivities of the two directions.

CHARACTERIZATION OF ELECTRODEPOSITED POLYANILINE BIOSENSOR PLATFORM FOR ESCHERICHIA COLI O157:H7 DETECTION

Amperometric electrodeposition has been used to obtain uniform, conductive, and repeatable polyaniline (PANi) thin films for use in nano scaled biochemical sensors. This report describes the characterization of these films. Techniques such as ellipsometry were used to test repeatability of the deposition and the uniformity of the deposited thin films. Raman spectroscopy was utilized to confirm the composition of the deposited PANi thin films. Fluorescence microscopy was used to determine the immobilization of antibodies to the PANi thin films using biotin-avidin interactions, as well as the density of active binding sites. Ellipsometry results demonstrated that biomolecules could be immobilized on PANi films as thin as 9nm. Evidence from the Raman spectroscopy demonstrated the conductive nature of the PANi films. The fluorescence microscopy demonstrated that antibodies could be immobilized on PANi films, although the experiment also demonstrated a low density of binding sites. The characterization demonstrates the utility of the PANi thin films as a conductive interface between the inorganic sensor platform and biochemical molecules.