Effect of Salivary Contamination and Decontamination on Bond Strength of Two One-Step Self-Etching Adhesives to Dentin of Primary and Permanent Teeth

Purpose: To evaluate the effects of human saliva contamination and two decontamination procedures at different stages of the bonding procedure on the bond strength of two one-step self-etching adhesives to primary and permanent dentin. Materials and Methods: Extracted human primary and permanent molars (210 of each) were ground to mid-coronal dentin. The dentin specimens were randomly divided into 7 groups (n = 15/group/molar type) for each adhesive (Xeno V+ and Scotchbond Universal): no saliva contamination (control); saliva contamination before or after light curing of the adhesives followed by air drying, rinsing with water spray/air drying, or by rinsing with water spray/air drying/reapplication of the adhesives. Resin composite (Filtek Z250) was applied on the treated dentin surfaces. The specimens were stored at 37°C and 100% humidity for 24 h. After storage, shear bond strength (SBS) was measured and data analyzed with nonparametric ANOVA followed by exact Wilcoxon rank sum tests. Results: Xeno V+ generated significantly higher SBS than Scotchbond Universal when no saliva contamination occurred. Saliva contamination reduced SBS of Xeno V+, with the reduction being more pronounced when contamination occurred before light curing than after. In both situations, decontamination involving reapplication of the adhesive restored SBS. Saliva contamination had no significant effect on Scotchbond Universal. There were no differences in SBS between primary and permanent teeth. Conclusion: Rinsing with water and air drying followed by reapplication of the adhesive restored bond strength to saliva-contaminated dentin.

Bonding of simplified adhesive systems to caries-affected dentin of primary teeth.

PURPOSE To evaluate the bonding of simplified adhesive systems to sound and caries-affected dentin of primary teeth with microtensile (µTBS) and nanoleakage (NL) tests. MATERIALS AND METHODS Occlusal cavities were prepared in 36 sound second primary molars. Half of the specimens were submitted to pH cycling to simulate caries-affected dentin. Teeth were randomly restored with one of three materials: the etch-and-rinse adhesive system Adper Single Bond 2 (SB), the two-step self-etching adhesive system Adper SE Plus (SE), and the one-step self-etching adhesive system Adper Easy One (EASY). After storage for 24 h, specimens with cross-sectional areas of 0.8 mm2 were prepared for microtensile testing (1 mm/min). One stick from each tooth was immersed in silver nitrate solution (24 h) and allowed to develop for 8 h in order to score the nano leakage with SEM. The fracture pattern was evaluated using a stereomicroscope (400X). The µTBS means were analyzed by two-way ANOVA and Tukey's post-hoc test. For NL, the Kruskal- Wallis and Mann-Whitney tests were used (α < 0.05). RESULTS SB (35.5 ± 3.5) showed the highest µTBS value to sound dentin, followed by EASY (26.3 ± 1.9) and SE (18.2 ± 6.5) (p < 0.05). No difference among materials was observed for caries-affected dentin (SB: 17.8 ± 4.2; SE: 13.9 ± 3.2; EASY: 14.4 ± 4.2, p > 0.05). For all groups, adhesive/mixed fracture prevailed. Caries affected dentin promoted silver nitrate uptake into the adhesive interface; however, with SE, the nano leakage was more pronounced than in the other adhesive systems, even in sound dentin. CONCLUSION Caries-affected dentin negatively influences the bond strength and nano leakage of the two-step etch-and-rinse and one-step self-etching adhesive systems tested in primary teeth.

Push-out bond strength of CAD/CAM-ceramic luted to dentin with self-adhesive resin cements

OBJECTIVES: This study evaluated the initial and the artificially aged push-out bond strength between ceramic and dentin produced by one of five resin cements. METHODS: Two-hundred direct ceramic restorations (IPS Empress CAD) were luted to standardized Class I cavities in extracted human molars using one of four self-adhesive cements (SpeedCEM, RelyX Unicem Aplicap, SmartCem2 and iCEM) or a reference etch-and-rinse resin cement (Syntac/Variolink II) (n=40/cement). Push-out bond strength (PBS) was measured (1) after 24h water storage (non-aged group; n=20/cement) or (2) after artificial ageing with 5000 thermal cycles followed by 6 months humid storage (aged group; n=20/cement). Nonparametrical ANOVA and pairwise Wilcoxon rank-sum tests with Bonferroni-Holm adjustment were applied for statistical analysis. The significance level was set at alpha=0.05. In addition, failure mode and fracture pattern were analyzed by stereomicroscope and scanning electron microscopy. RESULTS: Whereas no statistically significant effect of storage condition was found (p=0.441), there was a significant effect of resin cement (p<0.0001): RelyX Unicem showed significantly higher PBS than the other cements. Syntac/Variolink II showed significantly higher PBS than SmartCEM2 (p<0.001). No significant differences were found between SpeedCEM, SmartCem2, and iCEM. The predominant failure mode was adhesive failure of cements at the dentin interface except for RelyX Unicem which in most cases showed cohesive failure in ceramic. SIGNIFICANCE: The resin cements showed marked differences in push-out bond strength when used for luting ceramic restorations to dentin. Variolink II with the etch-and-rinse adhesive Syntac did not perform better than three of the four self-adhesive resin cements tested.

