Local degradation of structural, mechanical, electrical and chemical properties of membrane electrode assembly in polymer electrolyte fuel cell

Polymer electrolyte fuel cell (PEMFC) is promising source of clean power in many applications ranging from portable electronics to automotive and land-based power generation. However, widespread commercialization of PEMFC is primarily challenged by degradation. The mechanisms of fuel cell degradation are not well understood. Even though the numbers of installed units around the world continue to increase and dominate the pre-markets, the present lifetime requirements for fuel cells cannot be guarantee, creating the need for a more comprehensive knowledge of material’s ageing mechanism. The objective of this project is to conduct experiments on membrane electrode assembly (MEA) components of PEMFC to study structural, mechanical, electrical and chemical changes during ageing and understanding failure/degradation mechanism. The first part of this project was devoted to surface roughness analysis on catalyst layer (CL) and gas diffusion layer (GDL) using surface mapping microscopy. This study was motivated by the need to have a quantitative understanding of the GDL and CL surface morphology at the submicron level to predict interfacial contact resistance. Nanoindentation studies using atomic force microscope (AFM) were introduced to investigate the effect of degradation on mechanical properties of CL. The elastic modulus was decreased by 45 % in end of life (EOL) CL as compare to beginning of life (BOL) CL. In another set of experiment, conductive AFM (cAFM) was used to probe the local electric current in CL. The conductivity drops by 62 % in EOL CL. The future task will include characterization of MEA degradation using Raman and Fourier transform infrared (FTIR) spectroscopy. Raman spectroscopy will help to detect degree of structural disorder in CL during degradation. FTIR will help to study the effect of CO in CL. XRD will be used to determine Pt particle size and its crystallinity. In-situ conductive AFM studies using electrochemical cell on CL to correlate its structure with oxygen reduction reaction (ORR) reactivity

Sustainability study of nanomaterials including societal and occupational implications

In recent years there has been a tremendous amount of research in the area of nanotechnology. History tells us that the commercialization of technologies will always be accompanied by both positive and negative effects for society and the environment. Products containing nanomaterials are already available in the market, and yet there is still not much information regarding the potential negative effects that these products may cause. The work presented in this dissertation describes a holistic approach to address different dimensions of nanotechnology sustainability. Life cycle analysis (LCA) was used to study the potential usage of polyethylene filled with nanomaterials to manufacture automobile body panels. Results showed that the nanocomposite does not provide an environmental benefit over traditional steel panels. A new methodology based on design of experiments (DOE) techniques, coupled with LCA, was implemented to investigate the impact of inventory uncertainties. Results showed that data variability does not have a significant effect on the prediction of the environmental impacts. Material profiles for input materials did have a highly significant effect on the overall impact. Energy consumption and material characterization were identified as two mainstreams where additional research is needed in order to predict the overall impact of nanomaterials more effectively. A study was undertaken to gain insights into the behavior of small particles in contact with a surface exposed to air flow to determine particle lift-off from the surface. A mapping strategy was implemented that allows for the identification of conditions for particle liftoff based on particle size and separation distance from the wall. Main results showed that particles smaller than 0:1mm will not become airborne under shear flow unless the separation distance is greater than 15 nm. Results may be used to minimize exposure to airborne materials. Societal implications that may occur in the workplace were researched. This research task explored different topics including health, ethics, and worker perception with the aim of identifying the base knowledge available in the literature. Recommendations are given for different scenarios to describe how workers and employers could minimize the unwanted effects of nanotechnology production.