Halogen lamp and led activation of resin-modified glass ionomer restorative material. In vitro microhardness after long term storage

AIM: The purpose of this study was to evaluate the activation of resin-modified glass ionomer restorative material (RMGI, Vitremer-3M-ESPE, A3) by halogen lamp (QTH) or light-emitting diode (LED) by Knoop microhardness (KHN) in two storage conditions: 24hrs and 6 months and in two depths (0 and 2 mm). MATERIALS AND METHODS: The specimens were randomly divided into 3 experimental groups (n=10) according to activation form and evaluated in depth after 24h and after 6 months of storage. Activation was performed with QTH for 40s (700 mW/cm2) and for 40 or 20 s with LED (1,200 mW/scm2). After 24 hrs and 6 months of storage at 37°C in relative humidity in lightproof container, the Knoop microhardness test was performed. Statistics Data were analysed by three-way ANOVA and Tukey post-tests (p<0.05). RESULTS: All evaluated factors showed significant differences (p<0.05). After 24 hrs there were no differences within the experimental groups. KHN at 0 mm was significantly higher than 2 mm. After 6 months, there was an increase of microhardness values for all groups, being the ones activated by LED higher than the ones activated by QTH. CONCLUSION: Light-activation with LED positively influenced the KHN for RMGI evaluated after 6 months.

Microhardness and marginal adaptation of pre-warmed composites

Objectives: The aim of this study was to examine the effect of pre-warmed composite on the microhardness and marginal adaptation. Methods: Ninety six identical class II cavities were prepared in extracted human molars and filled/cured in three 2 mm increments using a metal matrix. Two composites (Tetric Evo Ceram (IvoclarVivadent) and ELS(Saremco)) were cured with a LED curing unit (Bluephase (IvoclarVivadent)) using curing cycles of 20 and 40 seconds. The composite was used at room temperature or pre-warmed at 54.5ºC (Calset(AdDent)). Twelve teeth were filled for every composite-curing time-composite temperature combination. The teeth were thermocycled (1000 cycles at 5º and 55ºC) and then stored at 37° C for seven days . Dye penetration (basic fuchsine 5% for 8 hours) was measured using a score scale. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500µm from the occlusal surface at a distance of 150 and 1000µm from the metal matrix. The total degree of polymerization of a composite specimen was determined by calculating the area under the hardness curve. Results: Statistical analyses showed no difference in marginal adaptation (p>0.05). Hardness values at 150µm from the matrix were lower than those at 1000µm. There was an increase of the microhardness at the top of each increment and decrease towards the bottom of each increment. Longer curing times resulted in harder composite samples. Multiple linear regression showed that only the curing time (p<0.001) and composite material (p<0.001) had a significant association with the degree of polymerization. The degree of polymerization was not influenced by pre-warming the composite at a temperature of 54.5ºC (p=4.86). Conclusion: Polymerization time can not be reduced by pre-warming the composite on a temperature of 54.5ºC. The marginal adaptation is not compromised by pre-warming the composite.

Influence of increment thickness on microhardness and dentin bond strength of bulk fill resin composites

OBJECTIVES To investigate the influence of increment thickness on Vickers microhardness (HV) and shear bond strength (SBS) to dentin of a conventional and four bulk fill resin composites. METHODS HV and SBS were determined on specimens of the conventional resin composite Filtek Supreme XTE (XTE) and the bulk fill resin composites SDR (SDR), Filtek Bulk Fill (FBF), x-tra fil (XFIL), and Tetric EvoCeram Bulk Fill (TEBF) after 24h storage. HV was measured either as profiles at depths up to 6mm or at the bottom of 2mm/4mm/6mm thick resin composite specimens. SBS of 2mm/4mm/6mm thick resin composite increments was measured to dentin surfaces of extracted human molars treated with the adhesive system OptiBond FL, and the failure mode was stereomicroscopically determined at 40× magnification. HV profiles and failure modes were descriptively analysed whereas HV at the bottom of resin composite specimens and SBS were statistically analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). RESULTS HV profiles (medians at 2mm/4mm/6mm): XTE 105.6/88.8/38.3, SDR 34.0/35.5/36.9, FBF 36.4/38.7/37.1, XFIL 103.4/103.9/101.9, TEBF 63.5/59.7/51.9. HV at the bottom of resin composite specimens (medians at 2mm/4mm/6mm): XTE (p<0.0001) 105.5>85.5>31.1, SDR (p=0.10) 25.8=21.9=26.0, FBF (p=0.16) 26.6=25.3=28.9, XFIL (p=0.18) 110.5=107.2=101.9, TEBF (p<0.0001) 63.0>54.9>48.2. SBS (MPa, medians at 2mm/4mm/6mm): XTE (p<0.0001) 23.9>18.9=16.7, SDR (p=0.26) 24.6=22.7=23.4, FBF (p=0.11) 21.4=20.3=22.0, x-tra fil (p=0.55) 27.0=24.0=23.6, TEBF (p=0.11) 21.0=20.7=19.0. The predominant SBS failure mode was cohesive failure in dentin. SIGNIFICANCE At increasing increment thickness, HV and SBS decreased for the conventional resin composite but generally remained constant for the bulk fill resin composites.

