This purpose of this project was to investigate the collision-induced dissociation of dipeptides in negative ion electrospray ionization tandem mass spectrometry, with a focus on the mechanism of the production of imidazole-type fragments not previously reported from the fragmentation of the dipeptides being studied. The majority of the dipeptides studied were alanine N-terminal or serine C-terminal dipeptides. All dipeptides were dissolved in 50:50 methanol:water, 3 mM ammonium formate. Collision-induced dissociation in the collision cell of a triple quadrupole mass spectrometer was used to fragment [M-H]- precursor ions. Accurate mass measurements confirmed the molecular formula of the imidazole-type fragments. Further MS/MS studies were performed to provide information about the fragmentation mechanism for the formation of the imidazole-type fragments. The m/z values of intermediate ions in the formation of the imidazole-type fragments were confirmed through second-generation product ion scans and precursor ion scans. More sophisticated instrumentation will be required to further probe the structure of the intermediate ions.

Effects Of The Flash Welding Process On Mechanical And Microstructural Properties Of Structural Steel Joints Assessed Using Dest

ASTM A529 carbon¿manganese steel angle specimens were joined by flash butt welding and the effects of varying process parameter settings on the resulting welds were investigated. The weld metal and heat affected zones were examined and tested using tensile testing, ultrasonic scanning, Rockwell hardness testing, optical microscopy, and scanning electron microscopy with energy dispersive spectroscopy in order to quantify the effect of process variables on weld quality. Statistical analysis of experimental tensile and ultrasonic scanning data highlighted the sensitivity of weld strength and the presence of weld zone inclusions and interfacial defects to the process factors of upset current, flashing time duration, and upset dimension. Subsequent microstructural analysis revealed various phases within the weld and heat affected zone, including acicular ferrite, Widmanstätten or side-plate ferrite, and grain boundary ferrite. Inspection of the fracture surfaces of multiple tensile specimens, with scanning electron microscopy, displayed evidence of brittle cleavage fracture within the weld zone for certain factor combinations. Test results also indicated that hardness was increased in the weld zone for all specimens, which can be attributed to the extensive deformation of the upset operation. The significance of weld process factor levels on microstructure, fracture characteristics, and weld zone strength was analyzed. The relationships between significant flash welding process variables and weld quality metrics as applied to ASTM A529-Grade 50 steel angle were formalized in empirical process models.