Multiscale Characterization of Acrylic Bone Cement Modified with Functionalized Mesoporous Silica Nanoparticles

Acrylic bone cement is widely used to anchor orthopedic implants to bone and mechanical failure of the cement mantle surrounding an implant can contribute to aseptic loosening. In an effort to enhance the mechanical properties of bone cement, a variety of nanoparticles and fibers can be incorporated into the cement matrix. Mesoporous silica nanoparticles (MSNs) are a class of particles that display high potential for use as reinforcement within bone cement. Therefore, the purpose of this study was to quantify the impact of modifying an acrylic cement with various low-loadings of mesoporous silica. Three types of MSNs (one plain variety and two modified with functional groups) at two loading ratios (0.1 and 0.2 wt/wt) were incorporated into a commercially available bone cement. The mechanical properties were characterized using four-point bending, microindentation and nanoindentation (static, stress relaxation, and creep) while material properties were assessed through dynamic mechanical analysis, differential scanning calorimetry, thermogravimetric analysis, FTIR spectroscopy, and scanning electron microscopy. Four-point flexural testing and nanoindentation revealed minimal impact on the properties of the cements, except for several changes in the nano-level static mechanical properties. Conversely, microindentation testing demonstrated that the addition of MSNs significantly increased the microhardness. The stress relaxation and creep properties of the cements measured with nanoindentation displayed no effect resulting from the addition of MSNs. The measured material properties were consistent among all cements. Analysis of scanning electron micrographs images revealed that surface functionalization enhanced particle dispersion within the cement matrix and resulted in fewer particle agglomerates. These results suggest that the loading ratios of mesoporous silica used in this study were not an effective reinforcement material. Future work should be conducted to determine the impact of higher MSN loading ratios and alternative functional groups. (C) 2014 Elsevier Ltd. All rights reserved.

Maximizing Product Formation and Minimizing Degradation: A Look at Buffering Conditions and Post-Reaction Degradation for the In-Line Jaffe Reaction with Capillary Electrophoresis

Creatinine levels in blood serum are typically used to assess renal function. Clinical determination of creatinine is often based on the Jaffe reaction, in which creatinine in the serum reacts with sodium picrate, resulting in a spectrophotometrically quantifiable product. Previous work from our lab has introduced an electrophoretically mediated initiation of this reaction, in which nanoliter plugs of individual reagent solutions can be added to the capillary and then mixed and reacted. Following electrophoretic separation of the product from excess reactant(s), the product can be directly determined on column. This work aims to gain a detailed understanding of the in-capillary reagent mixing dynamics, in-line reaction yield, and product degradation during electrophoresis, with an overall goal of improving assay sensitivity. One set of experiments focuses on maximizing product formation through manipulation of various conditions such as pH, voltage applied, and timing of the applied voltage, in addition to manipulations in the identity, concentration, and pH of the background electrolyte. Through this work, it was determined that dramatic changes in local voltage fields within the various reagent zones lead to ineffective reagent overlapping. Use of the software simulation program Simul 5 enabled visualization of the reaction dynamics within the capillary, specifically the wide variance between the electric field intensities within the creatinine and picrate zones. Because of this simulation work, the experimental method was modified to increase the ionic strength of the creatinine reagent zone to lower the local voltage field, thus producing more predictable and effective overlap conditions for the reagents and allowing the formation of more Jaffe product. As second set of experiments focuses on controlling the post-reaction product degradation. In that vein, we have systematically explored the importance of the identity, concentration, and pH of the background electrolyte on the post-reaction degradation rate of the product. Although prior work with borate background electrolytes indicated that product degradation was probably a function of the ionic strength of the background electrolyte, this work with a glycine background electrolyte demonstrates that degradation is in fact not a function of ionic strength of the background electrolyte. As the concentration and pH of the glycine background increased, the rate of degradation of product did not change dramatically, whereas in borate-buffered systems, the rate of Jaffe product degradation increased linearly with background electrolyte concentration above 100.0 mM borate. Similarly, increasing pH of the glycine background electrolyte did not result in a corresponding increase in product degradation, as it had with the borate background electrolyte. Other general trends that were observed include: increasing background electrolyte concentration increases peak efficiency and higher pH favors product formation; thus, it appears that use of a background electrolyte other than borate, such as glycine, the rate of degradation of the Jaffe product can be slowed, increasing the sensitivity of this in-line assay.