Surface Roughness and Microhardness of Two Recent CAD/CAM-Materials After Storage

Objectives: To investigate surface roughness and microhardness of two recent resin-ceramic materials for computer-aided design/computer-aided manufacturing (CAD/CAM) after polishing with three polishing systems. Surface roughness and microhardness were measured immediately after polishing and after six months storage including monthly artificial toothbrushing. Methods: Sixty specimens of Lava Ultimate (3M ESPE) and 60 specimens of VITA ENAMIC (VITA Zahnfabrik) were roughened in a standardized manner and polished with one of three polishing systems (n=20/group): Sof-Lex XT discs (SOFLEX; three-step (medium-superfine); 3M ESPE), VITA Polishing Set Clinical (VITA; two-step; VITA Zahnfabrik), or KENDA Unicus (KENDA; one-step; KENDA Dental). Surface roughness (Ra; μm) was measured with a profilometer and microhardness (Vickers; VHN) with a surface hardness indentation device. Ra and VHN were measured immediately after polishing and after six months storage (tap water, 37°C) including monthly artificial toothbrushing (500 cycles/month, toothpaste RDA ~70). Ra- and VHN-values were analysed with nonparametric ANOVA followed by Wilcoxon rank sum tests (α=0.05). Results: For Lava Ultimate, Ra (mean [standard deviation] before/after storage) remained the same when polished with SOFLEX (0.18 [0.09]/0.19 [0.10]; p=0.18), increased significantly with VITA (1.10 [0.44]/1.27 [0.39]; p=0.0001), and decreased significantly with KENDA (0.35 [0.07]/0.33 [0.08]; p=0.03). VHN (mean [standard deviation] before/after storage) decreased significantly regardless of polishing system (SOFLEX: 134.1 [5.6]/116.4 [3.6], VITA: 138.2 [10.5]/115.4 [5.9], KENDA: 135.1 [6.2]/116.7 [6.3]; all p<0.0001). For VITA ENAMIC, Ra (mean [standard deviation] before/after storage) increased significantly when polished with SOFLEX (0.37 [0.18]/0.41 [0.14]; p=0.01) and remained the same with VITA (1.32 [0.37]/1.31 [0.40]; p=0.58) and with KENDA (0.81 [0.35]/0.78 [0.32]; p=0.21). VHN (mean [standard deviation] before/after storage) remained the same regardless of polishing system (SOFLEX: 284.9 [24.6]/282.4 [31.8], VITA: 284.6 [28.5]/276.4 [25.8], KENDA: 292.6 [26.9]/282.9 [24.3]; p=0.42-1.00). Conclusion: Surface roughness and microhardness of Lava Ultimate was more affected by storage and artificial toothbrushing than was VITA ENAMIC.

Different bacterial models for in vitro induction of non-cavitated enamel caries-like lesions: Microhardness and polarized light miscroscopy analyses

The aim of this study was to compare different bacterial models for in vitro induction of non-cavitated enamel caries-like lesions by microhardness and polarized light microscopy analyses. One hundred blocks of bovine enamel were randomly divided into four groups (n = 25) according to the bacterial model for caries induction: (A) Streptococcus mutans, (B) S. mutans and Lactobacillus acidophilus, (C) S. mutans and L. casei, and (D) S. mutans, L. acidophilus, and L. casei. Within each group, the blocks were randomly divided into five subgroups according to the duration of the period of caries induction (4-20 days). The enamel blocks were immersed in cariogenic solution containing the microorganisms, which was changed every 48 h. Groups C and D presented lower surface hardness values (SMH) and higher area of hardness loss (ΔS) after the cariogenic challenge than groups A and B (P < 0.05). As regards lesion depth, under polarized light microscopy, group A presented significantly lower values, and groups C and D the highest values. Group B showed a higher value than group A (P < 0.05). Groups A and B exhibited subsurface caries lesions after all treatment durations, while groups C and D presented erosion-type lesions with surface softening. The model using S. mutans, whether or not it was associated with L. acidophilus, was less aggressive and may be used for the induction of non-cavitated enamel caries-like lesions. The optimal period for inducing caries-like lesions was 8 days.

