Elaboration et caractérisation de ciments géopolymères à base de scories volcaniques

Two types of volcanic ashes referenced as ZD (volcanic ashes from Djoungo) and ZG (volcanic ashes from Galim) were collected from two Cameroonian localities. They were characterized (chemical and mineralogical compositions, amorphous phase content, particle size distribution and specific surface area) and used as raw materials for the synthesis of geopolymer cements at ambient temperature of laboratory (24 ± 3 °C). The synthesized products were characterized by determining their setting time, linear shrinkage and compressive strength, X-ray Diffraction, Fourier Transform Infrared Spectroscopy and Scanning Electron Microscopy. The mineralogical composition, the amorphous phase content, the particle size distribution, the specific surface area of the volcanic ashes as well as the mass ratio of the alkaline solution (sodium silicate / sodium hydroxide) were the main parameters which influenced the synthesis of geopolymers with interesting characteristics at ambient temperature (24 ± 3 °C). The volcanic ashes (ZD) whose mineralogical composition contained anhydrite, low amorphous phase content and low specific surface area led to long setting times. Moreover, its products swelled and presented cracks due to the formation of ettringite and these resulted in low compressive strengths (7 to 19 MPa). The volcanic ashes (ZG) containing high amounts of amorphous phase and high specific surface area led geopolymers with setting times between 490 and 180 minutes and compressive strength between 7 and 50 MPa at ambient temperature of laboratory. The properties of geopolymers were improved when elaborated with a mixture of volcanic ashes and metakaolin (ZD–MK and ZG–MK). For geopolymers obtained from ZD–MK, the setting time was between 500 and 160 minutes while it was between 220 and 125 minutes for geopolymers obtained from ZG–MK. The compressive strength greatly increased between 23 and 68 MPa and 39 and 64 MPa for geopolymers obtained from ZG –MK and ZD–MK respectively. A comparative study of the properties of mixtures of metakaolin–alumina and volcanic ash–alumina based geopolymers shows that metakaolin is a good source of Al2O3 and SiO2 and which highly reactive with alkaline solution and produces geopolymers with better characteristics compared to volcanic ash based–geopolymer. The properties of volcanic ash–based geopolymer were also improved when amorphous alumina was incorporated into the volcanic ash. This additive is used to compensate the deficiencies in Al2O3 content in the volcanic ash. Compare to when volcanic ash is used alone 20 to 40 % incorporation of this additive corresponded to increases of the compressive strength by 18.1 % for metakaolin-alumina based-geopolymers and by 32.4 % for volcanic ash-based geopolymers.

DEVELOPMENT OF POROUS CONCRETE GEOPOLYMER USING HYDROGEN PEROXIDE AS BLOWING AGENT.

Metakaolin and volcanic ashes respectively called MK and ZG were used as aluminosilicate raw materials for the synthesis of porous geopolymers. The hydrogen peroxide was used as a blowing agent. The geopolymer prepared were characterized by Spectroscopy Fourier Transform Infrared (SFTI), X-ray Diffraction (XRD), Scanning Electron Microscopy (SEM) and the determination of some physical properties such as bulk density, total porosity, volume shrinkage, compressive strength and thermal conductivity was also carried out. The presence of pores in the geopolymer obtained is function of the percentage of hydrogen peroxide added, causing the concomitantly decrease in compressive strength, apparent density and thermal conductivity. The use of hydrogen peroxide as a blowing agent gave some thermal insulation properties to these geopolymers which could be close to the properties of some commercial insulation materials.

Influence of cristalline structure of two minerals clays of type 1/1 on their pozzolanic power

Two clayey materials, one provided by a patner in mineral sector and the other coming from Balengou (West Region Cameroon) were subject of a comparative study in order to evaluate the influence of their crystalline structure on their pozzolanic property. These two natural materials were preliminary enriched in clay minerals by wet sieving and the fractions obtained are denoted K and H respectively. K and H were calcinated at 700 °C, with a heating rate of 5 °C/min and 10 hours dwell at the peak temperature, the products obtained were named MK and MH. Samples K, H, MK and MH were physicochemically characterized by the chemical (ICP), thermal(TGA/DTA) and mineralogical (DRX and Spectrometry IR) analyses together with the measurement of specific surface (BET), crystallinity and the pouzzolanicity test. The results confirmed K as a kaolinitic and H halloysic clay. The kaolinite and the halloysite respectively presented in these clayey materials exhibited a poor crystallinity, but the degree of disorder is higher in K than in H. These results were largely affected by the significant fraction of gibbsite in kaolinitic clay K. At the crude state, the pozzolanic activity of the material H is weak compared with that of K, but the heat treatment makes largely improve this property for both samples.