Comparison among gold standard techniques used for the validation of methods for occlusal caries detection

The aim of this in vitro study was to assess the agreement among four techniques used as gold standard for the validation of methods for occlusal caries detection. Sixty-five human permanent molars were selected and one site in each occlusal surface was chosen as the test site. The teeth were cut and prepared according to each technique: stereomicroscopy without coloring (1), dye enhancement with rhodamine B (2) and fuchsine/acetic light green (3), and semi-quantitative microradiography (4). Digital photographs from each prepared tooth were assessed by three examiners for caries extension. Weighted kappa, as well as Friedman's test with multiple comparisons, was performed to compare all techniques and verify statistical significant differences. Results: kappa values varied from 0.62 to 0.78, the latter being found by both dye enhancement methods. Friedman's test showed statistical significant difference (P < 0.001) and multiple comparison identified these differences among all techniques, except between both dye enhancement methods (rhodamine B and fuchsine/acetic light green). Cross-tabulation showed that the stereomicroscopy overscored the lesions. Both dye enhancement methods showed a good agreement, while stereomicroscopy overscored the lesions. Furthermore, the outcome of caries diagnostic tests may be influenced by the validation method applied. Dye enhancement methods seem to be reliable as gold standard methods.

Microhardness and marginal adaptation of pre-warmed composites

Objectives: The aim of this study was to examine the effect of pre-warmed composite on the microhardness and marginal adaptation. Methods: Ninety six identical class II cavities were prepared in extracted human molars and filled/cured in three 2 mm increments using a metal matrix. Two composites (Tetric Evo Ceram (IvoclarVivadent) and ELS(Saremco)) were cured with a LED curing unit (Bluephase (IvoclarVivadent)) using curing cycles of 20 and 40 seconds. The composite was used at room temperature or pre-warmed at 54.5ºC (Calset(AdDent)). Twelve teeth were filled for every composite-curing time-composite temperature combination. The teeth were thermocycled (1000 cycles at 5º and 55ºC) and then stored at 37° C for seven days . Dye penetration (basic fuchsine 5% for 8 hours) was measured using a score scale. Knoop microhardness was determined 100, 200, 500, 1000, 1500, 2500, 3500, 4500 and 5500µm from the occlusal surface at a distance of 150 and 1000µm from the metal matrix. The total degree of polymerization of a composite specimen was determined by calculating the area under the hardness curve. Results: Statistical analyses showed no difference in marginal adaptation (p>0.05). Hardness values at 150µm from the matrix were lower than those at 1000µm. There was an increase of the microhardness at the top of each increment and decrease towards the bottom of each increment. Longer curing times resulted in harder composite samples. Multiple linear regression showed that only the curing time (p<0.001) and composite material (p<0.001) had a significant association with the degree of polymerization. The degree of polymerization was not influenced by pre-warming the composite at a temperature of 54.5ºC (p=4.86). Conclusion: Polymerization time can not be reduced by pre-warming the composite on a temperature of 54.5ºC. The marginal adaptation is not compromised by pre-warming the composite.