Impact of acquired enamel pellicle modification on initial dental erosion

The acquired enamel pellicle that forms on the tooth surface serves as a natural protective barrier against dental erosion. Numerous proteins composing the pellicle serve different functions within this thin layer. Our study examined the effect of incorporated mucin and casein on the erosion-inhibiting potential of the acquired enamel pellicle. Cyclic acidic conditions were applied to mimic the erosive environment present at the human enamel interface during the consumption of soft drinks. One hundred enamel specimens were prepared for microhardness tests and distributed randomly into 5 groups (n = 20) that received the following treatment: deionized water, humidity chamber, mucin, casein, or a combination of mucin and casein. Each group was exposed to 3 cycles of a 2-hour incubation in human saliva, followed by a 2-hour treatment in the testing solution and a 1-min exposure to citric acid. The microhardness analysis demonstrated that the mixture of casein and mucin significantly improved the erosion-inhibiting properties of the human pellicle layer. The addition of individual proteins did not statistically impact the function of the pellicle. These data suggest that protein-protein interactions may play an important role in the effectiveness of the pellicle to prevent erosion.

Depth of cure of resin composites: is the ISO 4049 method suitable for bulk fill materials?

To evaluate if depth of cure D(ISO) determined by the ISO 4049 method is accurately reflected with bulk fill materials when compared to depth of cure D(new) determined by Vickers microhardness profiles.

Curing capability of halogen and LED light curing units in deep class II cavities in extracted human molars

Class II cavities were prepared in extracted lower molars filled and cured in three 2-mm increments using a metal matrix. Three composites (Spectrum TPH A4, Ceram X mono M7 and Tetric Ceram A4) were cured with both the SmartLite PS LED LCU and the Spectrum 800 continuous cure halogen LCU using curing cycles of 10, 20 and 40 seconds. Each increment was cured before adding the next. After a seven-day incubation period, the composite specimens were removed from the teeth, embedded in self-curing resin and ground to half the orofacial width. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500 microm from the occlusal surface at a distance of 150 microm and 1000 microm from the metal matrix. The total degree of polymerization of a composite specimen for any given curing time and curing light was determined by calculating the area under the hardness curve. Hardness values 150 microm from the metal matrix never reached maximum values and were generally lower than those 1000 microm from the matrix. The hardest composite was usually encountered between 200 microm and 1000 microm from the occlusal surface. For every composite-curing time combination, there was an increase in microhardness at the top of each increment (measurements at 500, 2500 and 4500 microm) and a decrease towards the bottom of each increment (measurements at 1500, 3500 and 5500 microm). Longer curing times were usually combined with harder composite samples. Spectrum TPH composite was the only composite showing a satisfactory degree of polymerization for all three curing times and both LCUs. Multiple linear regression showed that only the curing time (p < 0.001) and composite material (p < 0.001) had a significant association with the degree of polymerization. The degree of polymerization achieved by the LED LCU was not significantly different from that achieved by the halogen LCU (p = 0.54).

The impact of ozone treatment on enamel physical properties

PURPOSE: To assess the effects of the highly reactive molecule of ozone on sound enamel physical properties and its effects on sealing ability. METHODS: The effect of ozone on sealant tag length, microleakage and unfilled area proportion were evaluated on intact and prepared sound molar fissures. Microhardness, contact angle and acid resistance tests were performed on ground sound smooth surfaces. The samples were treated with ozone for 40 seconds (HealOzone). Control samples were treated with air (modified HealOzone) or left untreated. RESULTS: No statistically significant difference was observed between the control and ozone treated samples in all tests. Prepared fissures exhibited no unfilled areas and a statistically significantly lower microleakage compared to intact fissures. Ozone was shown to dehydrate enamel and consequently enhance its microhardness, which was reversible.

