Effect of substrate surface roughening and cold spray coating on the fatigue life of AA2024 specimens

The effects of cold spray coating and substrate surface preparation on crack initiation under cyclic loading have been studied on Al2024 alloy specimens. Commercially pure (CP) aluminum feedstock powder has been deposited on Al2024-T351 samples using a cold-spray coating technique known as high velocity particle consolidation. Substrate specimens were prepared by surface grit blasting or shot peening prior to coating. The fatigue behavior of both coated and uncoated specimens was then tested under rotating bend conditions at two stress levels, 180 MPa and 210 MPa. Scanning electron microscopy was used to analyze failure surfaces and identify failure mechanisms. The results indicate that the fatigue strength was significantly improved on average, up to 50% at 180 MPa and up to 38% at 210 MPa, by the deposition of the cold-sprayed CP-Al coatings. Coated specimens first prepared by glass bead grit blasting experienced the largest average increase in fatigue life over bare specimens. The results display a strong dependency of the fatigue strength on the surface preparation and cold spray parameters

Study of the Compressive Strength of Aluminum Curved Elements

Currently, the Specification for Aluminum Structures (Aluminum Association, 2010) shows thin-walled aluminum plate sections with radii greater than eight inches have a lower compressive strength capacity than a flat plate with the same width and thickness. This inconsistency with intuition, which suggests any degree of folding a plate should increase its elastic buckling strength, inspired this study. A wide range of curvatures are studied—from a nearly flat plate to semi-circular. To quantify the curvature, a single non-dimensional parameter is used to represent all combinations of width, thickness and radius. Using the finite strip method (CU-FSM), elastic local buckling stresses are investigated. Using the ratio of stress values of curved plates compared to flat plates of the same size, equivalent plate-buckling coefficients are calculated. Using this data, nonlinear regression analyses are performed to develop closed form equations for five different edge support conditions. These equations can be used to calculate the elastic critical buckling stress for any curved aluminum section when the geometric properties (width, thickness, and radius) and the material properties (elastic modulus and Poisson’s ratio) are known. This procedure is illustrated in examples, each showing the applicability of the derived equations to geometries other than those investigated in this study and also providing comparisons with theoretically exact numerical analysis results.

Corrosion Characteristics And Mechanical Properties Of Aluminum Coatings Applied By The Cold Spray Process

Aluminum coatings were applied to 2024-T3 and 7075-T6 aluminum alloys via the Cold Spray process. The coatings were applied to substrateswith various surface preparation and Cold Spray carrier gas combinations. Some samples were coated with an additional sealant with and without a chromate conversion layer. An exhaustive corrosion analysis was then performed which utilized a number of long termand accelerated tests in order to characterize the corrosion protection of the coatings.