Quantifying The Diffusion And Erosion Of Degradable Hydrogels Using A Microfluidic Technique

Hydrogels are composed of cross-linked networks of hydrophilic polymers that are biocompatible due to their high water content. Mass transfer through hydrogels has been suggested as an effective method of drug delivery, specifically in degradable polymers to minimize lasting effects within the body. Diffusion of small molecules in poly (ethylene glycol) diacrylate (PEG-DA) and dextran methacrylate (dex-MA) hydrogels was characterized in a microfluidic device and by complementary techniques. Microfluidic devices were prepared by crosslinking a formulation of hydrogel and photo-initiator, with and without visible dye, using photolithography to define a central microchannel. Channel sizes within the devices were approximately 600 ¿m to simulate vessels within the body. The microfluidic technique allows for both image and effluent analyses. To visualize the diffusive behavior within the dextran hydrogel, methylene blue and sulforhodamine 101 dyes were used in both elution and uptake experiments. Three analysis techniques for measuring diffusion coefficients were used to quantify the diffusion of solute in the hydrogel, including optical microscopy, characterization of device effluent, and NMR analyses. The optical microscopy technique analyzes images of the dye diffusion captured by a stereomicroscope to generate dye concentration v. position profiles. The data was fit to a diffusion model to determine diffusion coefficients and the dye release profile. In a typical elution experiment, aqueous solution is pumped through the microchannel and dye diffuses out of the hydrogel and into the aqueous phase. During elution, images are taken at regular time intervals and the effluent was collected. Analysis of the device effluent was performed using ultraviolet-visible (UV/Vis) spectroscopy to determine the effluent dye concentration and thus a short-time diffusion coefficient. Nuclear magnetic resonance (NMR) was used to determine a free diffusion coefficient of molecules in hydrogel without the effect of a concentration gradient. Diffusion coefficients for methylene blue and sulforhodamine 101 dyes in dex-MA hydrogel calculated using the three analysis methods all agree well. It was determined that utilizing a combination of the three techniques offers greater insight into molecular diffusion in hydrogels than employing each technique individually. The use of the same microfluidic devices used to measure diffusion is explored in the use of studying the degradation of dex-MA hydrogels. By combining what is known about the degradation rate in regards to the effect of pH and crosslinking and the ability to use a dye solution in contrast to establish the hydrogel boundaries could be a novel approach to studying hydrogel degradation.

The Use Of Amido- And Imido-Functionalized Alpha Hydroxy Acids In The Creation Of Biodegradable Polyesters: An Exploration Of Va

The purpose of this thesis was to synthesize biodegradable polyesters from a wide array of functionalized ¿-hydroxy acids. The initial strategy was to use amido-functionalized ¿-hydroxy acids and 2-bromopropanoyl bromide to form amido-functionalized cyclic diesters. Then, the resulting cyclic diesters would be used in ring opening polymerization to create biodegradable polyesters. However, the spontaneous rapid degradation of the secondary amido-functionalized cyclic diester structure, as seen with 2-benzamido-hydroxyacetic acid, limited ring formation to tertiary amido-functionalized ¿-hydroxy acids. Also, the hydrophilic nature of most ¿-hydroxy acids allowed water into the crystal structure of the ¿-hydroxy acid. Then, when the ¿-hydroxy acid was used in ring forming reactions, the associated water deactivated reactive reagents and limited cyclic diester synthesis. These issues led to the synthesis of hydrophobic and tertiary amido- and imido-functionalized ¿-hydroxy acids, 2-phthalimido-2-hydroxyacetic acid and 2-(1-oxoisoindolin-2-yl) hydroxyacetic acid. The new ¿-hydroxy acids were used in two new polymerization techniques, melt polycondensation and solution polymerization, instead of ring open polymerization. Melt polycondensation and solution polymerization had shown previous success in forming oligomers of amido-functionalized ¿-hydroxy acids. Melt polycondensation was conducted by heating the monomer past its melting temperature under reduced pressure. The uncatalyzed melt polycondensation of 2-(1-oxoisoindolin-2-yl) hydroxyacetic acid created polyesters (¿ 960 g/mol). The scandium(III) trifluoromethanesulfonate enhanced melt polycondensation polymerization created slightly larger oligomers (¿ 1340 g/mol). However, 2-phthalimido-2-hydroxyacetic acid was not compatible with melt polycondensation because thermal degradation occurred. Thus, solution polymerization was conducted via Steglich esterification. Only oligomeric functionalized polyesters were formed (¿ 1060 g/mol). Future work should focus on optimization of the catalyst and the reaction conditions to obtain higher molecular weight polyesters. Also, 2-(1-oxoisoindolin-2-yl) hydroxyacetic acid should be utilized in the cyclic diester synthesis technique.