Natale und neonatale Zähne

Natal teeth have been defined as teeth which are present at birth, while neonatal teeth erupt during the first 30 days. Their occurrence is rare, the prevalence ranges from 1:2000 to 1:3000 with a higher frequency in the lip and palate clefts and syndroms. In about 85% natal or neonatal teeth are lower central incisors (60% in pairs), rare are upper teeth, molars and multiple teeth. In almost 90% they are part of the deciduous dentition. A lot of possible causes of early eruption are discussed, but only the relation to hereditary factors seems to be evident. An autosomal dominant trait is often described. The appearance of these teeth is dependent on the degree of maturity, but most of the time it is loose, small, discoloured and hypoplastic. Histologically, enamel hypoplasia with normal prism structure is apparent. No significant disturbances of the dentin structures are observed, only cervically dentin becomes atubular with spaces and enclosed cells. A large vascular pulp and failure of root formation are further investigations. Our microhardness measurements showed values from 24.3-32.4 KHN for enamel and 48.3-62.2 KHN for dentin, while normal deciduous teeth have an enamel hardness of 322.0 +/- 17.5 KHN. The thickness of enamel was never more than 280 microm compared to up to 1200 microm in normal teeth. This shows the retarded development of natal and neonatal teeth, because mineralization has not finished at the time of birth. In accordance with developmental age tooth structure and appearence are normal. In consideration of complications as Riga-Fede-disease, feeding problems, possibility of infection and hypermobility most of the time extraction is the treatment of choice, but in the interest of protecting the child this decision should be made carefully.

Impact of different toothpastes on the prevention of erosion

The aim of the present study was to test the impact of different toothpastes on the prevention of erosion. Enamel demineralization and remineralization were monitored using surface microhardness (SMH) measurements. Human enamel specimens were treated following two different procedures: (1) incubation in toothpaste slurry followed by acid softening and artificial saliva exposure; (2) acid softening followed by incubation in toothpaste slurry and artificial saliva exposure. For the control procedure, toothpaste treatment was excluded. The following toothpastes were tested: Zendium, Sensodyne Proschmelz (Pronamel), Prodent Rocket Power, Meridol and Signal active. Normalized SMH values compared to the baseline (= 1.00) after 1-hour artificial saliva exposure for procedure 1 (respectively for procedure 2) were as follows (mean: 95% CI): Sensodyne Proschmelz 0.97: 0.93, 1.00 (0.92: 0.90, 0.94), Zendium 0.97: 0.94, 1.00 (0.89: 0.83, 0.95), Meridol 0.97: 0.94, 1.00 (0.94: 0.92, 0.96), Signal active 0.94: 0.91, 0.97 (0.95: 0.91, 0.99), Prodent Rocket Power 0.92: 0.90, 0.94 (0.93: 0.89, 0.97) and control 0.91: 0.88, 0.94. Further exposure to artificial saliva for up to 4 h showed no significant improvement of SMH. Regression analyses revealed a significant impact of the applied procedure. Incubation in toothpaste slurries before the acid challenge seems to be favorable to prevent erosion. None of the tested toothpastes showed statistically significant better protection than another against an erosive attack.

Influence of human saliva on the development of artificial erosions

It was hypothesized that saliva from patients with erosion exhibits lower protective efficacy compared to saliva from patients without erosion, based on in vitro enamel softening studies. A total of 645 enamel specimens were distributed among seven experimental groups. Saliva was gathered from each of 10 volunteers without clinical signs of dental erosion and from 10 patients exhibiting severe erosive defects. Aliquots of 50 ml of saliva from each patient were mixed with sour drops or citric acid, respectively. Pooled saliva, sour drops and citric acid mixed with water served as controls. The enamel specimens were soaked in the respective mixture for 5 min and were subsequently incubated in pure saliva for 2 min. This cycle was repeated three times, then the specimens were kept in 100 ml of saliva for 8 h. Surface microhardness was evaluated at the beginning of the experiment and after each cycle. During the experiments, microhardness decreased significantly in all groups except for the pure saliva group. For sour drops and citric acid mixed with saliva from patients without erosion, the final microhardness was higher compared to the mixture of the two erosive compounds with saliva from patients with erosion. The storage of saliva for 8 h resulted in a certain amount of rehardening, with the highest level of rehardening being observed in the group that was least demineralized (sour drops plus saliva from patients without erosion). It is concluded that salivary components play a crucial role in the development of dental erosion.

