Rapid Facilitation of Ultrasound Production and Lordosis in Female Hamsters by Horizontal Cuts Between the Septum and Preoptic Area

Horizontal cuts between the septum and preoptic area (anterior roof deafferentation, or ARD) dramatically affect sexual behavior, and in ways that could explain a variety of differences across behavioral categories (precopulatory, copulatory), species, and the sexes. Yet little is known about how these effects develop. Such information would be useful generally and could be pivotal in clarifying the mechanism for ultrasonic vocalization in female hamsters. Ultrasounds serve these animals as precopulatory signals that can attract males and help initiate mating. Their rates can be increased by either ARD or lesions of the ventromedial hypothalamus (VMN). If these effects are independent, they would require a mechanism that includes multiple structures and pathways within the forebrain and hypothalamus. However, it currently is not clear if they are independent: VMN lesions could affect vocalization by causing incidental damage to the same fibers targeted by ARD. Fortunately, past studies of VMN lesions have described a response with a very distinctive time course. This raises the possibility of assessing the independence of the two lesion effects by describing just the development of the response to ARD. To accomplish this, female hamsters were observed for levels of ultrasound production and lordosis before and after control surgery or ARD. As expected, both behaviors were facilitated by these cuts. Further, these effects began to appear by two days after surgery and were fully developed by six days. These results extend previous descriptions of the ARD effect by describing its development and time course. In turn, the rapid responses to ARD suggest that these cuts trigger disinhibitory changes in pathways that differ from those affected by VMN lesions. 2013

Effects Of The Flash Welding Process On Mechanical And Microstructural Properties Of Structural Steel Joints Assessed Using Dest

ASTM A529 carbon¿manganese steel angle specimens were joined by flash butt welding and the effects of varying process parameter settings on the resulting welds were investigated. The weld metal and heat affected zones were examined and tested using tensile testing, ultrasonic scanning, Rockwell hardness testing, optical microscopy, and scanning electron microscopy with energy dispersive spectroscopy in order to quantify the effect of process variables on weld quality. Statistical analysis of experimental tensile and ultrasonic scanning data highlighted the sensitivity of weld strength and the presence of weld zone inclusions and interfacial defects to the process factors of upset current, flashing time duration, and upset dimension. Subsequent microstructural analysis revealed various phases within the weld and heat affected zone, including acicular ferrite, Widmanstätten or side-plate ferrite, and grain boundary ferrite. Inspection of the fracture surfaces of multiple tensile specimens, with scanning electron microscopy, displayed evidence of brittle cleavage fracture within the weld zone for certain factor combinations. Test results also indicated that hardness was increased in the weld zone for all specimens, which can be attributed to the extensive deformation of the upset operation. The significance of weld process factor levels on microstructure, fracture characteristics, and weld zone strength was analyzed. The relationships between significant flash welding process variables and weld quality metrics as applied to ASTM A529-Grade 50 steel angle were formalized in empirical process models.