Shear bands in metallic glasses are not necessarily hot

We have used the fusible tin coating method to detect shear band heating in amorphous Zr57Ti5Cu20Ni8Al10 loaded under quasi-static uniaxial compression. High-rate load data allowed a precise determination of the duration of shearing events and final fracture. When loading was halted prior to fracture we saw no evidence of melted tin despite the presence of shear offsets up to 6μm on some shear bands. Samples loaded to fracture showed evidence of tin melting near the fracture surface. We attribute the difference to the duration of the events, which is much longer for shear banding (milliseconds) than for fracture (microseconds).

High-speed Imaging of a Bulk Metallic Glass During Uniaxial Compression

High-speed imaging directly correlates the propagation of a particular shear band with mechanical measurements during uniaxial compression of a bulk metallic glass. Imaging shows shear occurs simultaneously over the entire shear plane, and load data, synced and time-stamped to the same clock as the camera, reveal that shear sliding is coincident with the load drop of each serration. Digital image correlation agrees with these results. These data demonstrate that shear band sliding occurs with velocities on the order of millimeters per second. Fracture occurs much more rapidly than the shear banding events, thereby readily leading to melting on fracture surfaces.