Cement-augmented anterior screw fixation of Type II odontoid fractures in elderly patients with osteoporosis

BACKGROUND CONTEXT: Closed reduction and internal fixation by an anterior approach is an established option for operative treatment of displaced Type II odontoid fractures. In elderly patients, however, inadequate screw purchase in osteoporotic bone can result in severe procedure-related complications. PURPOSE: To improve the stability of odontoid fracture screw fixation in the elderly using a new technique that includes injection of polymethylmethacrylat (PMMA) cement into the C2 body. STUDY DESIGN: Retrospective review of hospital and outpatient records as well as radiographs of elderly patients treated in a university hospital department of orthopedic surgery. PATIENT SAMPLE: Twenty-four elderly patients (8 males and 16 females; mean age, 81 years; range, 62-98 years) with Type II fractures of the dens. OUTCOME MEASURES: Complications, cement leakage (symptomatic/asymptomatic), operation time, loss of reduction, pseudarthrosis and revision surgery, patient complaints, return to normal activities, and signs of neurologic complications were all documented. METHODS: After closed reduction and anterior approach to the inferior border of C2, a guide wire is advanced to the tip of the odontoid under biplanar fluoroscopic control. Before the insertion of one cannulated, self-drilling, short thread screws, a 12 gauge Yamshidi cannula is inserted from anterior and 1 to 3 mL of high-viscosity PMMA cement is injected into the anteroinferior portion of the C2 body. During polymerization of the cement, the screws are further inserted using a lag-screw compression technique. The cervical spine then is immobilized with a soft collar for 8 weeks postoperatively. RESULTS: Anatomical reduction of the dens was achieved in all 24 patients. Mean operative time was 64 minutes (40-90 minutes). Early loss of reduction occurred in three patients, but revision surgery was indicated in only one patient 2 days after primary surgery. One patient died within the first eight postoperative weeks, one within 3 months after surgery. In five patients, asymptomatic cement leakage was observed (into the C1-C2 joint in three patients, into the fracture in two). Conventional radiologic follow-up at 2 and 6 months confirmed anatomical healing in 16 of the19 patients with complete follow-up. In two patients, the fractures healed in slight dorsal angulation; one patient developed a asymptomatic pseudarthrosis. All patients were able to resume their pretrauma level of activity. CONCLUSIONS: Cement augmentation of the screw in Type II odontoid fractures in elderly patients is technically feasible in a clinical setting with a low complication rate. This technique may improve screw purchase, especially in the osteoporotic C2 body.

Retention of Root Canal Posts: Effect of Cement Film Thickness, Luting Cement, and Post Pretreatment.

The aim of this study was to investigate the effect of the cement film thickness of a zinc phosphate or a resin cement on retention of untreated and pretreated root canal posts. Prefabricated zirconia posts (CosmoPost: 1.4 mm) and two types of luting cements (a zinc phosphate cement [DeTrey Zinc] and a self-etch adhesive resin cement [Panavia F2.0]) were used. After removal of the crowns of 360 extracted premolars, canines, or incisors, the root canals were prepared with a parallel-sided drill system to three different final diameters. Half the posts did not receive any pretreatment. The other half received tribochemical silicate coating according to the manufacturer's instructions. Posts were then luted in the prepared root canals (n=30 per group). Following water storage at 37°C for seven days, retention of the posts was determined by the pull-out method. Irrespective of the luting cement, pretreatment with tribochemical silicate coating significantly increased retention of the posts. Increased cement film thickness resulted in decreased retention of untreated posts and of pretreated posts luted with zinc phosphate cement. Increased cement film thickness had no influence on retention of pretreated posts luted with resin cement. Thus, retention of the posts was influenced by the type of luting cement, by the cement film thickness, and by the post pretreatment.