A new optical detection method to assess the erosion inhibition by in vitro salivary pellicle layer

OBJECTIVES Application of the recently developed optical method based on the monitoring of the specular reflection intensity to study the protective potential of the salivary pellicle layer against early enamel erosion. METHODS The erosion progression was compared between two treatment groups: enamel samples coated by the 15 h-in vitro-formed salivary pellicle layer (group P, n=90) and the non-coated enamel surfaces (control group C, n=90). Different severity of the erosive impact was modelled by the enamel incubation in 1% citric acid (pH=3.6) for 2, 4, 8, 10 or 15 min. Erosion quantification was performed by the optical method as well as by the microhardness and calcium release analyses. RESULTS Optical assessment of the erosion progression showed erosion inhibition by the in vitro salivary pellicle in short term acidic treatments (≤ 4 min) which was also confirmed by microhardness measurements proving significantly less (p<0.05) enamel softening in the group P at 2 and 4 min of erosion compared to the group C. SEM images demonstrated less etched enamel interfaces in the group P at short erosion durations as well. CONCLUSIONS Monitoring of the specular reflection intensity can be successfully applied to quantify early erosion progression in comparative studies. In vitro salivary pellicle (2h) provides erosion inhibition but only in short term acidic exposures. CLINICAL SIGNIFICANCE The proposed optical technique is a promising tool for the fast and non-invasive erosion quantification in clinical studies.

Combined effect of a fluoride-, stannous- and chitosan-containing toothpaste and stannous-containing rinse on the prevention of initial enamel erosion-abrasion.

OBJECTIVES The aim of this study was to assess the preventive effect of a fluoride-, stannous- and chitosan-containing (F/Sn/chitosan-) toothpaste (TP) on initial enamel erosion and abrasion. METHODS In total, 150 human premolar enamel specimens were ground, polished and divided into 5 toothpaste/rinse groups (n=30): (G1) placebo-TP/tap water, (G2) sodium fluoride (NaF-) TP/tap water, (G3) F/Sn/chitosan-TP/tap water, (G4) F/Sn/chitosan-TP/Sn-rinse, (G5) NaF-TP/NaF-rinse. The 8-day erosion-abrasion cyclic treatment (one cycle/day) consisted of incubating the samples in artificial saliva (30min), then submitting the samples to toothbrush abrasion (2min incubation in toothpaste slurry; brushing with 20 toothbrush strokes) and rinsing (2min; 10ml) with the respective solution: tap water (G1-G3), Sn-rinse (G4) or NaF-rinse (G5). Afterwards, the samples were submitted to erosion (2min; 30ml 1% citric acid, pH=3.6). Surface microhardness (SMH) was measured initially and after every abrasion and erosion treatment. Enamel substance loss was calculated after each abrasion. Non-parametric ANOVA followed by Wilcoxon rank tests were used for analysis. RESULTS G1 presented the greatest SMH decrease, while G4 presented the least SMH decrease (p<0.001). G3 had a similar SMH decrease to G2 and G5. Substance loss was significantly lower in G4 than all other groups (p<0.05), closely followed by G3. Both G2 and G5 showed similar calculated enamel substance loss to G1. CONCLUSION The treatment with F/Sn/chitosan-TP and tap water provided a similar SMH decrease to both NaF-TP groups, but significantly lower substance loss. F/Sn/Chitosan-TP and Sn-rinse showed a better preventive effect, which promoted less SMH decrease and reduced substance loss. CLINICAL SIGNIFICANCE The toothpaste containing fluoride, stannous and chitosan shows promising results in reducing substance loss from erosion and abrasion. The combination of this toothpaste with the stannous-containing rinse showed even better prevention against erosion-abrasion.

Toothbrushing after an erosive attack: will waiting avoid tooth wear?

The purpose of this study was to determine if storage for up to 4 h in human saliva results in a decrease of erosive tooth wear (ETW) and in an increase of surface microhardness (SMH) of enamel samples after an erosive attack with subsequent abrasion. Furthermore, we determined the impact of individual salivary parameters on ETW and SMH. Enamel samples were distributed into five groups: group 1 had neither erosion nor saliva treatment; groups 2-5 were treated with erosion, then group 2 was placed in a humid chamber and groups 3-5 were incubated in saliva for 30 min, 2 h, and 4 h, respectively. After erosion and saliva treatments, all groups were treated with abrasion. Surface microhardness and ETW were measured before and after erosion, incubation in saliva, and abrasion. Surface microhardness and ETW showed significant changes throughout the experiment: SMH decreased and ETW increased in groups 2-5, regardless of the length of incubation in saliva. The results of groups 3-5 (exposed to saliva) were not significantly different from those of group 2 (not exposed to saliva). Exposure of eroded enamel to saliva for up to 4 h was not able to increase SMH or reduce ETW. However, additional experiments with artificial saliva without proteins showed protection from erosive tooth wear. The recommendation to postpone toothbrushing of enamel after an erosive attack should be reconsidered.