Effect of microstructure and alloying elements on the resistance of fastener grade steels to hydrogen assisted cracking

Fastener grade steels with varying alloy contents and heat treatments were employed to measure changes in resistance to hydrogen assisted cracking. The testing procedure compared notched tension specimens fractured in air to threshold stress values obtained during hydrogen charging, utilizing a rising step load procedure. Bainitic structures improved resistance by 10-20% compared to tempered martensite structures. Dual phase steels with a tempered martensite matrix and 20% ferrite were more susceptible and notch sensitive. High strength, fully pearlitic structures showed an improvement in resistance. Carbon content, per se, had no effect on the resistance of steel to hydrogen assisted cracking. Chromium caused a deleterious effect but all other alloying elements studied did not cause much change in hydrogen assisted cracking susceptibility.

From Mill Gates to Magic City: U.S. Steel and Welfare Capitalism in Gary, Indiana, 1906-1930

Gary, Indiana is a city with indelible ties to industrial paternalism. Founded in 1906 by United States Steel Corporation to house workers of the trust’s showpiece mill, the emergence of this model company town was both the culmination of lessons learned from its predecessors’ mistakes and innovative corporate planning. U.S. Steel’s Progressive Era adaptation of welfare capitalism characterized the young city through a combination of direct community involvement and laissez-faire social control. This thesis examines the reactionary implementation of paternalist policies in Gary between 1906 and 1930 through the purviews of three elements under corporate influence: housing, education, and social welfare. Each category demonstrates how both the corporation and citizenry affected and adapted Gary’s physical and cultural landscape, public perceptions, and community identity. Parallel to the popular narrative throughout is that of Gary’s African-American community, and the controversial circumstances of this population’s segregated development.