Scale Up of PLA Nanoparticle Synthesis by Solvent Displacement and Functionalization of the Particles with a Silica Shell for Targeted Drug Delivery Applications

Biodegradable polymer nanoparticles have the properties necessary to address many of the issues associated with current drug delivery techniques including targeted and controlled delivery. A novel drug delivery vehicle is proposed consisting of a poly(lactic acid) nanoparticle core, with a functionalized, mesoporous silica shell. In this study, the production of PLA nanoparticles is investigated using solvent displacement in both a batch and continuous manner, and the effects of various system parameters are examined. Using Pluronic F-127 as the stabilization agent throughout the study, PLA nanoparticles are produced through solvent displacement with diameters ranging from 200 to 250 nm using two different methods: dropwise addition and in an impinging jet mixer. The impinging jet mixer allows for easy scale-up of particle production. The concentration of surfactant and volume of quench solution is found to have minimal impact on particle diameter; however, the concentration of PLA is found to significantly impact the diameter mean and polydispersity. In addition, the stability of the PLA nanoparticles is observed to increase as residual THF is evaporated. Lastly, the isolated PLA nanoparticles are coated with a silica shell using the Stöber Process. It is found that functionalizing the silica with a phosphonic silane in the presence of excess Pluronic F-127 decreases coalescence of the particles during the coating process. Future work should be conducted to fine-tune the PLA nanoparticle synthesis process by understanding the effect of other system parameters and in synthesizing mesoporous silica shells.

The Effects of Pi-Pi Stacking on the Controlled Radical Polymerization of Vinyl Aromatics

The atom transfer radical polymerization (ATRP) of styrene (St) was conducted in the presence of varying equivalence (eq) of hexafluorobenzene (HFB) and octafluorotoluene (OFT) to probe the effects of pi-pi stacking on the rate of the polymerization and on the tacticity of the resulting polystyrene (PSt). The extent of the pi-pi stacking interaction between HFB/OFT and the terminal polystyrenic phenyl group was also investigated as a function of solvent, both non-aromatic solvents (THF and hexanes) and aromatic solvents (benzene and toluene). In all cases the presence of HFB or OFT resulted in a decrease in monomer conversion indicating a reduction in the rate of the polymerization with greater retardation of the rate with increase eq of HFB or OFT (0.5 eq to 1 eq HFB/OFT compared to St). Additionally, when aromatic solvents were used instead of non-aromatic solvents the effect of the HFB/OFT on the rate was minimized, consistent with the aromatic solvent competitively interacting with the HFB/OFT. The effects of temperature and ligand strength on the ATRP of St in the presence of HFB were also probed. It was found that when using N,N,N’,N’,N’’-pentamethyldiethylenetriamine (PMDETA) as the ligand the effects of HFB at 38o were the same as at 86oC. When tris[2-(dimethylamino)ethyl]-amine (Me6TREN) was used as the ligand at 38o there was a decrease in monomer conversion similar to the analogous PMDETA reaction. When the polymerization was conducted at 86oC there was no effect on the monomer conversion with HFB present compared to when HFB was absent. To investigate the pi-pi stacking effect even further, the reverse pi-pi stacking system was observed by conducting the ATRP of pentafluorostyrene (PFSt) in the presence of varying eq of benzene and toluene, which in both cases resulted in an increase in monomer conversion compared to when benzene or toluene were absent; in summary the rate of the ATRP of PFSt increases when benzene or toluene waas present in the reaction. The pi-pi stacking interaction between the HFB/OFT and the dormant alkyl bromide of the polymer chain was verified by 1H-NMR with 1-bromoethylbenzene as the alkyl bromide. Also verified by 1H-NMR was the interaction between HFB/OFT and St and the interaction between PFSt and benzene. In all 1H-NMR spectra a perturbation in the aromatic and/or vinyl peaks was observed when the pi-pi stacking agent was present compared to when it was absent. The tacticity of the PSt formed in the presence of 1 eq of HFB was compared to the PSt formed in the absence of HFB by observing the C1 signal in their 13C-NMR spectra, but no change in shape or chemical shift of the signal was observed indicating that there was no change in tacticity.